Graphene oxide composites with photocatalysts may exhibit better properties than pure photocatalysts via improvement of their textural and electronic properties.

Here, the comparison of two different semiconductor materials is demonstrated, TiO₂ and melem/g-C₃N₄ composites—modified with balls of approximately 5 nm Ag nanoparticles (NPs) as photocatalysts for the degradation of the model dye acid orange 7 (AO7). The melem molecule synthesized here is one of a series of organic compounds consisting of triazine ring compounds with a structure similar to that of melam and melamine. The photodegradation process of AO7 was carried out to examine all powder materials as a potential photocatalyst. Additionally, two different lamps of wavelengths 368 nm (UV light) and 420 nm (VIS light) were applied to compare the photodegradation tests. A new synthesis route for the acquisition of Ag NPs (Ag content 0.5, 1.0 and 2.5 wt%), based on a wet and low temperature method without the use of reducing reagents was proposed. The best photocatalytic performances under UV and VIS light were obtained for both, TiO₂ and melem/g-C₃N₄ materials (new synthesis route) modified with a very low Ag content—0.5 wt%. The photodegradation activities using UV lamp (3 h, 368 nm irradiation) for samples with 0.5 wt% of Ag: TiO₂ and melem/g-C₃N₄, in excess of 95 and 94%, respectively, were achieved. The highest photoactive materials melem/g-C₃N₄ with 0.5 and 1 wt% Ag revealed 98% of activity under the VIS lamp after 3 h long irradiation. Our work demonstrates a novel, environmentally acceptable, and cost-effective chemical strategy for preparation of photocatalysts suitable for degradation of organic contaminants in wastewater treatment.

The work aims at improving photocatalytic activity of titania under Vis light irradiation using modification by Sn ions and an original, simple synthesis method. Tin-doped titania catalysts were prepared by thermal hydrolysis of aqueous solutions of titanium peroxo-complexes in the presence of SnCl4 or SnCl2 using an original, proprietary "one pot" synthesis not employing organic solvents, metallo-organic precursors, autoclave aging nor post-synthesis calcination. The products were characterized in details by powder diffraction, XPS, UV-vis, IR, and Raman spectroscopies, electron microscopy and surface area and porosity measurements The presence of tin in synthesis mixtures favors the formation of rutile and brookite at the expense of anatase, decreases the particle size of all formed titania polymorphs, and extends light absorption of titania to visible light region >400 nm by both red shift of the absorption edge and introduction of new chromophores. The photocatalytic activity of titania under UV irradiation and >400 nm light was tested by decomposition kinetics of Orange II dye in aqueous solution Doping by Sn improves titania photoactivity under UV light and affords considerable photoactivity under >400 nm light due to increased specific surface area and a phase heterogeneity of the Sn-doped titania powders.