The study investigated the effects of the addition of starch on the properties of oil palm biomass particleboard bonded with citric acid. Three kinds of oil palm biomasses were used in this study for the fabrication of particleboard, namely, oil palm frond (OPF), oil palm trunk (OPT), and empty fruit bunch (EFB) particles. Citric acid and tapioca starch at the mixing ratios of 100:0, 87.5:12.5, and 75:25 were prepared at a 60% solid content. A 30% resin content based on the oven-dried weight of the oil palm biomass particles was used. The sprayed particles were pre-dried at 80 °C for 12 h before being hot-pressed at 180 °C and 4 MPa pressure for 10 min. The physical and mechanical properties of the particleboard were evaluated. The mixtures of citric acid and tapioca starch were characterized by thermogravimetric analysis (TGA). Thermal stability of citric acid was reduced after the addition of tapioca starch. The addition of 12.5% tapioca starch improved the bending strength of the particleboard but increased the thickness swelling slightly. All UF-bonded particleboard exhibited significantly inferior performance than that of citric-acid-bonded particleboard. Citric-acid-bonded particleboard maintained its original shape after being subjected to a cyclic-aging treatment, while the UF-bonded particleboard disintegrated half way through the treatment. The performance of EFB particleboard was significantly inferior to its OPT and OPF counterparts.

Intensive land expansion of commercial oil palm agricultural lands results in reducing the size of peat swamp forests, particularly in Southeast Asia. The effect of this land conversion on macrofungal biodiversity is, however, understudied. We quantified macrofungal biodiversity by identifying mushroom sporocarps throughout four different habitats; logged peat swamp forest, large‐scale oil palm plantation, monoculture, and polyculture smallholdings. We recorded a total of 757 clusters of macrofungi belonging to 127 morphospecies and found that substrates for growing macrofungi were abundant in peat swamp forest; hence, morphospecies richness and macrofungal clusters were significantly greater in logged peat swamp forest than converted oil palm agriculture lands. Environmental factors that influence macrofungi in logged peat swamp forests such as air temperature, humidity, wind speed, soilpH, and soil moisture were different from those in oil palm plantations and smallholdings. We conclude that peat swamp forests are irreplaceable with respect to macrofungal biodiversity. They host much greater macrofungal biodiversity than any of the oil palm agricultural lands. It is imperative that further expansion of oil palm plantation into remaining peat swamp forests should be prohibited in palm oil producing countries. These results imply that macrofungal distribution reflects changes in microclimate between habitats and reduced macrofungal biodiversity may adversely affect decomposition in human‐modified landscapes.

In this study, the effects of stem canker disease caused by Chrysoporthe deuterocubensis on the chemical properties and durability of a Eucalyptus hybrid (E. urophylla x E. grandis) were investigated. Eleven-year-old healthy and infected trees were collected. The samples were grouped into four different classes based on the infection severity: healthy (class 1), moderately infected (class 2), severely infected (class 3), and very severely infected (class 4). The changes in chemical properties were evaluated via chemical analysis and Fourier transform infrared spectroscopy (FTIR) analysis. A resistance test against fungal decay (Pcynoporus sanguineus and Caniophora puteana) and termite (Coptotermes curvignathus) was also performed. The results showed that reductions in cellulose and hemicellulose content from 53.2% to 45.4% and 14.1% to 13.9%, respectively, were observed in the infected samples. Meanwhile, the percentages of lignin and extractives increased from 18.1% to 20.5% and 14.6% to 20.2%, respectively. The resistance against fungi and termites varied between severity classes. Generally, infected wood behaved better than healthy wood in terms of durability against fungi and termites. The durability classes for both tests were significantly improved, from resistant to highly resistant and poor to moderately resistant, respectively. These results suggest that E. urograndis that is infected by C. deuterocubensis might have a better potential use in lumber production with regard to its durability and processing cost compared to pulp and paper products.