The NiTi alloy, known as Nitinol, represents one of the most investigated smart alloys, exhibiting a shape memory effect and superelasticity. These, among many other remarkable attributes, enable its utilization in various applications, encompassing the automotive industry, aviation, space exploration, and, notably, medicine. Conventionally, Nitinol is predominantly produced in the form of wire or thin sheets that allow producing many required components. However, the manufacturing of complex shapes poses challenges due to the tenacity of the NiTi alloy, and different processing routes at elevated temperatures have to be applied. Overcoming this obstacle may be facilitated by additive manufacturing methods. This article provides an overview of the employment of additive manufacturing methods, allowing the preparation of the required shapes of Nitinol products while retaining their exceptional properties and potential applications.

4-methylumbelliferone (4MU) has been suggested as a potential therapeutic agent for a wide range of neurological diseases. The current study aimed to evaluate the physiological changes and potential side effects after 10 weeks of 4MU treatment at a dose of 1.2 g/kg/day in healthy rats, and after 2 months of a wash-out period. Our findings revealed downregulation of hyaluronan (HA) and chondroitin sulphate proteoglycans throughout the body, significantly increased bile acids in blood samples in weeks 4 and 7 of the 4MU treatment, as well as increased blood sugars and proteins a few weeks after 4MU administration, and significantly increased interleukins IL10, IL12p70 and IFN gamma after 10 weeks of 4MU treatment. These effects, however, were reversed and no significant difference was observed between control treated and 4MU-treated animals after a 9-week wash-out period.

Scaffolds made of degradable polymers, such as collagen, polyesters or polysaccharides, are promising matrices for fabrication of bioartificial vascular grafts or patches. In this study, collagen isolated from porcine skin was processed into a gel, reinforced with collagen particles and with incorporated adipose tissue-derived stem cells (ASCs). The cell-material constructs were then incubated in a DMEM medium with 2% of FS (DMEM_part), with added polyvinylalcohol nanofibers (PVA_part sample), and for ASCs differentiation towards smooth muscle cells (SMCs), the medium was supplemented either with human platelet lysate released from PVA nanofibers (PVA_PL_part) or with TGF-β1 + BMP-4 (TGF + BMP_part). The constructs were further endothelialised with human umbilical vein endothelial cells (ECs). The immunofluorescence staining of alpha-actin and calponin, and von Willebrand factor, was performed. The proteins involved in cell differentiation, the extracellular matrix (ECM) proteins, and ECM remodelling proteins were evaluated by mass spectrometry on day 12 of culture. Mechanical properties of the gels with ASCs were measured via an unconfined compression test on day 5. Gels evinced limited planar shrinkage, but it was higher in endothelialised TGF + BMP_part gel. Both PVA_PL_part samples and TGF + BMP_part samples supported ASC growth and differentiation towards SMCs, but only PVA_PL_part supported homogeneous endothelialisation. Young modulus of elasticity increased in all samples compared to day 0, and PVA_PL_part gel evinced a slightly higher ratio of elastic energy. The results suggest that PVA_PL_part collagen construct has the highest potential to remodel into a functional vascular wall.

This paper deals with wear of intramedullary milling cutters for the drilling of nail holes used for osteosynthesis of lower limbs long bones. After the physician’s complaints about the increasing resistance and total change of its properties that are caused by the reuse the instrument, we have designed a suitable methodology to verify and quantify this problem. The experiment was carried out on three types of milling cutters, differing in their diameter. Using statistical tests, we compared pressure force and torque before and after wear.

This work investigates the NiTi shape memory alloys fabricated via laser powder-directed energy deposition (LP-DED). The properties of NiTi alloys produced by powder metallurgy or additive manufacturing routes are strongly influenced by the type of feedstock material employed. Two powder feedstocks were used for DED fabrication: a blended mixture of elemental nickel and titanium powders with a nominal chemical composition of Ni56Ti44 (wt.%) and a pre-alloyed NiTi powder containing 55.75 wt.% Ni. Samples fabricated from both types of powders were subjected to microstructural characterization, phase composition analysis, and mechanical and corrosion testing. It was found that DED processing on a non-preheated CP-Ti substrate is prone to warping and that samples deposited from the elemental Ni and Ti powder mixture exhibited pronounced inhomogeneity of microstructure and mechanical properties along the build direction, accompanied by the formation of the Ti₂Ni secondary phase. The absence of a superelastic plateau was observed in the corresponding stress–strain response. On the contrary, the samples deposited from the pre-alloyed NiTi powder exhibited a microstructure composed of B2 and B19′ phases and already demonstrated a clear superelastic response in the as-built condition during tensile loading. Based on the tensile test results, this NiTi material was used only for superelasticity testing. The superelastic behavior was further enhanced by post-deposition heat treatment, which significantly increased the recovery rate from 53% to 89%.