The bonding of wood with assembly adhesives is crucial for manufacturing wood composites, such as solid wood panels, glulam, furniture parts, and sport and musical instruments. This work investigates 13 hardwoods—bangkirai, beech, black locust, bubinga, ipé, iroko, maçaranduba, meranti, oak, palisander, sapelli, wengé and zebrano—and analyzes the impact of their selected structural and physical characteristics (e.g., the density, cold water extract, pH value, roughness, and wettability) on the adhesion strength with the polyvinyl acetate (PVAc) adhesive Multibond SK8. The adhesion strength of the bonded hardwoods, determined by the standard EN 205, ranged in the dry state from 9.5 MPa to 17.2 MPa, from 0.6 MPa to 2.6 MPa in the wet state, and from 8.5 MPa to 19.2 MPa in the reconditioned state. The adhesion strength in the dry state of the bonded hardwoods was not influenced by their cold water extracts, pH values, or roughness parallel with the grain. On the contrary, the adhesion strength was significantly with positive tendency influenced by their higher densities, lower roughness parameters perpendicular to the grain, and lower water contact angles.

The paper deals with the properties of a beech wood surface treated by CO₂ laser engraving. The studied concerns were the discoloration, changes to morphology assessed through roughness and waviness parameters, and surface wetting with standard liquids (water and diiodomethane), with the aim of determining the wood surface free energy. The results have confirmed that the studied properties of the beech wood surface varied significantly, which were affected by the laser beam power P and raster density n. With increasing P and n, the lightness L* (expressed in CIE L*a*b* color space) decreased significantly. We also observed significant variation in the color coordinates a* and b*. At 8% laser power, the roughness and waviness parameters measured parallel as well as perpendicular to the grain increased proportionally with the increasing raster density. However, 4% laser power was not associated with distinct changes. Increasing the raster density reduced beech wood surface wetting equally with water and with diiodomethane. This was reflected in the higher contact angle values. The wood surface exhibited higher hydrophobicity at 4% laser power. At this power, the increasing raster density was reflected in the decreasing surface free energy, due to its polar component decrease. At 8% laser power, the changes in surface free energy were very minor from the practical viewpoint. The results suggest a potential good adhesion between film-forming materials and wood. However, the gluing performance may be negatively affected by the high roughness attained at 8% laser power and at higher raster densities.

Spruce wood is widely used in outdoor applications, but its susceptibility to degradation under exposure to sunlight and moisture is a major concern. This study investigates the impact of accelerated aging on spruce wood’s surface chemistry, microstructure, geometry, and discoloration. The study was performed in two outdoor aging modes: dry and wet. The accelerated aging effects were evident in the changes in spruce wood structure, as well as in the other studied properties. During aging, it developed significant discoloration. Under simulated rainless outdoor conditions (dry mode), spruce wood gradually became dark brown. Under conditions involving rain (wet mode), the discoloration was qualitatively different from the dry mode. FTIR spectroscopy showed that during the accelerated aging of wood, lignin was mainly degraded, especially in the early stages of the process. A linear correlation was found between the changes in lignin and the color changes in the wood. There was an increase in carbonyl groups in the dry mode, which contributed to the color change and was also influenced by changes in extractives. The wet mode caused the leaching out of carbonyl groups. The observed decrease in cellulose crystallinity, together with the degradation of hydrophobic lignin, may result in the increased hydrophilicity of photodegraded wood. For both modes, there were different changes in the wood micro- and macrostructure, reflected in the surface morphology. The roughness increased during the aging process in both modes. The slightest changes in the roughness parameters were identified in the grain direction in the dry mode; the most evident was that the roughness parameters increased perpendicular to the grain in the wet mode. The demonstrated mechanism backing up the aging-related changes to the spruce wood structure and the relations unveiled between these changes and the changes in the spruce wood surface properties can provide an issue point for seeking ways how to mitigate the negative effects of the environmental factors the wood is exposed to.

Thermal modification improves the properties of wood, especially its stability and durability. We thermally treated spruce wood with the Thermowood process at three temperatures (160 °C, 180 °C, and 210 °C) and subjected it to accelerated aging in wet mode. We evaluated the chemical composition (wet chemistry, infrared spectroscopy), color, surface morphology, and wetting of the wood surface with water. Thermal treatment caused a significant decrease in hemicelluloses (up to 72.39% at a temperature of 210 °C), which initiated an increase in the content of more resistant wood components—cellulose and lignin. With accelerated aging, the hemicellulose content decreased by another 5%. The most significant differences between the infrared spectra of thermally modified wood before and after exposure to accelerated aging were in the absorption bands of lignin (1509 and 1596 cm⁻¹) and in the region of carbonyl groups between 1800 and 1630 cm⁻¹. Thermal treatment also caused a change in the color of the wood to dark brown; the overall color difference ΔE increased several times. The thermal-induced shortening of polysaccharide fibers and reduction in their width were even more manifested during accelerated aging. This work contains new knowledge about the properties critical for the reuse of thermally modified wood after accelerated aging, simulating the end of its life cycle.

The work investigates the effects of CO₂ laser parameters (laser power and raster density) on wood mass loss in oak wood and impacts on its morphology, chemical structure, and surface properties (colour and hydrophilicity). The energy amount supplied onto the wood surface with a laser beam under different combinations of the irradiation parameters was expressed through a single variable—total irradiation dose. The mass loss was confirmed as linear-dependent on the irradiation dose. With the mass reduction, the roughness was enhanced. The roughness parameters Ra and Rz increased linearly with the mass loss associated with the increasing irradiation dose. The FTIR (Fourier transform infrared spectroscopy) spectroscopy also detected chemical changes in the main wood components, influencing primarily the wood colour space. Conspicuous discolouration of the engraved wood surface was observed, occurring just at the minimum laser power and raster density. The additional increasing of laser parameters caused a novel colour compared to the original one. The detected dependence of wood discolouration on the total irradiation dose enables us to perform targeted discolouration of the oak wood. The engraved surfaces manifested significantly better wettability with standard liquids, both polar and non-polar, and higher surface energy values. This guarantees appropriate adhesion of film-forming materials to wood. Identification of the changes in wood surface structure and properties, induced by specific CO₂ laser-treatments, is important for obtaining targeted discolouration of the wood surface as well as for the gluing or finishing of the surfaces treated in this way.

This work appraises the influence of CO₂ laser irradiation on mass loss, morphology, chemical changes and discolouration of spruce wood surfaces. The amount of energy applied to the surface was expressed as the total irradiation dose, which was demonstrated to have a strong impact on increasing wood weight loss. Along with increasing mass loss, surface roughness also increased, resulting from the differences in density between the early wood and late wood. The evaluated roughness parameters increased linearly with increasing irradiation dose and mass loss. At the maximum irradiation dose, the Ra parameter value parallel to the fibre direction showed a 6-fold increase; perpendicular to the grain, the increase was as much as 33.5-fold. Similar differences were also observed for the parameter Rz. At the lowest laser power and the lowest raster density, the engraved spruce wood surface exhibited some evidence of discolouration (ΔE* ≅ 9). An additional increase in the amount of supplied energy clearly resulted in a novel surface colour compared to the original (ΔE* = 12). The chemical analysis of the wood surface revealed that the discolouration was mainly caused by heat-induced cleavage of C=O groups in the lignin and hemicellulose structures. Part of these structures (so-called chromophores) are responsible for the natural colour of the wood as well as for colour changes caused by engraving. The detected dependences of the wood mass loss and colour values on the total radiation dose are the basis for achieving targeted modifications of spruce wood surfaces using a laser beam.