Cadmium telluride (CdTe) thin films have been successfully prepared from an aqueous electrolyte bath containing cadmium chloride (CdCl₂)·H₂O and tellurium dioxide (TeO₂) using an electrodeposition technique. The structural, electrical, morphological and optical properties of these thin films have been characterised using X-ray diffraction (XRD), Raman spectroscopy, optical profilometry, DC current-voltage (I-V) measurements, photoelectrochemical (PEC) cell measurement, scanning electron microscopy (SEM), atomic force microscopy (AFM) and UV-Vis spectrophotometry. It is observed that the best cathodic potential is 698 mV with respect to standard calomel electrode (SCE) in a three electrode system. Structural analysis using XRD shows polycrystalline crystal structure in the as-deposited CdTe thin films and the peaks intensity increase after CdCl₂ treatment. PEC cell measurements show the possibility of growing p-, i- and n-type CdTe layers by varying the growth potential during electrodeposition. The electrical resistivity of the as-deposited layers are in the order of 10⁴ Ω·cm. SEM and AFM show that the CdCl₂ treated samples are more roughness and have larger grain size when compared to CdTe grown by CdSO₄ precursor. Results obtained from the optical absorption reveal that the bandgap of as-deposited CdTe (1.48–1.52) eV reduce to (1.45–1.49) eV after CdCl₂ treatment. Full characterisation of this material is providing new information on crucial CdCl₂ treatment of CdTe thin films due to its built-in CdCl₂ treatment during the material growth. The work is progressing to fabricate solar cells with this material and compare with CdTe thin films grown by conventional sulphate precursors.

Electrodeposition of CdTe thin films was carried out from the late 1970s using the cadmium sulphate precursor. The solar energy group at Sheffield Hallam University has carried out a comprehensive study of CdTe thin films electroplated using cadmium sulfate, cadmium nitrate and cadmium chloride precursors, in order to select the best electrolyte. Some of these results have been published elsewhere, and this manuscript presents the summary of the results obtained on CdTe layers grown from cadmium sulphate precursor. In addition, this research program has been exploring the ways of eliminating the reference electrode, since this is a possible source of detrimental impurities, such as K⁺ and Ag⁺ for CdS/CdTe solar cells. This paper compares the results obtained from CdTe layers grown by three-electrode (3E) and two-electrode (2E) systems for their material properties and performance in CdS/CdTe devices. Thin films were characterized using a wide range of analytical techniques for their structural, morphological, optical and electrical properties. These layers have also been used in device structures; glass/FTO/CdS/CdTe/Au and CdTe from both methods have produced solar cells to date with efficiencies in the region of 5%–13%. Comprehensive work carried out to date produced comparable and superior devices fabricated from materials grown using 2E system.