This work investigated the mechanical and electrical behaviors of piezoelectric and triboelectric energy harvesters (PEHs and TEHs, respectively) as potential devices for harvesting impact-driven energy. PEH and TEH test benches were designed and developed, aiming at harvesting low-frequency mechanical vibration generated by human activities, for example, a floor-tile energy harvester actuated by human footsteps. The electrical performance and behavior of these energy harvesters were evaluated and compared in terms of absolute energy and power densities that they provided and in terms of these energy and power densities normalized to unit material cost. Several aspects related to the design and development of PEHs and TEHs as the energy harvesting devices were investigated, covering the following topics: construction and mechanism of the energy harvesters; electrical characteristics of the fabricated piezoelectric and triboelectric materials; and characterization of the energy harvesters. At a 4 mm gap width between the cover plate and the stopper (the mechanical actuation components of both energy harvesters) and a cover plate pressing frequency of 2 Hz, PEH generated 27.64 mW, 1.90 mA, and 14.39 V across an optimal resistive load of 7.50 kΩ, while TEH generated 1.52 mW, 8.54 µA, and 177.91 V across an optimal resistive load of 21 MΩ. The power and energy densities of PEH (4.57 mW/cm³ and 475.13 µJ/cm³) were higher than those of TEH (0.50 mW/cm³, and 21.55 µJ/cm³). However, when the material cost is taken into account, TEH provided higher power and energy densities per unit cost. Hence, it has good potential for upscaling, and is considered well worth the investment. The advantages and disadvantages of PEH and TEH are also highlighted as main design factors.

In this work, we improved the electromechanical properties, electrostrictive behavior and energy-harvesting performance of poly(vinylidenefluoridene-hexafluoropropylene) P(VDF-HFP)/zinc oxide (ZnO) composite nanofibers. The main factor in increasing their electromechanical performance and harvesting power based on electrostrictive behavior is an improved coefficient with a modified crystallinity phase and tuning the polarizability of material. These blends were fabricated by using a simple electrospinning method with varied ZnO contents (0, 5, 10, 15 and 20 wt%). The effects of the ZnO nanoparticle size and content on the phase transformation, dielectric permittivity, strain response and vibration energy harvesting were investigated. The characteristics of these structures were evaluated utilizing SEM, EDX, XRD, FT-IR and DMA. The electrical properties of the fabrication samples were examined by LCR meter as a function of the concentration of the ZnO and frequency. The strain response from the electric field was observed by the photonic displacement apparatus and lock-in amplifier along the thickness direction at a low frequency of 1 Hz. Moreover, the energy conversion behavior was determined by an energy-harvesting setup measuring the current induced in the composite nanofibers. The results showed that the ZnO nanoparticles’ component effectively achieves a strain response and the energy-harvesting capabilities of these P(VDF-HFP)/ZnO composites nanofibers. The electrostriction coefficient tended to increase with a higher ZnO content and an increasing dielectric constant. The generated current increased with the ZnO content when the external electric field was applied at a vibration of 20 Hz. Consequently, the ZnO nanoparticles dispersed into electrostrictive P(VDF-HFP) nanofibers, which offer a large power density and excellent efficiency of energy harvesting.

The aim of this study was to investigate the real-world electrical parameters that strongly affected the performance of a triboelectric energy-harvesting floor tile design: triboelectric material thickness, cover plate displacement distance or gap width, and cover plate pressing frequency, so that real-world specifications of the harvesting floor tile can be accurately specified. The structure of the designed triboelectric energy harvester, with readily available polytetrafluoroethylene (PTFE) film and aluminum foil, was simple and hence easy to fabricate, and the material cost was low. A square wave was used to simulate the pressing frequency on the test bench’s cover plate. The results showed that the voltage and current were proportional to the gap width, and the thinner the triboelectric layer thickness, the higher the output voltage and current. A test bench with a 0.2 mm thick PTFE triboelectric layer generated the highest energy output. In a later experiment, a triboelectric energy-harvesting floor tile (TEHFT) prototype was constructed with 0.1 and 0.2 mm thick PTFE layers. We found that at 2 Hz stepping frequency and 0.1 mm PTFE thickness, the optimal load and cumulative energy of the TEHFT were 0.8 MΩ and 3.81 mJ, respectively, while with 0.2 mm PTFE thickness, these two parameters were 1.1 MΩ and 7.69 mJ, respectively. The TEHFT with 0.2 mm thick PTFE layer was able to illuminate a series of 100 to 150 LEDs, sufficient power to drive small electronics and sensor nodes. This discovery provides important data on the structure, material, and contact surface area of a TEHFT that can be adjusted to suit specific requirements of a special function triboelectric energy harvester.

This paper proposed a more-accurate-than-conventional measurement technique for determining electrical power across exceptionally high-impedance of triboelectric energy harvester (TEH). The key idea of this proposed technique was to measure the voltage across an introduced, parallelly-connected resistor divider to the oscilloscope instead of the voltage across the harvester. An experiment was set up to verify the measurement accuracy performance of this technique against the ideal theoretical values. The maximum percentage error found was only 2.30%, while the conventional measurement technique could not be used to measure voltage across high impedance TEH at all because the readings were not accurate, i.e., the measurement error would be at least over 10%. Therefore, we concluded that this proposed technique should always be used instead of the conventional measurement technique for power measurement of any TEH. A suggestion that we would like to offer to researchers investigating or developing a TEH is that, in using our measurement technique, a good starting point for a load to probe resistance ratio is 1:10, a ratio that worked well for our TEH test bench that we developed.

The effects of epoxide content on the microstructure and characteristics of epoxidized natural rubber (ENR) were examined. Self-crosslinking between epoxide groups possibly occurred during the vulcanization, with C-O-C linkages in the ENR. Depending on the epoxide level, the self-crosslinking in ENR improved the maximum torque, overall crosslink density and stability at elevated temperature of the rubber. With increasing epoxide content, the moduli and tensile strengthes of the ENR also increased. The highest tensile strength was achieved at 25 mol% epoxide, exceeding that of crosslinked NR by 46%. The self-crosslinking also facilitated strain-induced crystallization (SIC), reducing the onset strain of crystallization and increasing the degree of crystallinity. Even though increased epoxide content in the NR made the crosslink network distribution less homogeneous, the crosslink density increased so much that the thermomechanical and mechanical characteristics of ENR were improved. The C-O-C linkages from ENR self-crosslinking were also sufficient to boost the thermal stability, complementing the conventional sulfide links.