Graphene quantum dots is a class of graphene nanomaterials with exceptional luminescence properties. Precise dimension control of graphene quantum dots produced by chemical synthesis methods is currently difficult to achieve and usually provides a range of sizes from 3 to 25 nm. In this work, fullerene C₆₀ is used as starting material, due to its well-defined dimension, to produce very small graphene quantum dots (∼2–3 nm). Treatment of fullerene C₆₀ with a mixture of strong acid and chemical oxidant induced the oxidation, cage-opening, and fragmentation processes of fullerene C₆₀. The synthesized quantum dots were characterized and supported by LDI-TOF MS, TEM, XRD, XPS, AFM, STM, FTIR, DLS, Raman spectroscopy, and luminescence analyses. The quantum dots remained fully dispersed in aqueous suspension and exhibited strong luminescence properties, with the highest intensity at 460 nm under a 340 nm excitation wavelength. Further chemical treatments with hydrazine hydrate and hydroxylamine resulted in red- and blue-shift of the luminescence, respectively.

Graphene oxide composites with photocatalysts may exhibit better properties than pure photocatalysts via improvement of their textural and electronic properties.

Nanometric particles of pure brookite TiO₂ were synthesized by modified thermolysis of reactant solutions containing titania powder, HCl, urea and PEG 10000. Unique flower-like brookite agglomerates with an average diameter of ∼400–450 nm composed of single brookite nanocrystals of ∼4–5 nm were obtained at 105 °C. The brookite → rutile transformation has been studied and TiO₂ mixtures with variable amount of anatase, brookite and rutile polymorphs at different temperatures (from 200 to 800 °C) were obtained. High resolution transmission electron microscopy (HRTEM), electron diffraction pattern and BET/BJH analyses were used to characterize the phase assemblages, crystallite size and pore volume of the pure-phase brookite and TiO₂ mixtures. In order to understand the metastable–stable TiO₂ phase transformation X-ray powder diffraction (XRD) was performed. The photoactivity of pure brookite and TiO₂ powders with different compositions of the brookite–anatase–rutile and anatase–rutile polymorphs obtained during the transitions was examined by photocatalyzed degradation of 4-chlorophenols in aqueous solution. The titania sample having the highest catalytic activity was obtained at 500 °C, contained 3.2% brookite, 42.9% anatase and 53.9% rutile and is referred to as TiO[B])/500 .