The Fused Filament Fabrication (FFF) method is an additive technology that is used for the creation of prototypes within Rapid Prototyping (RP) as well as for the creation of final components in piece or small-series production. The possibility of using FFF technology in the creation of final products requires knowledge of the properties of the material and, at the same time, how these properties change due to degradation effects. In this study, the mechanical properties of the selected materials (PLA, PETG, ABS, and ASA) were tested in their non-degenerate state and after exposure of the samples to the selected degradation factors. For the analysis, which was carried out by the tensile test and the Shore D hardness test, samples of normalized shape were prepared. The effects of UV radiation, high temperature environments, high humidity environments, temperature cycles, and exposure to weather conditions were monitored. The parameters obtained from the tests (tensile strength and Shore D hardness) were statistically evaluated, and the influence of degradation factors on the properties of individual materials was assessed. The results showed that even between individual manufacturers of the same filament there are differences, both in the mechanical properties and in the behavior of the material after exposure to degradation effects.

The presented article deals with the determination of selected mechanical properties of additive ma-terials used for 3D printing (PETG, PLA, ABS, ABS +, PLA ESD, ASA, PC / ABS). Due to the fact that 3D printing has exploded over recent years a...

Within the herein presented research, we studied the applicability of flax fabrics for composite parts in personal watercrafts in order to enhance damping of vibrations from the engine and noise reduction (which is relatively high for contemporary carbon constructions). Since the composite parts are intended to be exposed to humid environments requiring high levels of mechanical properties, a carbon–flax composite was selected. Samples of carbon, fiberglass, flax, and hybrid carbon–flax twill and biax fabrics were subjected to tensile and three-point bending tests. The mechanical properties were also tested after exposure of the samples to a humid environment. Damping was assessed by vibration and noise measurements directly on the complete float for samples as well as real parts. The hybrid carbon–flax material exhibited lower values of tensile strength than the carbon material (760 MPa compared to 463 MPa), but, at the same time, significantly higher than the other tested materials, or flax itself (115 MPa for a twill fabric). A similar trend in the results was observed for the three-point bending tests. Vibration tests and noise measurements showed reductions in vibration amplitude and frequency when using the carbon–flax hybrid material; the frequency response function for the watercraft part assembled from the hybrid material was 50% lower than for that made of carbon. Testing of samples located in a humid environment showed the necessity of surface treatment to prevent moisture absorption (mechanical properties were reduced at minimum by 28%). The tests confirmed that the hybrid material is satisfactory in terms of strength and its contribution to noise and vibration damping.

In this study, the research on 316L steel manufactured additively using two commercially available techniques, Material Extrusion (MEX) and Laser Powder Bed Fusion of Metals (PBF-LB/M), were compared. The additive manufacturing (AM) process based on powder bed synthesis is of great interest in the production of metal parts. One of the most interesting alternatives to PBF-LB/M, are techniques based on material extrusion due to the significant initial cost reduction. Therefore, the paper compares these two different methods of AM technologies for metals. The investigations involved determining the density of the printed samples, assessing their surface roughness in two printing planes, examining their microstructures including determining their porosity and density, and measuring their hardness. The tests carried out make it possible to determine the durability, and quality of the obtained sample parts, as well as to assess their strength. The conducted research revealed that samples fabricated using the PBF-LB/M technology exhibited approximately 3% lower porosity compared to those produced using the MEX technology. Additionally, it was observed that the hardness of PBF-LB/M samples was more than twice as high as that of the samples manufactured using the MEX technology.

The influence of plasma nitriding and gas nitriding processes on the change of surface roughness and dimensional accuracy of 42CrMo4 steel was investigated in this paper. Both processes almost always led to changes in the surface texture. After plasma nitriding, clusters of nitride ions were formed on the surface of steel, while gas nitriding very often led to the new creation of a formation of a “plate-like” surface texture. In both cases of these processes, a compound layer in specific thickness was formed, although the parameters of the processes were chosen with the aim of suppressing it. After the optimizing of nitriding parameters during nitriding processes, it was found that there were no changes in the surface roughness evaluated using the Ra parameter. However, it turned out that when using a multi-parameter evaluation of roughness (the parameters Rz, Rsk and Rku were used), there were presented some changes in roughness due to nitriding processes, which affect the functional behavior of the components. Roughness changes were also detected by evaluating surface roughness profiles, where nitriding led to changes in peak heights and valley depths. Nitriding processes further led to changes in dimensions in the form of an increase of 0.032 mm on average. However, the magnitude of the change has some context on chemical composition of material. A larger increase in dimensions was found with gas nitriding. The change in the degree of IT accuracy is closely related to the change in dimension. For both processes, there was a change of one degree of IT accuracy compared to the ground part (from IT8 to IT9). On the basis of the achieved dimensional accuracy results, a coefficient of change in the degree of accuracy IT was created, which can be used to predict changes in the dimensional accuracy of ground surfaces after nitriding processes in degrees of accuracy IT3–IT10. In this study, a tool for predicting changes in degrees of accuracy of ground parts after nitriding processes is presented.

Carburizing is used in applications where there is a high demand for surface hardness and abrasion resistance along with core toughness requirements. Carburizing is mainly used for parts which are subjected to abrasion, such as shafts, pins, g...