Novel 2D Ti₃C₂T_x (MXene)-reinforced polyvinyl alcohol (PVA) nanofibers have been successfully fabricated by an electrospinning technique. The high aspect ratio, hydrophilic surfaces, and metallic conductivity of delaminated MXene nanosheet render it promising nanofiller for high performance nanocomposites. Cellulose nanocrystals (CNC) were used to improve the mechanical properties of the nanofibers. The obtained electrospun nanofibers had diameter from 174 to 194 nm depending on ratio between PVA, CNC and MXene. Dynamic mechanical analysis demonstrated an increase in the elastic modulus from 392 MPa for neat PVA fibers to 855 MPa for fibers containing CNC and MXene at 25°C. Moreover, PVA nanofibers containing 0.14 wt. % Ti₃C₂T_x exhibited dc conductivity of 0.8 mS/cm conductivity which is superior compared to similar composites prepared using methods other than electrospinning. Improved mechanical and electrical characteristics of the Ti₃C₂T_x /CNC/PVA composites make them viable materials for high performance energy applications.

A novel flexible nanocomposite pressure sensor with a tensile strength of about 47 MPa is fabricated in this work. Nanolayers of titanium dioxide (titania nanolayers, TNL) synthesized by hydrothermal method are used to reinforce the polyvinylidene fluoride (PVDF) by simple solution mixing. A hybrid composite is prepared by incorporating the TNL (2.5 wt %) with reduced graphene oxide (rGO) (2.5 wt %) synthesized by improved graphene oxide synthesis to form a PVDF/rGO-TNL composite. A comparison between PVDF, PVDF/rGO (5 wt %), PVDF/TNL (5 wt %) and PVDF/rGO-TNL (total additives 5 wt %) samples are analyzed for their sensing, thermal and dielectric characteristics. The new shape of additives (with sharp morphology), good interaction and well distributed hybrid additives in the matrix increased the sensitivity by 333.46% at 5 kPa, 200.7% at 10.7 kPa and 246.7% at 17.6 kPa compared to the individual PVDF composite of TNL, confirming its possible application in fabricating low cost and light weight pressure sensing devices and electronic devices with reduced quantity of metal oxides. Increase in the β crystallinity percentage and removal of α phase for PVDF was detected for the hybrid composite and linked to the improvement in the mechanical properties. Tensile strength for the hybrid composite (46.91 MPa) was 115% higher than that of the neat polymer matrix. Improvement in the wettability and less roughness in the hybrid composites were observed, which can prevent fouling, a major disadvantage in many sensor applications.

Nanomaterials have emerged as the new future generation materials for high-performance water treatment membranes with potential for solving the worldwide water pollution issue. The incorporation of nanomaterials in membranes increases water permeability, mechanical strength, separation efficiency, and reduces fouling of the membrane. Thus, the nanomaterials pave a new pathway for ultra-fast and extremely selective water purification membranes. Membrane enhancements after the inclusion of many nanomaterials, including nanoparticles (NPs), two-dimensional (2-D) layer materials, nanofibers, nanosheets, and other nanocomposite structural materials, are discussed in this review. Furthermore, the applications of these membranes with nanomaterials in water treatment applications, that are vast in number, are highlighted. The goal is to demonstrate the significance of nanomaterials in the membrane industry for water treatment applications. It was found that nanomaterials and nanotechnology offer great potential for the advancement of sustainable water and wastewater treatment.