Biodegradable plastics can make an important contribution to the struggle against increasing environmental pollution through plastics. However, biodegradability is a material property that is influenced by many factors. This review provides an overview of the main environmental conditions in which biodegradation takes place and then presents the degradability of numerous polymers. Polylactide (PLA), which is already available on an industrial scale, and the polyhydroxyalkanoates polyhydroxybutyrate (PHB) and polyhydroxybutyrate-co-valerate (PHBV), which are among the few plastics that have been proven to degrade in seawater, will be discussed in detail, followed by a summary of the degradability of further petroleum-, cellulose-, starch-, protein- and CO₂-based biopolymers and some naturally occurring polymers.

Polylactide (PLA) is known as one of the most promising biopolymers as it is derived from renewable feedstock and can be biodegraded. During the last two decades, it moved more and more into the focus of scientific research and industrial use. It is even considered as a suitable replacement for standard petroleum-based polymers, such as polystyrene (PS), which can be found in a wide range of applications—amongst others in foams for packaging and insulation applications—but cause strong environmental issues. PLA has comparable mechanical properties to PS. However, the lack of melt strength is often referred to as a drawback for most foaming processes. One way to overcome this issue is the incorporation of chemical modifiers which can induce chain extension, branching, or cross-linking. As such, a wide variety of substances were studied in the literature. This work should give an overview of the most commonly used chemical modifiers and their effects on rheological, thermal, and foaming behavior. Therefore, this review article summarizes the research conducted on neat and chemically modified PLA foamed with the conventional foaming methods (i.e., batch foaming, foam extrusion, foam injection molding, and bead foaming).

In response to the global challenge of reducing carbon emissions and energy consumption from regulating indoor climates, we investigate the applicability of biobased cellulosic materials and bioinspired 4D-printing for weather-responsive adaptive shading in building facades. Cellulose is an abundantly available natural material resource that exhibits hygromorphic actuation potential when used in 4D-printing to emulate motile plant structures in bioinspired bilayers. Three key aspects are addressed: (i) examining the motion response of 4D-printed hygromorphic bilayers to both temperature and relative humidity, (ii) verifying the responsiveness of self-shaping shading elements in lab-generated conditions as well as under daily and seasonal weather conditions for over a year, and (iii) deploying the adaptive shading system for testing in a real building facade by upscaling the 4D-printing manufacturing process. This study demonstrates that hygromorphic bilayers can be utilized for weather-responsive facades and that the presented system is architecturally scalable in quantity. Bioinspired 4D-printing and biobased cellulosic materials offer a resource-efficient and energy-autonomous solution for adaptive shading, with potential contributions towards indoor climate regulation and climate change mitigation.

In this comprehensive study, the influence of (i) material specific properties (e.g., molecular weight, zero shear viscosity, D-content) and (ii) process parameters (e.g., saturation temperature, -time, -pressure, and pressure drop rate) on the expansion behavior during the autoclave foaming process were investigated on linear Polylactide (PLA) grades, to identify and evaluate the foam relevant parameters. Its poor rheological behavior is often stated as a drawback of PLA, that limits its foamability. Therefore, nine PLA grades with different melt strength and zero shear viscosity were systematically chosen to identify whether these are the main factors governing the foam expansion and whether there is a critical value for these rheological parameters to be exceeded, to achieve low density foams with fine cells. With pressure drop induced batch foaming experiments, it could be shown that all of the investigated PLA grades could be foamed without the often used chemical modifications, although with different degrees of expansion. Interestingly, PLAs foaming behavior is rather complex and can be influenced by many other factors due to its special nature. A low molecular weight combined with a high ability to crystallize only lead to intermediate density reduction. In contrast, a higher molecular weight (i.e., increased zero shear viscosity) leads to significant increased expandability independent from the D-content. However, the D-content plays a crucial role in terms of foaming temperature and crystallization. Furthermore, the applied process parameters govern foam expansion, cell size and crystallization.

Hydrogels are an interesting class of materials used in extrusion-based 3D printing, e.g., for drug delivery or tissue engineering. However, new hydrogel formulations for 3D printing as well as a detailed understanding of crucial formulation properties for 3D printing are needed. In this contribution, hydrogels based on poly(ethylene glycol) diacrylate (PEG-DA) and the charged monomers 3-sulfopropyl acrylate and [2-(acryloyloxy)ethyl]trimethylammonium chloride are formulated for 3D printing, together with Poloxamer 407 (P407). Chemical curing of formulations with PEG-DA and up to 5% (w/w) of the charged monomers was possible without difficulty. Through careful examination of the rheological properties of the non-cured formulations, it was found that flow properties of formulations with a high P407 concentration of 22.5% (w/w) possessed yield stresses well above 100 Pa together with pronounced shear thinning behavior. Thus, those formulations could be processed by 3D printing, as demonstrated by the generation of pyramidal objects. Modelling of the flow profile during 3D printing suggests that a plug-like laminar flow is prevalent inside the printer capillary. Under such circumstances, fast recovery of a high vicosity after material deposition might not be necessary to guarantee shape fidelity because the majority of the 3D printed volume does not face any relevant shear stress during printing.