Silicon films were deposited at moderate substrate temperatures (280–500° C) from pure silane and a silane-hydrogen mixture (10% SiH₄, 90% H₂) in a hotwire CVD reactor. The morphology, structure and composition of the samples were studied with scanning electron microscopy, transmission electron microscopy, transmission electron diffraction, X-ray diffraction, Raman spectroscopy and secondary ion mass spectrometry. The sample deposited at 500° C with pure silane has an amorphous structure, whereas the samples obtained from silane diluted in hydrogen have a polycrystalline structure, even that grown at the lowest temperature (280° C). Polycrystalline samples have a columnar structure with 0.3–1 μm crystallite sizes with preferential orientation in [220] direction. Deposition rates depend on the filament-substrate distance and range from 9.5 to 37 Å/s for the polycrystalline samples. The high quality of the polycrystalline samples obtained makes the hot-wire technique very promising. Moreover, it is expected to be easily scaled up for applications to large-area optoelectronic devices and to photovoltaic solar cells.

The possible use of polyethylene naphthalate as substrate for low-temperature deposited solar cells has been studied in this paper. The transparency of this polymer makes it a candidate to be used in both substrate and superstrate configurations. ZnO:Al has been deposited at room temperature on top of PEN. The resulting structure PEN/ZnO:Al presented good optical and electrical properties. PEN has been successfully textured (nanometer and micrometer random roughness) using hot-embossing lithography. Reflector structures have been built depositing Ag and ZnO:Al on top of the stamped polymer. The deposition of these layers did not affect the final roughness of the whole. The reflector structure has been morphologically and optically analysed to verify its suitability to be used in solar cells

In this work, we have studied the texturization process of (100) c-Si wafers using a low concentration potassium hydroxide solution in order to obtain good quality textured wafers. The optimization of the etching conditions have led to random but uniform pyramidal structures with good optical properties. Then, symmetric heterojunctions were deposited by Hot-Wire CVD onto these substrates and the Quasi-Steady-State PhotoConductance technique was used to measure passivation quality. Little degradation in the effective lifetime and implicit open circuit voltage of these devices (< 20 mV) was observed in all cases. It is especially remarkable that for big uniform pyramids, the open-circuit voltage is comparable to the values obtained on flat substrates

Spectroscopic ellipsometry and high resolution transmission electron microscopy have been used to characterize microcrystalline silicon films. We obtain an excellent agreement between the multilayer model used in the analysis of the optical data and the microscopy measurements. Moreover, thanks to the high resolution achieved in the microscopy measurements and to the improved optical models, two new features of the layer‐by‐layer deposition of microcrystalline silicon have been detected: (i) the microcrystalline films present large crystals extending from the a‐Si:H substrate to the film surface, despite the sequential process in the layer‐by‐layer deposition; and (ii) a porous layer exists between the amorphous silicon substrate and the microcrystalline silicon film.