Compositing is an interesting strategy that has always been employed to introduce or enhance desired functionalities in material systems. In this paper, sponges containing polypropylene, lignin, and octavinyl-polyhedral oligomeric silsesquioxane (OV-POSS) were successfully prepared via an easy and elegant strategy called thermally induced phase separation (TIPS). To fully explore the behaviour of different components of prepared sponges, properties were characterized by a thermogravimetric analyser (TGA), differential scanning calorimetry (DSC), Fourier transform infrared measurement (FTIR), and scanning electron microscopy (SEM). Furthermore, wettability properties toward an organic liquid and oil were investigated. The FTIR analysis confirmed the chemical modification of the components. TGA and DSC measurements revealed thermal stability was much better with an increase in OV-POSS content. OV-POSS modified sponges exhibited ultra-hydrophobicity and high oleophilicity with water contact angles of more than 125°. The SEM revealed that POSS molecules acted as a support for reduced surface roughness. Moreover, OV-POSS-based blend sponges showed higher sorption capacities compared with other blend sponges without OV-POSS. The new blend sponges demonstrated a potential for use as sorbent engineering materials in water remediation.

Recently, the natural dyeing process has achieved great importance in the textile wet processing industry due to its clean dyeing, eco-friendliness, and nontoxicity in nature. In the above research project, a unique natural dye extracted from dragon fruit was applied to wool fabric using various mordanting agents to encourage the use of natural dyes and lessen the negative environmental effects caused by synthetic dyeing. The color characteristics (K/S), fastness properties, Fourier transform infrared spectroscopy (FTIR), absorption spectra, and thermal and ultraviolet (UV) resistance of the extracted dye and dyed wool samples were tested and characterized. The K/S values of the dyed wool fabrics were between 5.75 and 13.29. The color fastness ratings obtained from the dyed wool fabric were found to be between good and excellent. Hence, the overall results proved that the novel natural dye obtained from dragon fruit can be utilized for dyeing wool material for the production of eco-friendly and sustainable antimicrobial textiles.

The interest in multifunctional textile materials has been increased due to the health and safety measures of living beings, especially in severe conditions. Therefore, this study investigated the hydrophobicity, oil sorption capacity, and bending properties of untreated or uncoated and treated or coated 3D weft-knitted spacer fabric samples (92% polyester/8% spandex), i.e. sample 1, sample 2, and sample 3, having thicknesses of 2 mm (300 gm⁻²), 3 mm (350 gm⁻²), and 4 mm (540 gm⁻²), with silica aerogels (SAs) through the sol-gel method. SEM, FTIR-ATR, and surface roughness test of fabric samples were analyzed to comprehend the influence of SAs. The experimental results revealed the excellent hydrophobicity and oleophilicity of all the treated 3D weft-knitted spacer fabric samples, providing a higher water contact angle (CA) 142 ± 0.84° and an oil sorption capacity 7.51 ± 0.08g/g and 6.88 ± 0.06g/g for vegetable oil and engine oil, especially of sample 2 owing to the most silica particles. The statistical analysis also demonstrated a significant performance (P < 0.05) of treated spacer fabric samples at the 0.05 level. Thus, these fabrics are suitable for an industrial application of hydrophobic and oleophilic properties.