The present work describes the effect of Ce³⁺ ion doping on the structural, morphological, and magnetic properties of spinel manganese ferrite (MnFe₂O₄) nanocrystallites (NCs) using various instrument techniques. Rare earth element (REE) Cerium (Ce³⁺) doped MnFe₂O₄ NCs were prepared by a simple microwave combustion technique. In the present scenario, ferrites are widely used for photocatalytic dye degradation and antibacterial applications. Aiming to achieve this, we prepared Ce³⁺ doped MnFe₂O₄ NCs by microwave combustion method and urea as burning agent and the obtained powder samples were characterized by powder X-ray diffraction (XRD), Fourier transform infrared (FT-IR), high resolution scanning electron microscope (HR-SEM), high resolution transmission electron microscope (HR-TEM) and vibration sample magnetometer (VSM) techniques. The pure spinel phase formation was confirmed by XRD analysis. FTIR spectra show two prominent absorption bands under 1000 cm⁻¹, which confirms the formation of the spinel structure. HR-SEM and HR-TEM pictures demonstrated a sphere-shaped morphology and also expose the combination and agglomeration of grains, which are mostly due to the magnetic characteristics of the samples. The magnetic properties of the synthesized MnCe_xFe_2−xO₄ (x = 0.0, 0.1, 0.3, and 0.5) NCs were studied by VSM analysis at room temperature (RT) shows ferromagnetic behavior. The photodegradation results showed that MnFe₂O₄ and Ce doped MnFe₂O₄ NCs have a higher potential to degrade methylene blue (MB) and the sample MnCe_0.3Fe_1.7O₄ NCs showed superb photocatalytic performance (91.53%) compared to other samples. The antibacterial activities of Gram-positive S. aureus, B. subtilis and Gram-negative K. pneumonia and E. coli were investigated using pure and Ce³⁺ substituted MnFe₂O₄ NCs and a higher activity for MnCe_0.3Fe_1.7O₄ NCs than other samples was observed, which indicated that they can be used in biomedical applications.

Two new homologues series, based on two rings of the azomethine central group bearing the terminal alkoxy group of various chain lengths, were prepared. The alkoxy chain length varied between 6 and 16 carbons. The other terminal wing in the first series was the F atom, and the compound is named N-4-florobenzylidene-4-(alkoxy)benzenamine (In). The second group of compounds included a lateral NO₂ substituent in addition to the terminal F atom, named N-(4-fluoro-3-nitrobenzylidene)-4-(alkyloxy)aniline (IIn). Mesomorphic and optical properties were carried out via differential scanning calorimetry (DSC) and polarized optical microscopy (POM). Elemental analyses, FT-IR, and NMR spectroscopy were carried out to elucidate the molecular structures of the synthesized groups. Mesomorphic investigations indicated that all the synthesized homologues (In) were monomorphic, possessing the smectic A (SmA) phase monotropically, while the second group (IIn) members were non-mesomorphic. The experimental data indicated that the formation of the mesophase is affected by the protrusion of the lateral nitro group. The disruption of the mesophase in the second group was attributed to the increase of its molecular width, which affects its lateral intermolecular interactions. The computational simulations were in agreement with the experimental data. On the other hand, the location of NO₂ group within the molecular geometry increased the melting temperature of the molecule, and thus, affected their thermal and physical properties. By discussing the estimated parameters, it was found that the molecular architecture, the dipole moment, and the polarizability of the investigated compounds are highly affected by the electronic nature and position of the terminal and lateral substituents as well as their volumes.

New complex Co(III) with ligand Pyridoxal-S-methyl-isothiosemicarbazone, (PLITSC) was synthesized. X-ray analysis showed the bis-ligand octahedral structure of the cobalt complex [Co(PLITSC-H)₂]BrNO₃·CH₃OH (compound 1). The intermolecular interactions governing the crystal structure were described by the Hirsfeld surface analysis. The structure of compound 1 and the corresponding Zn complex (([Zn(PLTSC)(H₂O)₂]SO₄·H₂O)) were optimized at the B3LYP/6–31 + G (d,p)/LanL2DZ level of theory, and the applicability was assessed by comparison with the crystallographic structure. The natural bond orbital analysis was used for the discussion on the stability of formed compounds. The antibacterial activity of obtained complexes towards S. aureus and E. coli was determined, along with the effect of compound 1 on the formation of free radical species. Activity of compound 1 towards the removal of methylene blue was also investigated. The voltammograms of these compounds showed the reduction of metal ions, as well as the catalyzed reduction of CO₂ in acidic media.

