Valorization of industrial low-value side-streams are of great interest, contributing to boosts in the circular economy. In this context, lignin side-streams of the pulp and paper industry were oxypropylated to produce biobased polyols and tested in the synthesis of rigid polyurethane (RPU) foams. E. globulus lignins, namely a lignin isolated from an industrial Kraft black liquor and depolymerized lignins obtained as by-products of an oxidation process, were used. RPU foams, synthesized with 100% lignin-based polyols and using a 1.1 NCO/OH ratio, were characterized concerning apparent density, morphology, thermal conductivity, thermal stability, and heat release rate (HRR). Foams containing the lignin-based polyols presented densities varying from 44.7 to 112.2 kg/m³ and thermal conductivity in the range of 37.2–49.0 mW/mK. For the reference foam (sample produced with 100% wt. Daltofoam TP 32015 polyol), values of 70.9 kg/m³ and 41.1 mW/mK were obtained, respectively. The achieved results point out the viability of using the generated lignin-based polyols at 100% content in RPU foams, mainly when depolymerized lignins are used. Moreover, fire retardancy was favored when the lignin-based polyols were introduced. The proposed strategies can contribute to establishing the integrated pulp and paper biorefinery concept where material synthesis (polyols and RPU foams) can be combined with chemical production (vanillin and syringaldehyde).

An investigation of two different intumescent coatings used in steel fire protection has been performed to evaluate their efficiency. A set of experimental tests is presented. They were conducted in a cone calorimeter, considering different thicknesses and heat fluxes. Among other quantities, the steel temperature and the intumescence thickness variation were measured. A numerical model for the paint decomposition is also presented. Based on the intumescence experimental value, the model is able to provide a reasonably good prediction of the steel temperature evolution.

The main goal of this study is to assess the behaviour of soil–cement blocks with incorporation of organic wastes. The problem of waste accumulation exists worldwide and has become a concern in today’s society, leading to enormous environmental damage. One of the possibilities for reducing their environmental impact is the reuse of these wastes in new materials. However, incorporating waste changes the mechanical, physical and thermal properties of the new material. In order to evaluate the potential use of waste in blocks composition, laboratory tests were conducted and the results were analysed. This article presents the fire behaviour of ecological soil–cement blocks with waste incorporation. Therefore, an experimental programme was performed using samples of wall panel with soil–cement blocks. The wall specimen under fire conditions was also analysed by a non-linear transient finite element numerical model, in time and temperature domains, and the numerical and experimental temperature fields were compared.