The demand for truck–bus radial (TBR) tires with enhanced fuel efficiency has grown in recent years. Many studies have investigated silica-filled natural rubber (NR) compounds to address these needs. However, silica-filled compounds offer inferior abrasion resistance compared to carbon black-filled compounds. Further, the use of NR as a base rubber can hinder silanization and coupling reactions due to interference by proteins and lipids. Improved silica dispersion be achieved without the use of a silane coupling agent by introducing epoxide groups to NR, which serve as silica-affinitive functional groups. Furthermore, the coupling reaction can be promoted by facilitating chemical interaction between the hydroxyl group of silica and the added epoxide groups. Thus, this study evaluated the properties of commercialized NR, ENR-25, and ENR-50 compounds with or without an added silane coupling agent, and the filler–rubber interaction was quantitatively calculated using vulcanizate structure analysis. The increased epoxide content, when the silane coupling agent was not used, improved silica dispersion, abrasion resistance, fuel efficiency, and wet grip. Once a basic level of silica dispersion was secured by using the silane coupling agent, both the abrasion resistance and wet grip improved with increasing epoxide content. Furthermore, the silane coupling agent could be partially replaced by ENR due to the high filler–rubber interaction between the ENR and silica. Therefore, epoxidation shows potential for resolving the issues associated with poor coupling reactions and abrasion resistance in silica-filled NR compounds.

The tire industry has shown an increasing demand for the reduction in rolling resistance. Efforts have been made to improve the viscoelastic properties of tire compounds and reduce the weight of tires through optimization of the vulcanizate structure, which has become extremely complex. In this study, vulcanizates using carbon black and silica as binary fillers were prepared at various curing temperatures. Vulcanizate structures with respect to curing temperature were classified according to the chemical crosslink density by sulfur, carbon black bound rubber (i.e., physical crosslink due to carbon black), and silica-silane–rubber network. All properties exhibited a decreasing trend under the application of high curing temperatures, and the decrease in the crosslink density per unit content of filler with an increase in curing temperature was shown to be greater in carbon black than in silica. Mechanical and viscoelastic properties were also measured to evaluate the impact that the compound variates have on tire tread performance. These results serve as a guideline for determining the content and filler type and for setting the cure condition during the design of actual compound formulations to increase the crosslink density of rubber while retaining the necessary mechanical and viscoelastic properties for practical application.

Liquid butadiene rubber (LqBR) which used as a processing aid play a vital role in the manufacturing of high-performance tire tread compounds. However, the studies on the effect of molecular weight, microstructure, and functionalization of LqBR on the properties of compounds are still insufficient. In this study, non-functionalized and center-functionalized liquid butadiene rubbers (N-LqBR and C-LqBR modified with ethoxysilyl group, respectively) were synthesized with low vinyl content and different molecular weights using anionic polymerization. In addition, LqBR was added to the silica-filled SSBR compounds as an alternative to treated distillate aromatic extract (TDAE) oil, and the effect of molecular weight and functionalization on the properties of the silica-filled SSBR compound was examined. C-LqBR showed a low Payne effect and Mooney viscosity because of improved silica dispersion due to the ethoxysilyl functional group. Furthermore, C-LqBR showed an increased crosslink density, improved mechanical properties, and reduced organic matter extraction compared to the N-LqBR compound. LqBR reduced the glass transition temperature (T_g) of the compound significantly, thereby improving snow traction and abrasion resistance compared to TDAE oil. Furthermore, the energy loss characteristics revealed that the hysteresis loss attributable to the free chain ends of LqBR was dominant.

The vulcanizate structure of filled compounds is affected by filler–rubber interactions (FRI) and the chemical crosslink density (CCD) of the matrix rubber. In particular, in filled compounds using a silica–silane system, FRIs due to silica–rubber coupling are a major influencing factor for the vulcanizate structure and physical properties. In this study, the effect of sulfur variation on the vulcanizate structure of silica-filled solution styrene–butadiene rubber compounds using a sulfide–silane coupling agent was studied. The vulcanizate structure according to sulfur variation was quantitatively analyzed using the swelling test and Flory–Rehner and Kraus equations. As the sulfur content increased, both FRI and the CCD increased, and it was confirmed that sulfur variation influenced the silica–rubber coupling efficiency through increased FRI. In addition, field emission scanning electron microscope images showed that increased FRI contributed to improvements in silica dispersion, abrasion resistance, and energy loss characteristics.

Recently, research conducted on tread compounds with liquid butadiene rubber (LqBR) have been conducted in the tire industry. In particular, the introduction of functional groups into LqBRs is expected to lower hysteresis loss caused by the free chain ends of LqBR. To study this, LqBRs with functional groups at different positions were synthesized. The occurrences of in-chain and chain-end functionalization of functionalized LqBRs (F-LqBRs) were confirmed, the microstructure and functionalization efficiency of F-LqBRs were calculated through the characterizations. This novel functionalization technology was beneficial not only to immobilizing the free chain ends of LqBRs to the surfaces of silica to decrease the number of free chain ends, but also chemically bonding the LqBR chains on the base polymer through a crosslinking reaction to enhance the filler-rubber interaction. The effects of the functional group position and number of the free chain ends on the physical properties and hysteresis of the compounds were investigated by partially replacing the treated distillate aromatic extract (TDAE) oil with LqBR in silica-filled rubber compounds. The results showed that compounds that had applied DF-LqBR with both end functionalization performed better, including improving the silica dispersion, higher extraction resistance, and lower rolling resistance, than other F-LqBRs compounds.

As the world is shifting from internal combustion engine vehicles to electric vehicles in response to environmental pollution, the tire industry has been conducting research on tire performance to meet the requirements of electric vehicles. In this experiment, functionalized liquid butadiene rubber (F-LqBR) with triethoxysilyl groups at both ends was introduced into a silica-filled rubber compound as a substitute for treated distillate aromatic extract (TDAE) oil, and comparative evaluation was conducted according to the number of triethoxysilyl groups. The results showed that F-LqBRs improved silica dispersion in the rubber matrix through the formation of chemical bonds between silanol groups and the base rubber, and reduced rolling resistance by limiting chain end mobility and improving filler–rubber interaction. However, when the number of triethoxysilyl groups in F-LqBR was increased from two to four, self-condensation increased, the reactivity of the silanol groups decreased, and the improvement of properties was reduced. As a result, the optimized end functionality of triethoxysilyl groups for F-LqBR in silica-filled rubber compound was two. The 2-Azo-LqBR with the optimized functionality showed an improvement of 10% in rolling resistance, 16% in snow traction, and 17% in abrasion resistance when 10 phr of TDAE oil was substituted.