New methods of diffusion metallization of AISI W1-7 steel have been developed. The paper proposes a comparative analysis of the properties and characteristics of AISI W1-7 steel after three methods of chemical heat treatment: diffusion nitriding, nitrogen titration by physical deposition from the gas phase, and diffusion chromium plating with subsequent titanium alloys. The results are presented as a comprehensive analysis of coatings: metallographic, micro-X-ray spectral, X-ray phase, durometric, heat resistance, and wear resistance. It is established that multilayer protective coatings are formed as a result of treatments. It is shown that the coatings consist of carbide and nitride zones, intermetallic, and an Al₂O₃ layer outside the coating. The coatings have been found to contain barrier layers that prevent aluminum from penetrating the substrate. The maximum microhardness is typical for layers based on titanium carbide—30.3–35.5 GPa and titanium nitride—22.0–22.6 GPa, heat-resistant steels AISI W1-7 at a temperature of 900 °C in 4.2–8.5 times and wear resistance under sliding friction without lubrication up to 5.4 times compared to samples without treatment.

The study examined the influence of ion-plasma nitriding on the structure, mechanical, and tribological properties of high-speed steels AISI M2 and AISI M41. A comprehensive study was conducted on the changes in phase composition, microhardness, and wear resistance of the obtained modified layers. It was established that the optimal approach was the formation of high-nitrogen martensite without excessive nitrides, which ensured improved mechanical properties of the steels. The dependence of the nitrided layer depth and its microhardness on nitriding temperature and duration was investigated. It was found that at a temperature of 480–520 °C and a processing duration of up to 1 h, a hardened layer with a depth of 25–40 μm was formed, exhibiting increased wear resistance and microhardness of up to 10–12 GPa. The analysis of structural transformations confirmed the presence of ε and γ’ phases, which contributed to increased strength and reduced friction coefficient. The obtained results can be used to improve the technological processes of heat treatment for high-speed steels used in the production of cutting tools. The proposed nitriding parameters contribute to extending the service life of steel components, which is relevant for the mechanical engineering and metallurgical industries.

The analysis of various methods of machining of rope internal thread ISO 10208, DIN 20317 has been carried out and the criteria of high-efficiency machining have been formulated. The concept of the method has been developed, which supposes the designing of the construction of noncore tool and the calculation of the parameters of mechanical trajectory with the purpose of ensuring the machining per one pass on the computer numerical control (CNC) milling machine. The compensation procedure of dimensional wear of insert has been developed. While machining the production batch of the parts in an experimental way, the optimum cutting conditions have been determined which allow ensuring the maximum efficiency on reaching the required roughness and the dimensional accuracy of the profile of rope thread. The performed statistical analysis of the machined parts allowed to establish that dispersions of the actual values of profiles' roughness follow Gauss' law. In an experimental way, it has been proved that the application of the proposed method increased the efficiency of machining of the internal rope thread by 2.5 times. On the basis of comparison of engineering-and-economical performance, the efficient fields of application of high-efficient method of machining of the rope threads have been determined.

This article explores the issue of surface modification through tumbling and vaporisation of 3D-printed materials, and its impact on the electrolytic deposition of metal coatings on previously non-conductive materials. Plastic materials represent an affordable alternative, but their surface treatment, in the form of post-coating, achieves properties comparable to those of metal parts while saving expensive metal material. Samples prepared by selective laser sintering (SLS) with different surface treatments were used. Polyamide 12 (PA12) was chosen as the base material and copper (Cu) as the metallic coating. Graphite was sprayed on the samples to ensure conductivity. The Cu coating was electrodeposited from an acidic copper electrolyte. The quantitative analysis of the surface was carried out using standard ISO parameters. The thickness of the deposited copper layer was determined using destructive measurements on a digital microscope. The results show that surface modification has a significant effect on the functional properties of the surface quality and the thickness of the deposited copper layer.