Recently, research into the factors that influence the formation and growth of intermetallic compounds (IMCs) layer in lead-free solders has piqued interest, as IMCs play an important role in solder joints. The reliability of solder joints is critical to the long-term performance of electronic products. One of the most important factors which are known to influence solder joint reliability is the intermetallic compound (IMC) layer formed between the solder and the substrate. Although the formation of an IMC layer signifies good bonding between the solder and substrate, its main disadvantage is due to its brittle nature. This paper reviews the formation and growth of IMCs in lead-free solder joints detailing the effect of alloying additions, surface finishes, aging time, aging temperature and solder volume. The formation and growth of the brittle IMCs were significantly affected by these factors and could be possibly controlled. This review may be used as a basis in understanding the major factors effecting the IMC formation and growth and relating it to the reliability of solder joints.

This paper elucidates the effect of isothermal ageing at temperature of 85 °C, 125 °C and 150 °C for 100, 500 and 1000 h on Sn-3.0Ag-0.5Cu (SAC305) lead-free solder with the addition of 1 wt% kaolin geopolymer ceramic (KGC) reinforcement particles. SAC305-KGC composite solders were fabricated through powder metallurgy using a hybrid microwave sintering method and reflowed on copper substrate printed circuit board with an organic solderability preservative surface finish. The results revealed that, the addition of KGC was beneficial in improving the total thickness of interfacial intermetallic compound (IMC) layer. At higher isothermal ageing of 150 °C and 1000 h, the IMC layer in SAC305-KGC composite solder was towards a planar-type morphology. Moreover, the growth of total interfacial IMC layer and Cu₃Sn layer during isothermal ageing was found to be controlled by bulk diffusion and grain-boundary process, respectively. The activation energy possessed by SAC305-KGC composite solder for total interfacial IMC layer and Cu₃Sn IMC was 74 kJ/mol and 104 kJ/mol, respectively. Based on a lap shear test, the shear strength of SAC305-KGC composite solder exhibited higher shear strength than non-reinforced SAC305 solder. Meanwhile, the solder joints failure mode after shear testing was a combination of brittle and ductile modes at higher ageing temperature and time for SAC305-KGC composite solder.

Solder interconnection in three-dimensional (3D) electronic packaging is required to undergo multiple reflow cycles of the soldering process. This paper elucidates the effects of multiple reflow cycles on the solder joints of Sn-3.0Ag-0.5Cu (SAC305) lead (Pb)-free solder with the addition of 1.0 wt.% kaolin geopolymer ceramics (KGC). The samples were fabricated using powder metallurgy with the hybrid microwave sintering method. Apart from using conventional cross-sectioned microstructure imaging, advanced synchrotron real-time in situ imaging was used to observe primary IMC formation in SAC305-KGC solder joints subjected to multiple reflow soldering. The addition of KGC particles in SAC305 suppressed the Cu₆Sn₅ IMC’s growth as primary and interfacial layers, improving the shear strength after multiple reflow soldering. The growth rate constant for the interfacial Cu₆Sn₅ IMC was also calculated in this study. The average growth rate of the primary Cu₆Sn₅ IMCs decreased from 49 µm/s in SAC305 to 38 µm/s with the addition of KGC particles. As a result, the average solidified length in the SAC305-KGC is shorter than SAC305 for multiple reflow soldering. It was also observed that with KGC additions, the growth direction of the primary Cu₆Sn₅ IMC in SAC305 changed from one growth to two growth directions. The observed results can be attributed to the presence of KGC particles both at grains of interfacial Cu₆Sn₅ IMCs and at the surface of primary Cu₆Sn₅ IMC.

This paper reviews the impact of the thermal ageing and multiple reflow to the intermetallic compound (IMC) layer and mechanical performance of lead free solder reinforced with various reinforcements. Based on available literatures it had been proved that, the IMC layer and mechanical properties can be affected with the exposure of different temperatures and time. Besides that, the incorporation of the reinforcement in the matrix of solder alloys could improve the thickness of IMC layer and strength of the solder joints although it had been subjected to thermal ageing and multiple reflow cycles as compared to unreinforced solder. Therefore, the composite solder system could be possibly applied and adapted in current electronic devices even with the exposure of high temperatures.