This article presents a review on the recent advances in the field of ternary diglycidyl ether of bisphenol A epoxy nanocomposites containing nanoparticles and other modifiers. Particular attention is paid to their mechanical and thermal properties. The properties of epoxy resins were improved by incorporating various single toughening agents, in solid or liquid states. This latter process often resulted in the improvement in some properties at the expense of others. The use of two appropriate modifiers for the preparation of hybrid composites, possibly will show a synergistic effect on the performance properties of the composites. Due to the huge amount of modifiers that were used, the present paper will focus mainly on largely employed nanoclays with modifiers in a liquid and solid state. The former modifier contributes to an increase in the flexibility of the matrix, while the latter modifier is intended to improve other properties of the polymer depending on its structure. Various studies which were carried out on hybrid epoxy nanocomposites confirmed the occurrence of a synergistic effect within the tested performance properties of the epoxy matrix. Nevertheless, there are still ongoing research works using other nanoparticles and other modifiers aiming at enhancing the mechanical and thermal properties of epoxy resins. Despite numerous studies carried out so far to assess the fracture toughness of epoxy hybrid nanocomposites, some problems still remain unresolved. Many research groups are dealing with many aspects of the subject, namely the choice of modifiers and preparation methods, while taking into account the protection of the environment and the use of components from natural resources.

The aim of our research was to investigate the effect of a small nanocellulose (NC) addition on an improvement of the mechanical properties of epoxy composites. A procedure of chemical extraction from pressed lignin was used to obtain nanocellulose fibers. The presence of nanoparticles in the cellulose pulp was confirmed by FTIR/ATR spectra as well as measurement of nanocellulose particle size using a Zetasizer analyzer. Epoxy composites with NC contents from 0.5% to 1.5% w/w were prepared. The obtained composites were subjected to strength tests, such as impact strength (IS) and resistance to three-point bending with a determination of critical stress intensity factor (Kc). The impact strength of nanocellulose composites doubled in comparison to the unmodified epoxy resin (EP 0). Moreover, Kc was increased by approximately 50% and 70% for the 1.5 and 0.5% w/w NC, respectively. The maximum value of stress at break was achieved at 1% NC concentration in EP and it was 15% higher than that for unmodified epoxy resin. The highest value of destruction energy was characterized by the composition with 0.5% NC and corresponds to the increase of 102% in comparison with EP 0. Based on the analysis of the results it was noted that satisfactory improvement of the mechanical properties of the composite was achieved with a very small addition of nanofiller while other research indicates the need to add much more nanocellulose. It is also expected that this kind of use of raw materials will allow increasing the economic efficiency of the nanocomposite preparation process. Moreover, nanocomposites obtained in this way can be applied as elements of machines or as a modified epoxy matrix for sandwich composites, enabling production of the structure material with reduced weight but improved mechanical properties.

The paper presents results of investigations on the binderless nanostructured tungsten carbide (WC) cutting tools fabrication and performance. The scientific novelty includes the description of some regularities of the powder consolidation under electric current and the subsequent possibility to utilize them for practical use in the fabrication of cutting tools. The sintering process of WC nanopowder was performed with the electroconsolidation method, which is a modification of spark plasma sintering (SPS). Its advantages include low temperatures and short sintering time which allows retaining nanosize grains of ca. 70 nm, close to the original particle size of the starting powder. In respect to the application of the cutting tools, pure WC nanostructure resulted in a smaller cutting edge radius providing a higher quality of TiC/Fe machined surface. In the range of cutting speeds, v_c = 15–40 m/min the durability of the inserts was 75% of that achieved by cubic boron nitride ones, and more than two times better than that of WC-Co cutting tools. In additional tests of machining 13CrMo4 material at an elevated cutting speed of v_c = 100 m/min, binderless nWC inserts worked almost three times longer than WC-Co composites.

Fabrication of alumina–tungsten carbide nanocomposite was investigated. Characteristics of the densification and sintering were analyzed considering both the nano-size particle starting powders and the processing stages. Different heating rates were generated during densification and consolidation with a maximal load was applied only after a temperature of 1000 °C was reached. Due to the varying dominance of different physical processes affecting the grains, appropriate heating rates and pressure at different stages ensured that a structure with submicron grains was obtained. With directly applied alternating current, it was found that the proportion Al₂O₃ (50 wt.%)–WC provided the highest fracture toughness, and a sintering temperature above 1600 °C was found to be disadvantageous. High heating rates and a short sintering time enabled the process to be completed in 12 min, saving energy and time.