The demand for truck–bus radial (TBR) tires with enhanced fuel efficiency has grown in recent years. Many studies have investigated silica-filled natural rubber (NR) compounds to address these needs. However, silica-filled compounds offer inferior abrasion resistance compared to carbon black-filled compounds. Further, the use of NR as a base rubber can hinder silanization and coupling reactions due to interference by proteins and lipids. Improved silica dispersion be achieved without the use of a silane coupling agent by introducing epoxide groups to NR, which serve as silica-affinitive functional groups. Furthermore, the coupling reaction can be promoted by facilitating chemical interaction between the hydroxyl group of silica and the added epoxide groups. Thus, this study evaluated the properties of commercialized NR, ENR-25, and ENR-50 compounds with or without an added silane coupling agent, and the filler–rubber interaction was quantitatively calculated using vulcanizate structure analysis. The increased epoxide content, when the silane coupling agent was not used, improved silica dispersion, abrasion resistance, fuel efficiency, and wet grip. Once a basic level of silica dispersion was secured by using the silane coupling agent, both the abrasion resistance and wet grip improved with increasing epoxide content. Furthermore, the silane coupling agent could be partially replaced by ENR due to the high filler–rubber interaction between the ENR and silica. Therefore, epoxidation shows potential for resolving the issues associated with poor coupling reactions and abrasion resistance in silica-filled NR compounds.

As the world is shifting from internal combustion engine vehicles to electric vehicles in response to environmental pollution, the tire industry has been conducting research on tire performance to meet the requirements of electric vehicles. In this experiment, functionalized liquid butadiene rubber (F-LqBR) with triethoxysilyl groups at both ends was introduced into a silica-filled rubber compound as a substitute for treated distillate aromatic extract (TDAE) oil, and comparative evaluation was conducted according to the number of triethoxysilyl groups. The results showed that F-LqBRs improved silica dispersion in the rubber matrix through the formation of chemical bonds between silanol groups and the base rubber, and reduced rolling resistance by limiting chain end mobility and improving filler–rubber interaction. However, when the number of triethoxysilyl groups in F-LqBR was increased from two to four, self-condensation increased, the reactivity of the silanol groups decreased, and the improvement of properties was reduced. As a result, the optimized end functionality of triethoxysilyl groups for F-LqBR in silica-filled rubber compound was two. The 2-Azo-LqBR with the optimized functionality showed an improvement of 10% in rolling resistance, 16% in snow traction, and 17% in abrasion resistance when 10 phr of TDAE oil was substituted.

In this study, we examined the feasibility of using epoxidized liquid isoprene rubber (E-LqIR) as a processing aid for truck and bus radial (TBR) tire treads and investigated the effects of the epoxide content on the wear resistance, fuel efficiency, and resistance to extraction of the E-LqIRs. The results confirmed that, compared to the treated distillate aromatic extract (TDAE) oil, the E-LqIRs could enhance the filler–rubber interactions and reduce the oil migration. However, the consumption of sulfur by the E-LqIRs resulted in a lower crosslink density compared to that of the TDAE oil, and the higher epoxide content decreased the wear resistance and fuel efficiency because of the increased glass-transition temperature (T_g). In contrast, the E-LqIR with a low epoxide content of 6 mol% had no significant effect on the T_g of the final compound and resulted in superior wear resistance and fuel efficiency, compared to those shown by TDAE oil, because of the higher filler–rubber interactions.

This study aims to analyze tire wear particulate matter (TWP) from tread rubber with different formulations and to compare the concentration of TWP with different wear devices. The TWP generated during the abrasion of truck and bus radial (TBR) tires were examined, and the effect of using different types of rubber and carbon black (CB) were investigated. When natural rubber (NR) was solely used as the tire tread rubber material, there was a higher concentration of 5–10 µm TWP. However, when the tread formulation consisted of NR mixed with butadiene rubber, the TWP concentration decreased. Changing the type of CB also reduced the amount of TWP in the 2.5 µm size range. The TWP concentration in the specimens increased with increasing speed and vertical load. The TWP generated during the abrasion tests using wear testers and tire simulators exhibited similar trends. These findings suggest that modifying tire tread formulations can effectively control the distribution and amount of TWP generation.

The implementation of vehicle electrification and autonomous driving technologies has recently emphasized the importance of abrasion resistance and fuel efficiency of truck bus radial (TBR) tire treads that undergo high loads and long driving times. In this study, a functionalized liquid butadiene rubber (F-LqBR) was introduced to replace the treated distillate aromatic extracted (TDAE) oil as a way to improve abrasion resistance and fuel efficiency in the TBR tire tread compound and to solve the oil migration. First, radical polymerization was used to synthesize nonfunctionalized LqBR (N-LqBR) and amino-LqBR with an amine group at the chain ends. The synthesized LqBRs were then substituted in place of TDAE oil to manufacture carbon-black-filled natural rubber (NR) compounds and to evaluate their physical properties. The results show that LqBRs improved the migration resistance and enhanced the abrasion resistance by lowering the glass transition temperature (T_g) of the compound. In particular, amino-LqBR improved carbon black dispersion in the rubber matrix through a chemical bond between the functional group of the carbon black surface and the base rubber. In conclusion, amino-LqBR successfully served as a processing aid in a carbon black-filled NR compound while simultaneously enhancing its fuel efficiency and abrasion resistance.