Lately, in orthodontic treatments, the use of transparent aligners for the correction of malocclusions has become prominent owing to their intrinsic advantages such as esthetics, comfort, and minimal maintenance. Attempts at improving upon this technology by varying various parameters to investigate the effects on treatments have been carried out by several researchers. Here, we aimed to investigate the biomechanical and clinical effects of aligner thickness on stress distributions in the periodontal ligament and changes in the tooth’s center of rotation. Dental finite element models comprising the cortical and cancellous bones, gingiva, teeth, and nonlinear viscoelastic periodontal ligaments were constructed, validated, and used together with aligner finite element models of different aligner thicknesses to achieve the goal of this study. The finite element analyses were conducted to simulate the actual orthodontic aligner treatment process for the correction of malocclusions by generating pre-stresses in the aligner and allowing the aligner stresses to relax to induce tooth movement. The results of the analyses showed that orthodontic treatment in lingual inclination and axial rotation with a 0.75 mm-thick aligner resulted in 6% and 0.03% higher principal stresses in the periodontal ligament than the same treatment using a 0.05 mm-thick aligner, respectively. Again, for both aligner thicknesses, the tooth’s center of rotation moved lingually and towards the root direction in lingual inclination, and diagonally from the long axis of the tooth in axial rotation. Taken together, orthodontic treatment for simple malocclusions using transparent aligners of different thicknesses will produce a similar effect on the principal stresses in the periodontal ligament and similar changes in the tooth’s center of rotation, as well as sufficient tooth movement. These findings provide orthodontists and researchers clinical and biomechanical evidence about the effect of transparent aligner thickness selection and its effect on orthodontic treatment.

Objectives. This biomechanical study was conducted to compare fixation stability of the proximal fragments and their mechanical characteristics in proximal femur models of unstable basicervical IT fractures fixed by cephalomedullary nailing using 3 different types of the femoral head fixation.Methods. A total of 36 composite femurs corresponding to osteoporotic human bone were used. These specimens were fixed with Gamma 3 (hip screw type; group 1) in 12, Gamma 3 U-blade (screw-blade hybrid type; group 2) in 12, and proximal femoral nail antirotation-II (helical blade type; group 3) in 12, respectively, and an unstable basicervical IT fracture was created by an engraving machine. After preloading and cyclic loading, the migration of the proximal fragment according to 3 axes was assessed by the stereophotogrammetric method and the migration of screw or blade tip within the femoral head was measured radiographically. Next, the vertical load was continued at a speed of 10 mm/min until the construct failure occurred. Finite element analysis was additionally performed to measure the stress and compressive strain just above the tip of screw or blade within the femoral head.Results. The rotational change of the proximal fragment according to the axis of screw or blade was much greater in group 1 than in groups 2 and 3 (p=0.016 and p=0.007, respectively). Varus collapse was greater in group 3 than in group 2 (p=0.045). Cranial and axial migration of screw or blade within the femoral head were significantly greater in group 3 than in both group 1 (p=0.001 and p=0.002, respectively) and group 2 (p=0.002 and p=0.016, respectively). On finite element analysis, group 3 showed the highest peak von-Mises stress value (13.3 MPa) and compressive strain (3.2%) just above the tip of the blade within the femoral head. Meanwhile, groups 1 and 2 showed similar results on two values.Conclusions. Screw-blade hybrid type and blade type would be more effective in minimizing rotation instability of the proximal fragment in unstable basicervical IT fractures. However, varus collapse of the proximal fragment and cranial and axial migration within the femoral head were greater with blade type than screw-blade hybrid type.

Incidents of lumbar degenerative diseases, such as spinal stenosis and degenerative spondylolisthesis, are increasing due to the aging population, and as a result, posterior lumbar interbody fusion (PLIF) is widely used. However, the interbody fusion cage used in the fusion surgery has been reported to cause subsidence in the fusion cage of the titanium material and bone nonunion in the case of the polyetheretherketone (PEEK) material cage. Therefore, we aim to reduce the possibility of subsidence of the spinal fusion cage through its elastic modulus difference with the cortical bone of the vertebral body. For the vertebral end plate, which is related to the fusion rate, we also aim to design a new composite vertebral cage, which integrates a cover of porous structure using the additive manufacturing method of titanium alloy to fabricate a prototype, and to biomechanically verify the prototype. The method was as follows. In order to find a similar pore size of human cancellous bone, the pore size was adjusted and the results were measured with SEM. The pore size of each surface was measured individually and the mean value was calculated. Next, an animal experiment was conducted to confirm the degree of fusion of each structural type, and prototypes of various structures were fabricated. The degree of fusion was confirmed by a push down test. A prototype of the fusion cage composed of titanium and PEEK material was fabricated, and the possibility of subsidence by existence of porous structure was confirmed by using the lumbar spine finite element model. Then, the prototype was compared with the composite fusion cage developed by ASTM F2077 and ASTM F2267 methods, and with the commercial PEEK and titanium cages. As a result, the correlation between bone fusion and the porous structure, as well as size of the spine fusion cage composing the composite for porous structure and elasticity, was confirmed. Type 3 structures showed the best performance in bone fusion and the pore size of 1.2 mm was most suitable. In addition, the likelihood of subsidence of a cage with a porous structure was considered to be lower than that of a cage with a solid structure. When the new composite cage combined with two composites was compared with commercial products to verify, the performance was better than that of the existing PEEK material. The subsidence result was superior to the titanium product and showed similar results to PEEK products. In conclusion, the performance value was superior to the existing PEEK material, and the subsidence result was superior to the titanium product and was similar to the PEEK product, and thus, performance-wise, it is concluded that the PEEK product can be completely replaced with the new product.