Highly sensitive silver (Ag) modified zinc oxide (ZnO) humidity sensors were prepared by hydrothermal synthesis and the mechanism was studied. Experimental results show that Ag-modified ZnO can effectively enhance the performance of a humidity sensor. Large number of oxygen vacancies and many active sites are generated on the surface when molar ratio of Ag⁺ to Zn²⁺ is 1:100, which can accelerate the decomposition of water molecules on surface of the material, thereby improving the response of humidity sensor. Moreover, the linearity of ZnO humidity sensor is greatly improved by silver nanoparticles. Compared with previously reported ZnO-based humidity sensors, Ag/ZnO humidity sensors have a better response (151,700%), good linearity, low hysteresis (3%), and short response/recovery time (36/6 s). At the same time, it is found that the light had little effect on the performance of Ag/ZnO. Therefore, this kind of ZnO sensor with stable performance and excellent performance is expected to be used in the detection of relative humidity in conventional environments.

Oxyhalides, containing oxygen and halogen atoms and combining the advantages of oxides and halides in geometry and optical response, have great potential in optical materials. In this study, the electronic structures and the optical properties of the Pb₃O₂X₂ (X = Cl, Br, I) compounds have been investigated using the first principles method. The results show that these compounds have birefringence at 0.076, 0.078, and 0.059 @ 1064 nm, respectively. And, the asymmetric stereochemical active lone pair electrons were found around lead atoms, which were confirmed by the projected density of states, the electronic localization functions, and the crystal orbitals. The contribution of atoms and polyhedra to birefringence was further evaluated using the Born effective charge. The results show that halogen atoms give negative contribution, and lead—oxygen polyhedra give positive contribution. The spin—orbit coupling effect is also investigated, and the downshift of the conduction band and variation in the valence band are found after relevant spin—orbit coupling (SOC), which leads to a reduction in the band gap and birefringence.