Nanometric particles of pure brookite TiO₂ were synthesized by modified thermolysis of reactant solutions containing titania powder, HCl, urea and PEG 10000. Unique flower-like brookite agglomerates with an average diameter of ∼400–450 nm composed of single brookite nanocrystals of ∼4–5 nm were obtained at 105 °C. The brookite → rutile transformation has been studied and TiO₂ mixtures with variable amount of anatase, brookite and rutile polymorphs at different temperatures (from 200 to 800 °C) were obtained. High resolution transmission electron microscopy (HRTEM), electron diffraction pattern and BET/BJH analyses were used to characterize the phase assemblages, crystallite size and pore volume of the pure-phase brookite and TiO₂ mixtures. In order to understand the metastable–stable TiO₂ phase transformation X-ray powder diffraction (XRD) was performed. The photoactivity of pure brookite and TiO₂ powders with different compositions of the brookite–anatase–rutile and anatase–rutile polymorphs obtained during the transitions was examined by photocatalyzed degradation of 4-chlorophenols in aqueous solution. The titania sample having the highest catalytic activity was obtained at 500 °C, contained 3.2% brookite, 42.9% anatase and 53.9% rutile and is referred to as TiO[B])/500 .

The thermal decomposition of hydrotalcite (HT), with chemical composition Mg_1-xAl_x(OH)₂(CO₃)_x/2.(1-3x/2)H₂O, (0.20 < x ≤ 0.33), is a complex sequence of dehydration, dehydroxylation and decarbonization and leads to the formation of a series of metaphases: HT-D (dehydrated HT), HT-B (partially dehydroxylated HT) and MO (mixed oxides with periclase-like structure). The evolution of water and CO₂ in natural and synthetic hydrotalcites (a Mg/Al ratio between 2:1and 3.7:1), heated to 800°C, was investigated by differential thermal analysis, thermogravimetry and evolved gas analysis. At least six endothermic and two exothermic effects were established by computer-aided resolving of the curves. The formation of each HT metaphase was related to the release of a discrete number of water molecules depending on the Al content in the samples and each appeared as a corresponding endothermic peak in the DTA curves. The exothermic processes associated with the crystallization of HT-B and MO metaphases were specified by decomposition of DTA curves. The evolution of CO₂ during the thermal decomposition of the carbonate groups was found to be different for the samples studied. The preservation of CO₃ even at high temperatures was established for synthetic samples with a high Al content. The release of volatile H₂O and CO₂ (which comprise ~40% of the sample mass) provokes fine cracking both along and across the layers.

The purpose of the study was to investigate the stability and biopharmaceutical characteristics of ketoprofen, loaded in polymeric carriers, which were included into a bigel in a semisolid dosage form. The polymer carriers with in situ-included ketoprofen were obtained by emulsifier-free emulsion polymerization of the monomers in aqueous medium or a solution of the polymers used. The morphological characteristics of the carriers, the in vitro release and the photochemical stability of ketoprofen were evaluated. The model with optimal characteristics was included in a bigel formulation. The bigel was characterized in terms of pH, rheological behavior, spreadability, and in vitro drug release. Acute skin toxicity, antinociceptive activity, anti-inflammatory activity, and antihyperalgesic effects of the prepared bigel with ketoprofen-loaded polymer carrier were evaluated. The carriers of ketoprofen were characterized by a high yield and drug loading. The particle size distribution varied widely according to the polymer used, and a sustained release was provided for up to 6 hours. The polymer mixture poly(vinyl acetate) and hydroxypropyl cellulose as a drug carrier, alone or included in the bigel composition, improved the photostability of the drug compared with unprotected ketoprofen. The bigel with ketoprofen-loaded particles provided sustained release of the drug and had optimal rheological parameters. In vivo experiments on the bigel showed no skin inflammation or irritation. Four hours after its application, a well-defined analgesic, anti-inflammatory, and antihyperalgesic effect was registered. The polymer mixture of poly(vinyl acetate) and hydroxypropyl cellulose as a carrier of ketoprofen and the bigel in which it was included provided an enhanced photostability and sustained drug release.