Recent trends to improve the aesthetic properties—tooth-like color and translucency—of ceramic dental crowns have led to the development of yttria-stabilized zirconia (Y-TZP) materials with higher stabilizer content. These 5Y-TZP materials contain more cubic or t’ phase, which boosts translucency. The tradeoff as a consequence of a less transformable tetragonal phase is a significant reduction of strength and toughness compared to the standard 3Y-TZP composition. This study aims at determining the durability of such 5Y-TZP crowns under lab conditions simulating the conditions in the oral cavity during mastication and consumption of different nutrients. The test included up to 10,000 thermal cycles from 5 °C to 55 °C “from ice cream to coffee” and a chewing simulation representing 5 years of use applying typical loads. The investigation of the stress-affected zone at the surface indicates only a very moderate phase transformation from tetragonal to monoclinic after different varieties of testing cycles. The surface showed no indication of crack formation after testing. It can, therefore, be assumed that over the simulated period, dental crowns of 5Y-TZP are not prone to fatigue failure.

Cobalt alloys are widely used in biomedicine, implantology, and dentistry due to their high corrosion resistance and good mechanical properties. The high carbon improves the wear properties, but causes fragility and dangerous cracking of elements during use. The aim of the present work was to analyze and compare the structure and wear resistance of Co-based alloy samples with low carbon content, produced by Selective Laser Sintering (SLS) and Powder Injection Molding (PIM). Structure characterization, mainly with the use of transmission electron microscopy, was applied to investigate the differences in tribological properties. The better resistance to abrasive wear for SLS was explained by the presence of a hard, intermetallic phase, present as precipitates limited in size and evenly distributed in the cobalt matrix. The second factor was the structure of the cobalt matrix, with dominant content of the hexagonal phase. By combining the characteristic features of the matrix and the reinforcing phase, the analyzed material gains an additional advantage, namely a higher resistance to abrasive wear.

The main purpose of the research was to analyze the influence of surface modification of the cobalt-based alloy used in dental prosthetics by applying zirconium oxide (ZrO₂) layers using the ALD (Atomic Layer Deposition) method. The samples were made using the DMLS (Direct Metal Laser Sintering) technique, and their surfaces were prepared in accordance with the principles of removable partial dentures (RPDs). A 50 nm-thick zirconium oxide coating was applied to the prepared substrates. This paper deals with the issues of prosthetic stomatopathy, which is a complex of pathological changes occurring in approx. 40% of the Polish population using removable dentures. Often, these changes, occurring on the mucosa, are related to improper performance, allergic reactions or the multiplication of bacteria on the surface of partial dentures. An innovative method of surface modification was proposed, together with the analysis of its influence on the physicochemical properties of the alloy and the adhesion of bacteria to the surface.