Periodontal disease and diabetes mellitus are two pathologies that are extremely widespread worldwide and share the feature of chronic inflammation. Carvacrol is a phenolic monoterpenoid, produced by a variety of herbs, the most well-known of which is Origanum vulgare. Magnolol is a traditional polyphenolic compound isolated from the stem bark of Magnolia officinalis, mainly used in Chinese medicine. The purpose of this paper is to review the therapeutic properties of these bioactive compounds, in the treatment of periodontitis and diabetes. Based on our search strategy we conducted a literature search in the PubMed and Google Scholar databases to identify studies. A total of one hundred eighty-four papers were included in the current review. The results show that carvacrol and magnolol have anti-inflammatory, antioxidant, antimicrobial, anti-osteoclastic, and anti-diabetic properties that benefit both pathologies. Knowledge of the multiple activities of carvacrol and magnolol can assist with the development of new treatment strategies, and the design of clinical animal and human trials will maximize the potential benefits of these extracts in subjects suffering from periodontitis or diabetes.

The effective recovery of wood waste generated in wood processing and also at the end of wood product life is important from environmental and economic points of view. In a laboratory, 16 mm-thick three-layer urea–formaldehyde (UF)-bonded particleboards (PBs) were produced at 5.8 MPa and 240 °C and with an 8 s/mm pressing factor, using wood particles prepared from (1) fresh spruce wood (C), (2) a mixture of several recycled wood products (R1), and (3) recycled faulty PBs bonded with UF resin (R2). Particles from spruce wood were combined with particles from R1 or R2 recyclates in weight ratios of 100:0, 80:20, 50:50 and 0:100. In comparison to the control spruce PB, the PBs containing the R1 recyclate from old wood products were characterized by lower thickness swelling after 2 and 24 h (TS-2h and TS-24h), lower by 18 and 31%; water absorption after 2 and 24 h (WA-2h and WA-24h), lower by 33 and 28%; modulus of rupture in bending (MOR), lower by 28%; modulus of elasticity in bending (MOE), lower by 18%; internal bond (IB), lower by 33%; and resistance to decay determined by the mass loss under the action of the brown-rot fungus Coniophora puteana (Δm), lower by 32%. The PBs containing the R2 recyclate from faulty PBs were also characterized by a lower TS-2h and TS-24h, lower by 45% and 59%; WA-2h and WA-24h, lower by 61% and 51%; MOR, lower by 37%; MOE, lower by 17%; and IB, lower by 33%; however, their biological resistance to C. puteana was more effective, with a decreased Δm in the decay test, lower by 44%.

The bonding of wood with assembly adhesives is crucial for manufacturing wood composites, such as solid wood panels, glulam, furniture parts, and sport and musical instruments. This work investigates 13 hardwoods—bangkirai, beech, black locust, bubinga, ipé, iroko, maçaranduba, meranti, oak, palisander, sapelli, wengé and zebrano—and analyzes the impact of their selected structural and physical characteristics (e.g., the density, cold water extract, pH value, roughness, and wettability) on the adhesion strength with the polyvinyl acetate (PVAc) adhesive Multibond SK8. The adhesion strength of the bonded hardwoods, determined by the standard EN 205, ranged in the dry state from 9.5 MPa to 17.2 MPa, from 0.6 MPa to 2.6 MPa in the wet state, and from 8.5 MPa to 19.2 MPa in the reconditioned state. The adhesion strength in the dry state of the bonded hardwoods was not influenced by their cold water extracts, pH values, or roughness parallel with the grain. On the contrary, the adhesion strength was significantly with positive tendency influenced by their higher densities, lower roughness parameters perpendicular to the grain, and lower water contact angles.

Special particleboards (PBs) proposed for kitchens, bathrooms, hospitals, and some other specific products for interiors should have a sufficient resistance against bacteria, molds, and decaying fungi. This work deals about effects of zinc oxide nanoparticles (nano‐ZnO) added into melamine‐urea‐formaldehyde (MUF) glue in the amounts of 0, 2, 6, 12, or 24% wt. on selected biological, moisture, and strength properties of laboratory‐produced one‐layer PBs. The nano‐ZnO‐treated PBs had a higher biological resistance: (1) against the Gram‐positive bacterium Staphylococcus aureus by up to ca. 70% and the Gram‐negative bacterium Escherichia coli by up to 50%, since their bacterial activities at using 1.0 McFarland bacterial inoculum decreased from 0.38–0.40 by up to 0.12–0.19 × 10⁸ CFU/ml; (2) against the molds Penicillium brevicompactum and Aspergillus niger by up to ca. 50–63%, since their growth intensities (0–4) on the top surfaces of treated PBs decreased according to a modified EN 15457 from 2.33–2.67 by up to 1.17–1.0; (3) against the brown‐rot fungus Coniophora puteana by up to 85.7%, since their weight losses reduced according to a modified ENV 12038 from 17.4% by up to 2.5%. The presence of nano‐ZnO in PBs uninfluenced their swelling, water absorption, and bending strength; however, it decreased their internal bond strength by up to 38.8%.

Worldwide production of wooden pallets continually increases, and therefore in future higher number of damaged pallets need to be recycled. One way to conveniently recycle pallets is their use for the production of particleboards (PBs). The 3-layer PBs, bonded with urea-formaldehyde (UF) resin, were prepared in laboratory conditions using particles from fresh spruce logs (FSL) and recycled spruce pallets (RSP) in mutual weight ratios of 100:0, 80:20, 50:50 and 0:100. Particles from RSP did not affect the moisture properties of PBs, i.e., the thickness swelling (TS) and water absorption (WA). The mechanical properties of PBs based on particles from RSP significantly worsened: the modulus of rupture (MOR) in bending from 14.6 MPa up to 10 MPa, the modulus of elasticity (MOE) in bending from 2616 MPa up to 2012 MPa, and the internal bond (IB) from 0.79 MPa up to 0.61 MPa. Particles from RSP had only a slight negative effect on the decay resistance of PBs to the brown-rot fungus Serpula lacrymans, while their presence in surfaces of PBs did not affect the growth activity of moulds at all.

In recent years, the production and consumption of thermally modified wood (TMW) has been increasing. Offcuts and other waste generated during TMWs processing into products, as well as already disposed products based on TMWs can be an input recycled raw material for production of particleboards (PBs). In a laboratory, 16 mm thick 3-layer PBs bonded with urea-formaldehyde (UF) resin were produced at 5.8 MPa, 240 °C and 8 s pressing factor. In PBs, the particles from fresh spruce wood and mixed particles from offcuts of pine, beech, and ash TMWs were combined in weight ratios of 100:0, 80:20, 50:50 and 0:100. Thickness swelling (TS) and water absorption (WA) of PBs decreased with increased portion of TMW particles, i.e., TS after 24 h maximally about 72.3% and WA after 24 h maximally about 64%. However, mechanical properties of PBs worsened proportionally with a higher content of recycled TMW—apparently, the modulus of rupture (MOR) up to 55.5% and internal bond (IB) up to 46.2%, while negative effect of TMW particles on the modulus of elasticity (MOE) was milder. Decay resistance of PBs to the brown-rot fungus Serpula lacrymans (Schumacher ex Fries) S.F. Gray increased if they contained TMW particles, maximally about 45%, while the mould resistance of PBs containing TMW particles improved only in the first days of test. In summary, the recycled TMW particles can improve the decay and water resistance of PBs exposed to higher humidity environment. However, worsening of their mechanical properties could appear, as well.