As part of the experiments herein, the mechanical properties of specimens made of poly-ether-ether-ketone (PEEK) material using 3D printing technology were determined. Two populations of specimens were investigated, the first of which contained an amorphous structure, while the other held a crystal structure. The studies also investigated the influence of the print directionality on the mechanical properties obtained. Static tensile, three-point bending, and impact tests were carried out. The results for the effect of the structure type on the tensile properties showed that the modulus of elasticity was approximately 20% higher for the crystal than for the amorphous PEEK form. The Poisson’s ratios were similar, but the ratio was slightly higher for the amorphous samples than the crystalline ones. Furthermore, the studies included a chemical PEEK modification to increase the hydrophilicity. For this purpose, nitrite and hydroxyl groups were introduced into the chain by chemical reactions. The results demonstrate that the modified PEEK specimens had worse thermoplastic properties than the unmodified specimens.

When designing a wind turbine, the main objective is to generate maximum effective power with the lowest possible production costs. The power of a wind turbine depends primarily on the aerodynamic properties of its blades. Moreover, the cost of making a blade for a wind turbine, and therefore also for the entire wind turbine, depends on the materials used for its production. Therefore, wind turbine blades are the most studied element of a wind turbine. By selecting the optimal material and geometric properties of the wind turbine blade, it is possible to reduce the costs of making the entire wind turbine. These rationales led the authors to investigate composite wind turbine blades. A two-criteria optimization task was formulated, which allowed for the simultaneous consideration of two criteria: minimizing the mass and minimizing the vertical deflection of the wind turbine blade. Geometric properties of the blade, influencing the considered criteria, were assumed as decision variables. The weighted sum method was used. The results obtained allowed us to determine the optimal geometric and material properties of a wind turbine blade.

Eco-friendly composites are proposed to substitute commonly available polymers. Currently, wood–plastic composites and natural fiber-reinforced composites are gaining growing recognition in the industry, being mostly on the thermoplastic matrix. However, little data are available about the possibility of producing biocomposites on a silicone matrix. This study focused on assessing selected organic fillers’ impact (ground coffee waste (GCW), walnut shell (WS), brewers’ spent grains (BSG), pistachio shell (PS), and chestnut (CH)) on the physicochemical and mechanical properties of silicone-based materials. Density, hardness, rebound resilience, and static tensile strength of the obtained composites were tested, as well as the effect of accelerated aging under artificial seawater conditions. The results revealed changes in the material’s properties (minimal density changes, hardness variation, overall decreasing resilience, and decreased tensile strength properties). The aging test revealed certain bioactivities of the obtained composites. The degree of material degradation was assessed on the basis of the strength characteristics and visual observation. The investigation carried out indicated the impact of the filler’s type, chemical composition, and grain size on the obtained materials’ properties and shed light on the possibility of acquiring ecological silicone-based materials.

Halloysite nanotube (HNT) additions to the thermoplastic polyurethane (TPU) system were thoroughly evaluated in this study. The resultant composites have been designed for future personalized intervertebral disc implant applications, which requires additional technology to obtain the appropriate geometry unique to each patient. These requirements can be fulfilled using 3D printing. In this work, a technology was developed to produce filaments for fused deposition modeling (FDM). Nanocomposites were prepared using variable HNT content (1, 2, and 3 wt.%). The nanostructure of the resultant composites was confirmed using scanning transmission electron microscopy (STEM). Mechanical tests were used to measure the tensile modulus, stress, and elongation the composites and TPU matrix. Nanocomposites with 2% HNT content were able to withstand 26% increased stress and 50% increased elongation compared to pure TPU before fracturing in addition to a 13% reduction in the friction coefficient. A MTT cytotoxicity assay confirmed the cytotoxicity of all tested materials against human epidermal keratinocyte cells (HaCaT).

Silicones are often used for various types of coatings, but due to their poor mechanical properties, they often require modification to meet specific requirements. At the same time, various production processes throughout the world generate different types of waste, the disposal of which is harmful to the environment. One possible solution is to use production waste as a filler. In this paper, the authors investigated how the use of metallurgical production waste products as fillers changed the mechanical properties of silicone composites prepared by casting. Composite samples were characterized using tensile tests, resilience, pin-on-disc, Schopper–Schlobach abrasion, hardness, and density measurements. Based on the obtained results, the authors assessed the effect of each of the fillers used in different weight proportions. The results showed that the silicone composite filled with 5 wt% zinc dust showed the lowest decrease in tensile strength and Young’s modulus, with a simultaneous significant reduction in abrasion compared with the reference sample. This research shows that zinc waste can be successfully introduced into a silicone matrix in cases where it is important to reduce abrasive wear.

Waste from large-scale production processes is a growing environmental problem that can potentially be solved by using this waste as fillers in polymeric composites to improve the mechanical and tribological properties of polymeric matrixes. This paper presents research concerning how the introduction of fillers in the form of manganese residue and manganese(II) oxide changes the mechanical and tribological properties of epoxy composites produced by gravity casting. The research was carried out for composites with 2.5 wt.%, 5 wt.%, and 10 wt.% of fillers. Properties such as the density, hardness, resilience, flexural strength, deflection, flexural modulus, tensile strength, elongation at break, and Young’s modulus were determined. Moreover, based on the ball-on-plate test, the wear volume and friction coefficients of the tested materials were determined. Microscopic images of the abrasion profiles were also obtained. The geometry of the wear paths was measured with a profilometer, and the results showed that introducing fillers reduced the abrasive wear of the composites; however, in all cases, the fillers decreased the strength of the tested materials.