CdCl₂ treatment is a crucial step in development of CdS/CdTe solar cells. Although this processing step has been used over a period of three decades, full understanding is not yet achieved. This paper reports the experimental evidence for improvement of composition of CdTe layers during CdCl₂ treatment. This investigation makes use of four selected analytical techniques; Photo-electro-chemical (PEC) cell, X-ray diffraction (XRD), Raman spectroscopy and Scanning electron microscopy (SEM). CdTe layers used were electroplated using three Cd precursors; CdSO₄, Cd(NO₃)₂ and CdCl₂. Results show the improvement of stoichiometry of CdTe layers during CdCl₂ treatment through chemical reaction between Cd from CdCl₂ and elemental Te that usually precipitate during CdTe growth, due to its natural behaviour. XRD and SEM results show that the low-temperature (~85 °C) electroplated CdTe layers consist of ~(20–60) nm size crystallites, but after CdCl₂ treatment, the layers show drastic recrystallisation with grains becoming a few microns in size. These CdCl₂ treated layers are then comparable to high temperature grown CdTe layers by the size of grains.

Cadmium telluride (CdTe) thin films have been successfully prepared from an aqueous electrolyte bath containing cadmium chloride (CdCl₂)·H₂O and tellurium dioxide (TeO₂) using an electrodeposition technique. The structural, electrical, morphological and optical properties of these thin films have been characterised using X-ray diffraction (XRD), Raman spectroscopy, optical profilometry, DC current-voltage (I-V) measurements, photoelectrochemical (PEC) cell measurement, scanning electron microscopy (SEM), atomic force microscopy (AFM) and UV-Vis spectrophotometry. It is observed that the best cathodic potential is 698 mV with respect to standard calomel electrode (SCE) in a three electrode system. Structural analysis using XRD shows polycrystalline crystal structure in the as-deposited CdTe thin films and the peaks intensity increase after CdCl₂ treatment. PEC cell measurements show the possibility of growing p-, i- and n-type CdTe layers by varying the growth potential during electrodeposition. The electrical resistivity of the as-deposited layers are in the order of 10⁴ Ω·cm. SEM and AFM show that the CdCl₂ treated samples are more roughness and have larger grain size when compared to CdTe grown by CdSO₄ precursor. Results obtained from the optical absorption reveal that the bandgap of as-deposited CdTe (1.48–1.52) eV reduce to (1.45–1.49) eV after CdCl₂ treatment. Full characterisation of this material is providing new information on crucial CdCl₂ treatment of CdTe thin films due to its built-in CdCl₂ treatment during the material growth. The work is progressing to fabricate solar cells with this material and compare with CdTe thin films grown by conventional sulphate precursors.