Polypyrrole (PPy) and polypyrrole/cerium oxide nanocomposite (PPy/CeO₂) were prepared by the chemical oxidative method in an aqueous medium using anhydrous ferric chloride (FeCl₃) as an oxidant. The successful formulation of materials was confirmed by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and transmittance electron microscopy (TEM). A four-in-line probe device was used for studying DC electrical conductivity and ammonia vapor sensing properties of PPy and PPy/CeO₂. The significant improvement in both the conductivity and sensing parameters of PPy/CeO₂ compared to pristine PPy reveals some synergistic/electronic interaction between PPy and cerium oxide nanoparticles (CeO₂ NPs) working at molecular levels. The initial conductivity (i.e., conductivity at room temperature) was found to be 0.152 Scm⁻¹ and 1.295 Scm⁻¹ for PPy and PPy/CeO₂, respectively. Also, PPy/CeO₂ showed much better conductivity retention than pristine PPy under both the isothermal and cyclic ageing conditions. Ammonia vapor sensing was carried out at different concentration (0.01, 0.03, 0.05, 0.1, 0.2, 0.3, 0.4, and 0.5 vol %). The sensing response of PPy/CeO₂ varied with varying concentrations. At 0.5 vol % ammonia concentration, the % sensing response of PPy and PPy/CeO₂ sensor was found to be 39.1% and 93.4%, respectively. The sensing efficiency of the PPy/CeO₂ sensor was also evaluated at 0.4. 0.3, 0.2, 0.1, 0.05, 0.03, and 0.01 vol % ammonia concentration in terms of % sensing response, response/recovery time, reversibility, selectivity as well as stability at room temperature.

In this study, zinc oxide (ZnO) as well as ZnO/GO (zinc oxide/graphene oxide) were successfully synthesized. The Carica papaya leaf extract was used to synthesize ZnO and oil palm empty fruit bunch biomass to obtain graphene, which was further used to obtain graphene oxide. The samples were characterized through a variety of analytical methods such as scanning electron microscopy, transmission electron microscopy, X-ray diffraction analysis, Fourier transform infrared spectroscopy and UV–Visible spectroscopy in order to understand their morphology, size, structural phase purity, functional groups and optical properties. Various peaks such as O-H, Zn-OH and Zn-O were found in the case of ZnO. Some additional peaks, such as C-C and C=C, were also been detected while analyzing the sample by Fourier-transform infrared spectroscopy. The results of the XRD and SEM studies demonstrated that the synthesized material shows the crystalline nature of the substance in the case of ZnO, and the crystallinity decreases for ZnO/GO. The average crystallite size was found to 80.0 nm for ZnO and 74.0 nm for ZnO/GO. Further, a red shift was shown in the case of ZnO/GO, which was indicated by the UV–Vis absorption spectrum. In the TEM analysis, the particles were shown to be nanosized. For instance, the highest number of particles was found in the range of 100 to 120 nm in the case of ZnO, while 80–100 nm sized particles were found for ZnO/GO. Using synthesized ZnO and ZnO/GO, the decolorization of methylene blue was found to be 64% and 91%, respectively.

Four new non-symmetrical derivatives based on central naphthalene moiety, 4-((4–(alkoxy)phenyl) diazenyl)naphthalen–1–yl 4–substitutedbenzoate (I_n/x), were prepared, and their properties were investigated experimentally and theoretically. The synthesized materials bear two wing groups: an alkoxy chain of differing proportionate length (n = 6 and 16 carbons) and one terminal attached to a polar group, X. Their molecular structures were elucidated via elemental analyses and FT-IR and NMR spectroscopy. Differential scanning calorimetry (DSC) and polarized optical microscopy (POM) were carried out to evaluate their mesomorphic properties. The results of the experimental investigations revealed that all the synthesized analogues possess only an enantiotropic nematic (N) mesophase with a high thermal stability and broad range. Density functional theory (DFT) calculations were in accordance with the experimental investigations and revealed that all prepared materials are to be linear and planar. Moreover, the rigidity of the molecule increased when an extra fused ring was inserted into the center of the structural shape, so its thermal and geometrical parameters were affected. Energy gap predictions confirmed that the I_16/c derivative is more reactive than other compounds.