Natural calcium phosphates derived from fish wastes are a promising material for biomedical application. However, their sintered ceramics are not fully characterized in terms of mechanical and biological properties. In this study, natural calcium phosphate was synthesized through a thermal calcination process from salmon fish bone wastes. The salmon-derived calcium phosphates (sCaP) were sintered at different temperatures to obtain natural calcium phosphate bioceramics and then were investigated in terms of their microstructure, mechanical properties and biocompatibility. In particular, this work is concerned with the effects of grain size on the relative density and microhardness of the sCaP bioceramics. Ca/P ratio of the sintered sCaP ranged from 1.73 to 1.52 when the sintering temperature was raised from 1000 to 1300 °C. The crystal phase of all the sCaP bioceramics obtained was biphasic and composed of hydroxyapatite (HA) and tricalcium phosphate (TCP). The density and microhardness of the sCaP bioceramics increased in the temperature interval 1000–1100 °C, while at temperatures higher than 1100 °C, these properties were not significantly altered. The highest compressive strength of 116 MPa was recorded for the samples sintered at 1100 °C. In vitro biocompatibility was also examined in the behavior of osteosarcoma (Saos-2) cells, indicating that the sCaP bioceramics had no cytotoxicity effect. Salmon-derived biphasic calcium phosphates (BCP) have the potential to contribute to the development of bone substituted materials.

So far, the sol-gel process has been available to prepare precursor gels of bioactive glasses with various compositions. In this report, we described a novel coating method of bioactive gels on a titanium substrate where the sol-gel transition is controlled by applying external electric fields. The application of a constant current of 10 mA/cm² in an acidic sol containing pre-hydrolyzed tetraethoxysilane, calcium nitrate, and ammonium dihydrogen phosphate led to the deposition of gels on the titanium cathodes due to the generation of OH^– by water electrolysis as a catalyst of the sol-gel transition. The obtained gels, which were characterized to be amorphous and consisted of Si, Ca, and P, covered the titanium substrates as a coating. The bioactivity of the gels deposited was confirmed by soaking in a simulated body fluid (SBF) up to 7 days, suggesting that the electrochemically assisted sol-gel process is promising for providing bioactive coatings on metallic implants. Graphical Abstract