Soft tissue integration of dental implants lags behind natural biological integration of teeth mainly because of non-optimal surface features. Peri-implant infections resulting in loss of supporting bone jeopardize the success of implants. Our aim was to compare an anodized surface design with a turned one for a more optimal surface. Morphological and chemical structures of turned and anodized Ti surfaces (grade 5: Ti6Al4V) discs were examined by scanning electron microscopy (SEM-EDS), energy dispersive X-ray spectroscopy (EDS), and atomic force microscopy (AFM). The hydrophilic or hydrophobic features of the surfaces were determined by dynamic contact angle measurement. SEM and AFM revealed significant differences in the morphology and roughness (R_a) of the samples. Anodized discs presented a granular structure, while turned ones had circular grooves. The roughness was significantly higher for the anodized samples compared to the turned ones. XPS and EDS confirmed typical elements for both Ti6Al4V samples. Due to anodization, the amount of Ti (IV) had increased and Ti (III) had decreased in the thicker oxide layer. Anodized samples resulted in a more hydrophilic surface than the turned ones. The results suggest that the tested anodized samples present optimal surface characteristics to be used as abutment material for an optimal soft tissue integration.

Background: The purpose of this in vitro study was to compare the accuracy of implant placement in model surgeries according to the design of the drills (straight drills or step drills) used to finalize the implant bed during pilot-guided static computer-assisted implant surgery (sCAIS). Methods: Model surgeries were carried out on resin models randomly assigned to three study groups. Virtual planning software (coDiagnostiX 10.6, Dental Wings, Montreal, Canada) was used to plan the implant positions. In Groups 1 and 2, pilot-guided sCAIS was performed. Straight drills were used in Group 1, and step drills were used in Group 2 to finalize the implant beds. In Group 3, fully guided sCAIS was performed using a universal fully guided kit (RealGUIDE Full Surgical Kit 3DIEMME, RealGUIDE, Cantù, Como, Italy). A total of 90 dental implants (Callus Pro, Callus Implant Solutions GmbH, Nuremberg, Germany) were placed (six implants per model, five models per study group). The primary outcome variables (angular deviation, coronal global deviation, and apical global deviation) were calculated for all implants based on the comparison of the preoperative surgical plan with the postoperative scans. Results: Group 2 (coronal global deviation, 0.78 ± 0.29 mm; apical global deviation, 1.02 ± 0.56 mm) showed significantly lower values of both global deviation variables than Group 1 (coronal global deviation, 0.95 ± 0.20 mm; apical global deviation, 1.42 ± 0.49 mm). However, there was no significant difference in angular deviation between Groups 1 and 2 (7.56 ± 2.92° and 6.44 ± 2.84°). Group 3 produced significantly lower values of all three primary outcome variables (angular deviation, 2.36 ± 0.90°; coronal global deviation, 0.59 ± 0.28 mm; apical global deviation, 0.90 ± 0.29 mm) than Group 1 and significantly lower angular deviation and coronal global deviation values than Group 2. Conclusions: The design of the drills used to finalize implant osteotomies during pilot-guided sCAIS influences dental implant placement accuracy. Using step drills instead of straight drills for final osteotomies decreases deviation from the surgical plan. The fully guided approach performed better than the pilot-guided sCAIS.

Class II malocclusion is one of the most common dental anomalies and the use of intermaxillary elastomers is the standard method in its treatment. However, orthodontic elastics cannot exert continuous force over a period of time due to force degradation. Our goal was to mechanically characterize the different types of elastomers during static and cyclic loads, based on uniform methodology and examine the morphological changes after loading. Ten types of latex-containing and four latex-free intermaxillary elastics were examined from six different manufacturers. To determine the mechanical characteristics of the elastomers, tensile tests, cyclical tensile fatigue tests and 24 h relaxation tests were performed, and the elastics were also subjected to scanning electron microscopy (SEM) and Raman spectroscopy. Regardless of the manufacturer, the latex-containing elastomers did not show significant differences in the percentage of elongation at break during the tensile test. Only one type of latex-containing elastomer did not tear during the 24 h cyclical fatigue test. Fatigue was confirmed by electron microscopy images, and the pulling force reduced significantly. During the force relaxation test, only one latex-free ligature was torn; the force degradation was between 7.8% and 20.3% for latex ligatures and between 29.6% and 40.1% for latex-free elastomers. The results showed that dynamic loading was more damaging to ligatures than static loading, latex-containing elastomers were more resistant than latex-free elastics, and which observation could have clinical consequences or a potential effect on patient outcome.

