Polyaniline/graphene oxide (PANI-GO) fibrous nanocomposites have been prepared and the electrochemical catalytic activity towards the electro-oxidation of ascorbic acid (AA), Dopamine (DA) and Uric acid (UA) has been investigated. The nanocomposites were synthesized via an in situ chemical polymerization method. The morphology, composition, thermal and electrochemical properties of the resulting nanocomposites were characterized by scanning electron microscopy, X-ray diffraction, Raman spectroscopy, FT-IR spectroscopy, thermo gravimetric analysis and cyclic voltammetry. The catalytic behavior of PANI-GO nanocomposite modified glassy carbon electrode (GCE) towards AA, DA and UA has been investigated by cyclic voltammetry (CV), differential pulse voltammetry (DPV). The PANI-GO/GCE showed excellent catalytic activity towards electrochemical oxidation of AA, DA and UA compared to the bare GCE. The electrochemical oxidation signal of AA, DA and UA are well separated into three distinct peaks with peak potential separation of 343 mV, 145 mV and 488 mV between AA-DA, DA-UA and AA-UA respectively in CV studies and the corresponding peak potential separation in DPV mode are 320 mV, 230 mV and 550 mV. Under the optimized DPV experimental conditions, the peak current of AA, DA and UA give linear response over the range of 25–200 μM (R² = 0.9955), 2–18 μM (R² = 0.9932) and 2–18 μM (R² = 0.9902) with detection limit of 20 μM, 0.5 μM and 0.2 μM at S/N = 3, respectively. The attractive features of PANI-GO provide potential applications in the simultaneous detection of AA, DA and UA. The excellent electrocatalytic behavior of PANI-GO may lead to new applications in electrochemical analysis.

Recently, polymeric graphitic carbon nitride (g-C₃N₄) has been explored as a potential catalytic material for the removal of organic pollutants in wastewater. In this work, graphitic carbon nitride (g-C₃N₄) photocatalysts were synthesized using mixtures of low-cost, environment-friendly urea and thiourea as precursors by varying calcination temperatures ranging from 500 to 650 °C for 3 h in an air medium. Different analytical methods were used to characterize prepared g-C₃N₄ samples. The effects of different calcination temperatures on the structural, morphological, optical, and physiochemical properties of g-C₃N₄ photocatalysts were investigated. The results showed that rhodamine B (RhB) dye removal efficiency of g-C₃N₄ prepared at a calcination temperature of 600 °C exhibited 94.83% within 180 min visible LED light irradiation. Photocatalytic activity of g-C₃N₄ was enhanced by calcination at higher temperatures, possibly by increasing crystallinity that ameliorated the separation of photoinduced charge carriers. Thus, controlling the type of precursors and calcination temperatures has a great impact on the photocatalytic performance of g-C₃N₄ towards the photodegradation of RhB dye. This investigation provides useful information about the synthesis of novel polymeric g-C₃N₄ photocatalysts using a mixture of two different environmentally benign precursors at high calcination temperatures for the photodegradation of organic pollutants.

Room temperature (RT) synthesis of the ternary cesium lead bromide CsPbBr₃ quantum dots with oleic acid and oleylamine ligands was developed by Zeng and coworkers in 2016. In their works, the supersaturated recrystallization (SR) was adopted as a processing method without requiring inert gas and high-temperature injection. However, the oleic acid ligand for haloplumbate is known to be relatively unstable. Hence, in this work, we employed the eco-friendly olive oil to replace the oleic acid portion for the SR process at RT. Resultantly, we found that the cube-shaped nanocrystal has a size of ~40–42 nm and an optical bandgap of ~2.3 eV independent of the surface ligands, but the photoluminescence lifetime (τ_av) and crystal packing are dependent on the ligand species, e.g., τ_av = 3.228 ns (olive oil and oleylamine; here less ordered) vs. 1.167 ns (oleic acid and oleylamine). Importantly, we explain the SR mechanism from the viewpoint of the classical LaMer model combined with the solvent engineering technique in details.