The aim of this study was to assess the effect of different remineralizing agents on enamel microhardness (KHN) and surface topography after an erosive challenge. Forty-eight human enamel specimens (4 × 4 mm) were randomly assigned to 4 groups: control (no treatment), fluoride varnish, calcium nanophosphate paste and casein phosphopeptide-amorphous calcium phosphate paste (CPP-ACP). Both pastes were applied for 5 minutes, and fluoride varnish, for 24 h. Four daily erosive cycles of 5 minutes of immersion in a cola drink and 2 h in artificial saliva were conducted for 5 days. KHN readings were performed at baseline and after 5 days. The percentage of enamel hardness change (%KHN) was obtained after erosion. The surface topography was evaluated by atomic force microscopy (AFM). The data were tested using ANOVA, Tukey's and paired-T tests (p < 0.05). After an erosive challenge, there was no statistically significant difference between the control (96.8 ± 11.4 KHN / 72.4 ± 3.0 %KHN) and the varnish (91.7 ± 14.1 KHN / 73.4 ± 5.5 %KHN) groups. The nanophosphate group showed lower enamel hardness loss (187.2 ± 27.9 / 49.0 ± 7.9 %KHN), compared with the CPP-ACP group (141.8 ± 16.5 / 60.6 ± 4.0 %KHN), and both were statistically different from the varnish and the control groups. AFM images showed a rough surface for the control and the varnish groups, a non-homogeneous layer with globular irregularities for CPP-ACP, and a thick homogeneous layer for the nanophosphate group. None of the agents provided protection against the development of erosion; however, nanophosphate paste was able to reduce enamel surface softening after the erosive challenge

After gas atomization, a quasicrystalline powder based on aluminium was used to prepare a thick coating by high-velocity oxygen-fuel flame torch spraying. This layer was deposited on top of a bond-coat layer on a steel plate. A post-spraying annealing treatment turned the two layers to their stable state, a γ-brass crystal and an icosahedral quasicrystal, respectively. The projection parameters were selected in such a way that the coating behaved like a self-lubricating material, which offered very good wear resistance (duration of pin-on-disk tests superior to 5 km with negligible material loss) and low friction (µ ≤ 6% against sintered tungsten carbide), in contrast to the state of the art. This property was achieved thanks to, on the one hand, excellent bonding to the substrate via the bound coat, and on the other hand, presence at the boundaries between quasicrystalline flakes of a mixture of both threefold and fourfold coordinated carbon originating from spray processing. Application to hard materials used in mechanical devices is appealing, especially because soft, lubricating additives may not be needed, thus considerably increasing the lifetime of the devices and reducing waste of materials.

As solar radiation is the most plentiful energy source on earth, thermoelectric energy harvesting emerges as an interesting solution for the Internet of Things (IoTs) in outdoor applications, particularly using semiconductor thermoelectric generators (TEGs) to power IoT devices. However, when a TEG is under solar radiation, the temperature gradient through TEG is minor, meaning that the TEG is useless. A method to keep a significant temperature gradient on a TEG is by using a solar absorber on one side for heating and a heat sink on the other side. In this paper, a compact TEG-based energy harvester that features a solar absorber based on a new class of solid matter, the so-called quasicrystal (QC), is presented. In addition, a water-cooled heat sink to improve the temperature gradient on the TEG is also proposed. The harvester is connected to a power management circuit that can provide an output voltage of 3 V and store up to 1.38 J in a supercapacitor per day. An experimental evaluation was carried out to compare the performance of the proposed QC-based harvester with another similar harvester but with a solar absorber based on conventional black paint. As a result, the QC-based harvester achieved 28.6% more efficient energy generation and achieved full charge of a supercapacitor around two hours earlier. At last, a study on how much the harvested energy can supply power to a sensor node for Smart agriculture during a day while considering a trade-off between the maximum number of measurements and the maximum number of transmission per day is presented.

Objective: To test the hypothesis that treatment time, debris/biofilm, and oral pH have an influence on the physical-chemical properties of orthodontic brackets and arch wires. Materials and Methods: One hundred twenty metal brackets were evaluated. They were divided into four groups (n = 30) according to treatment time: group C (control) and groups T12, T24, and T36 (brackets recovered after 12, 24, and 36 months of treatment, respectively). Rectangular stainless-steel arch wires that remained in the oral cavity for 12 to 24 months were also analyzed. Dimensional stability, surface morphology, composition of brackets, resistance to sliding of the bracket-wire set, surface roughness of wires, and oral pH were analyzed. One-way analysis of variance, followed by a Tukey multiple comparisons test, was used for statistical analysis ( P < .05). Results: Carbon and oxygen were shown to be elements that increased expressively and in direct proportion to time, and there was a progressive increase in the coefficient of friction and roughness of wires as a function of time of clinical use after 36 months. Oral pH showed a significant difference between group T36 and its control ( P = .014). Conclusions: The hypothesis was partially accepted: treatment time and biofilm and debris accumulation in bracket slots were shown to have more influence on the degradation process and frictional force of these devices than did oral pH.