Key message: An efficient use of thermal treatment of wood requires a depth understanding of the chemical modifications induced. This is a prerequisite to avoid problems of process control, and to provide high quality treated wood with accurately assessed properties to the market. Properties and structural anatomy of thermally modified woods are slightly different than un-processed woods from a same wood species. So it is necessary to create or adapt new analytical methods to control their quality.Context: Heat treatment as a wood modification process is based on chemical degradation of wood polymer by heat transfer. It improves mainly the resistance of wood to decay and provides dimensional stability. These improvements, which come at the expense of a weakening of mechanical properties, have been extensively studied. Since a decade, researches focused mainly on the understanding of wood thermal degradation, on modelling, on quality prediction and quality control.Aims: We aimed at reviewing the recent advances about (i) the analytical methods used to control thermal treatment; (ii) the effects on wood decay resistance and (iii) the advantages and drawbacks of a potential industrial use of wood heating.Methods: We carried out a literature review of the main industrial methods used to evaluate the conferred wood properties, by thermal treatment. We used papers and reports published between 1970 and 2015, identified in the web of science data base..Results: Approximately 100 papers mostly published after 2000 were retrieved. They concentrated on: (i) wood mass loss due to thermal degradation determination, (ii) spectroscopic analyses of wood properties, (iii) colour measurements, (iv) chemical composition, (v) non-destructive mechanical assessments and (vi) use of industrial data.Conclusions: One of most interesting property of heat-treated wood remains its decay resistance. Durability test with modified wood in laboratory are expensive and time-consuming. This review displays data from different analytical methods, such as spectroscopy, thermogravimetry, chemical analyses or mechanical tests that have the potential to be valuable indicators to assess the durability of heat treated wood at industrial scale. However, each method has its limits and drawbacks, such as the required investment for the equipment, reliability and accuracy of the results and ease of use at industrial scale.

Thermogravimetric analysis, performed on small samples of earlywood (EW) or latewood (LW), indicated that earlywood is more susceptible to thermal degradation than latewood. These results suggest a direct relationship between wood density (which depends on the EW/LW ratio and indirectly on silviculture) and the response of wood during thermo-modification processes. One of the main difficulties in developing thermo-modified wood products at an industrial scale lies in the difficulty of obtaining consistent products with a stable quality (durability, dimensional stability, color). This may be due either to the thermal treatment process itself or to inter- or intra-specific heterogeneity of wood properties. We investigated the effect of the natural variability of oak wood, particularly in density, on the degree of thermo-degradation during thermal treatments. X-ray computed tomography was used to assess the effect of initial wood density of oak boards on their thermo-degradation. Intra-ring wood density was estimated using thermogravimetric analysis and micro-densitometry. X-ray CT did not allow establishment of a clear correlation between initial wood density and mass loss due to thermo-degradation, while thermogravimetric analysis, performed separately on earlywood and latewood samples, revealed a larger susceptibility to thermal degradation of the less dense earlywood samples compared to more dense latewood samples Initial wood density, which is directly controlled by the earlywood/latewood ratio modulated by silvicultural practices, directly influences thermo-degradation during thermal treatment. Initial wood density therefore appears to be a potential parameter influencing industrial thermal treatment processes.

Wood heat treatment is an attractive alternative to improve decay resistance of wood species with low natural durability. However, this improvement of durability is realized at the expense of the mechanical resistance. Decay resistance and mechanical properties are strongly correlated to thermal degradation of wood cells wall components. Mass loss resulting from this degradation is a good indicator of treatment intensity and final treated wood properties. However, the introduction of a fast and accurate system for measuring this mass loss on an industrial scale is very difficult. Nowadays, many studies are conducted on the determination of control parameters which could be correlated with the treatment conditions and final heat treated wood quality such as decay resistance. The aim of this study is to investigate the relations between kinetics of temperature used during thermal treatment process representing heat treatment intensity, mass losses due to thermal degradation and conferred properties to heat treated wood. It might appear that relative area of treatment temperature curves is a good indicator of treatment intensity. Heat treatment with different treatment conditions (temperature-time) have been performed under vacuum, on four wood species (one hardwood and three softwoods) in order to obtain thermal degradation mass loses of 8, 10 and 12%. For each experiment, relative areas corresponding to temperature kinetics, mass loss, decay resistance and mechanical properties have been determined. Results highlight the statement that the temperature curves’ area constitutes a good indicator in the prediction of needed treatment intensity, to obtain required wood durability and mechanical properties such as bending resistance and Brinell hardness.

Green infrastructure has a role to play in climate change adaptation strategies in cities. Alternative urban spaces should be designed considering new requirements in terms of urban microclimate and thermal comfort. Pervious pavements such as green parking lots can contribute to this goal through solar evaporative cooling. However, the cooling benefits of such systems remain under debate during dry and warm periods. The aim of this study was to compare experimentally the thermal behavior of different parking lot types (PLTs) with vegetated urban soil. Four parking lots were instrumented, with temperature probes buried at different depths. Underground temperatures were measured during summer 2019, and the hottest days of the period were analyzed. Results show that the less mineral used in the surface coating, the less it warms up. The temperature difference at the upper layer can reach 10 °C between mineral and non-mineral PLTs. PLTs can be grouped into three types: (i) high surface temperature during daytime and nighttime, important heat transfer toward the sublayers, and low time shift (asphalt system); (ii) high (resp. low) surface temperature during daytime (resp. nighttime), weak heat transfer toward the sublayers, and important time shift (paved stone system); and (iii) low surface temperature during daytime and nighttime, weak heat transfer toward the sublayers, and important time shift (vegetation and substrate system, wood chips system, vegetated urban soil). The results of this study underline that pervious pavements demonstrate thermal benefits under warm and dry summer conditions compared to conventional parking lot solutions. The results also indicate that the hygrothermal properties of urban materials are crucial for urban heat island mitigation.

Condensed tannin copolymerized with hyperbranched tris(2-aminoethyl)amine-urea formed by amine-amido deamination yields a particleboard thermosetting adhesive without any aldehydes satisfying the requirements of relevant standards for the particleboard internal bond strength. The tannin–triamine–urea cures well at 180 °C, a relatively low temperature for today’s particleboard hot pressing. As aldehydes were not used, the formaldehyde emission was found to be zero, not even in traces due to the heating of wood. The effect is ascribed to the presence of many reactive sites, such as amide, amino, and phenolic groups belonging to the three reagents used. The tannin appears to function as an additional cross-linking agent, almost a nucleating agent, for the triamine–urea hyperbranched oligomers. Chemical analysis by MALDI ToF and ¹³C NMR has shown that the predominant cross-linking reaction is that of the substitution of the tannin phenolic hydroxyls by the amino groups of the triamine. The reaction of tannin with the still-free amide groups of urea is rather rare, but it may occur with the rarer tannin flavonoid units in which the heterocyclic ring is opened. Due to the temperature gradient between the surfaces and the board core in the particleboard during hot pressing, the type and the relative balance of covalent and ionic bonds in the resin structure may differ in the surfaces and the board core.