Recent developments within the topic of biomaterials has taken hold of researchers due to the mounting concern of current environmental pollution as well as scarcity resources. Amongst all compatible biomaterials, polycaprolactone (PCL) is deemed to be a great potential biomaterial, especially to the tissue engineering sector, due to its advantages, including its biocompatibility and low bioactivity exhibition. The commercialization of PCL is deemed as infant technology despite of all its advantages. This contributed to the disadvantages of PCL, including expensive, toxic, and complex. Therefore, the shift towards the utilization of PCL as an alternative biomaterial in the development of biocomposites has been exponentially increased in recent years. PCL-based biocomposites are unique and versatile technology equipped with several importance features. In addition, the understanding on the properties of PCL and its blend is vital as it is influenced by the application of biocomposites. The superior characteristics of PCL-based green and hybrid biocomposites has expanded their applications, such as in the biomedical field, as well as in tissue engineering and medical implants. Thus, this review is aimed to critically discuss the characteristics of PCL-based biocomposites, which cover each mechanical and thermal properties and their importance towards several applications. The emergence of nanomaterials as reinforcement agent in PCL-based biocomposites was also a tackled issue within this review. On the whole, recent developments of PCL as a potential biomaterial in recent applications is reviewed.

Blends of polystyrene (PS) with polypropylene (PP) are usually developed to overcome the inherent brittleness of PS. However, PS with PP are immiscible and (in the absence of a compatibiliser) incompatible. The present study investigated the effects of styrene-b (ethylene-co-butylene)-b-styrene (SEBS) on the mechanical properties and compatibility of PS-rich PS/PP blends. Using a Brabender PL2000 twin-screw extruder, blends of PS/PP in various compositions ranging from 100-60 wt% PS with and without SEBS were prepared and injection moulded. The overall results clearly showed that the mechanical properties of PS/PP blends are dependent on blend composition (ratio of PS/PP) and SEBS content. The impact strength and elongation at break of the PS/PP blends increase with SEBS content, at the expense of tensile strength and flexural modulus. The improvements in impact strength and elongation at break with the addition of SEBS are due to the improved interfacial adhesion between the dispersed phase (PP) and matrix phase (PS). The improvement in miscibility of the PS/PP blend with the addition of SEBS is supported by DMA analysis. This showed that the 60/40 PS/PP blends possess two endothermic peaks whereas 60/40/25 PS/PP/SEBS blends have a single endothermic peak at 102 °C, indicating that they have an improved miscibility. The effectiveness of SEBS in enhancing the blends depends on the blend composition. A significant improvement was observed upon addition of more than 10 phr of SEBS into the 70/30 and 60/40 PS/PP blends, but not much improvement in the case of the 90/10 and 80/20 PS/PP blends. However, a higher SEBS content is more effective at higher PS contents, as illustrated by the 90/10/25 PS/PP/SEBS blends having higher impact strengths than 60/40/25 PS/PP/SEBS. The optimum blend, based on achieving a balance between toughness (impact strength) and stiffness (flexural modulus), is 90/10/25 PS/PP/SEBS, followed by 80/20/25 PS/PP/SEBS.