The study evaluated the interaction of a titanium dental implant surface with three different antibacterial solutions: chlorhexidine, povidone-iodine, and chlorine dioxide. Implant surface decontamination is greatly challenging modern implant dentistry. Alongside mechanical cleaning, different antibacterial agents are widely used, though these could alter implant surface properties. Commercially pure (CP) grade 4 titanium (Ti) discs were treated with three different chemical agents (chlorhexidine 0.2% (CHX), povidone-iodine 10% (PVPI), chlorine dioxide 0.12% (ClO₂)) for 5 min. Contact angle measurements, X-ray photoelectron spectroscopy (XPS) analysis, and cell culture studies were performed. Attachment and proliferation of primary human osteoblast cells were investigated via MTT (dimethylthiazol–diphenyl tetrazolium bromide), alamarBlue, LDH (lactate dehydrogenase), and fluorescent assays. Contact angle measurements showed that PVPI-treated samples (Θ = 24.9 ± 4.1) gave no difference compared with controls (Θ = 24.6 ± 5.4), while CHX (Θ = 47.2 ± 4.1) and ClO₂ (Θ = 39.2 ± 9.8) treatments presented significantly higher Θ values. All samples remained in the hydrophilic region. XPS analysis revealed typical surface elements of CP grade 4 titanium (Ti, O, and C). Both MTT and alamarBlue cell viability assays showed similarity between treated and untreated control groups. The LDH test revealed no significant difference, and fluorescent staining confirmed these results. Although there was a difference in surface wettability, a high proliferation rate was observed in all treated groups. The in vitro study proved that CHX, PVPI, and ClO₂ are proper candidates as dental implant decontamination agents.

(1) Background: The retention of intraradicular posts is an important factor for the prognosis of endodontically treated teeth. The purpose of this study was to evaluate the push-out bond strength (PBS) of the posts relating to their diameter and region of the root. (2) Methods: A total of 40 premolar teeth (decoronated and root canal-filled) were divided into four groups (n = 10). After post-space preparation, different sizes (1.0, 1.2, 1.5, and 2.0 mm) of glass fiber posts were luted with resin cement into the root canals. After placement, 2 mm thick slices were cut from the roots according to their apical, middle, and coronal regions (n = 116). Push-out tests were carried out in a universal testing machine on each slice. A statistical evaluation of the data was applied. (3) Results: When comparing the diameter, the 2.0 mm posts had the highest PBS (111.99 ± 10.40 N), while the 1.0 mm posts had the lowest PBS (99.98 ± 8.05 N). Divided by the surface of the bonded area, the average PBS value was the highest for the 1.0 mm posts (18.20 ± 1.67 MPa) and the lowest for the 2.0 mm posts (12.08 ± 1.05 MPa). (4) Conclusions: Within the limitations of the study, when comparing the regions of the roots, no significant differences were found among the PBS values of the three regions (p = 0.219). When comparing the diameters, significant differences were shown between the PBS values of the four groups (p = 0.023 and p = 0.003, respectively).

The goal of the study was to compare the surface characteristics of typical implant materials used in orthopedic surgery and traumatology, as these determine their successful biointegration. The morphological and chemical structure of Vortex plate anodized titanium from commercially pure (CP) Grade 2 Titanium (Ti2) is generally used in the following; non-cemented total hip replacement (THR) stem and cup Ti alloy (Ti6Al4V) with titanium plasma spray (TPS) coating; cemented THR stem Stainless steel (SS); total knee replacement (TKR) femoral component CoCrMo alloy (CoCr); cemented acetabular component from highly cross-linked ultrahigh molecular weight polyethylene (HXL); and cementless acetabular liner from ultrahigh molecular weight polyethylene (UHMWPE) (Sanatmetal, Ltd., Eger, Hungary) discs, all of which were examined. Visualization and elemental analysis were carried out by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). Surface roughness was determined by atomic force microscopy (AFM) and profilometry. TPS Ti presented the highest R_a value (25 ± 2 μm), followed by CoCr (535 ± 19 nm), Ti2 (227 ± 15 nm) and SS (170 ± 11 nm). The roughness measured in the HXL and UHMWPE surfaces was in the same range, 147 ± 13 nm and 144 ± 15 nm, respectively. EDS confirmed typical elements regarding the investigated prosthesis materials. XPS results supported the EDS results and revealed a high % of Ti⁴⁺ on Ti2 and TPS surfaces. The results indicate that the surfaces of prosthesis materials have significantly different features, and a detailed characterization is needed to successfully apply them in orthopedic surgery and traumatology.