Plasma technology has been widely used to increase the surface energy of the polymer surfaces for many industrial applications; in particular to increase in wettability. The present work was carried out to investigate how surface modification using plasma treatment modifies the surface energy of micro-injection moulded microneedles and its influence on drug delivery. Microneedles of polyether ether ketone and polycarbonate and have been manufactured using micro-injection moulding and samples from each production batch have been subsequently subjected to a range of plasma treatment. These samples were coated with bovine serum albumin to study the protein adsorption on these treated polymer surfaces. Sample surfaces structures, before and after treatment, were studied using atomic force microscope and surface energies have been obtained using contact angle measurement and calculated using the Owens-Wendt theory. Adsorption performance of bovine serum albumin and release kinetics for each sample set was assessed using a Franz diffusion cell. Results indicate that plasma treatment significantly increases the surface energy and roughness of the microneedles resulting in better adsorption and release of BSA.

Shape memory polymers with surface micropatterns have seen rising demand for high value applications such as adjustable adherence surfaces, dynamic micro-geometries for cell culture studies and switchable information carriers. Recently, microinjection molding has emerged as an efficient way to manufacture devices which contain surface micro-features using a wide range of polymers with high accuracy. In this study, shape memory polyurethane–carbon nanotube composites were prepared by twin-screw melt extrusion and subsequently processed using microinjection molding to obtain components with surface micropatterns. Then an electro-activated surface micropattern tuning system was developed which could recover the original micropatterned surface of the components after a thermal deformation by applying a current which heats the component using resistive heating. In order to optimize the technique, three key areas were investigated in this work: conductivity of the microinjection molded microparts, the retention of shape memory micropatterns on the surface of microparts during annealing treatment, and the macroscopic area shrinkage of microparts after thermal treatment. It has been found that the electrical conductivity of microinjection molded parts is relatively low due to the high shear rates prevalent in the process. An annealing treatment improves the electrical conductivity by several orders of magnitude, but can be detrimental to the dimensional stability of the micropatterns, which depends significantly on the micro-injection molding parameters, especially the mold temperature. Increasing the mold temperature, melt temperature, injection speed and injection pressure result in better retention of the micropattern and improved dimension stability during annealing treatment. This work demonstrates the potential of electro-activated surface micropattern control for microinjection molded electrically conductive shape memory polymer composites, which could be a promising technology for a range of application areas including electro-adjustable adherence, information storage, and anti-counterfeiting technology.

YesThe present work deals with the flow-induced multiple orientations and crystallization structure of polymer melts under a complex flow field. This complex flow field is characteristic of the consistent coupling of extensional “pulse” and closely followed shear flow in a narrow channel. Utilizing an ingenious combination of an advanced micro-injection device and long chain aliphatic polyamides (LCPA), the flow-induced crystallization morphology was well preserved for ex-situ synchrotron micro-focused wide angle X-ray scattering (μWAXS) as well as small angle X-ray scattering (SAXS). An inverted anisotropic crystallization structure was observed in two directions: perpendicular and parallel to the flow direction (FD). The novel anisotropic morphology implies the occurrence of wall slip and “global” fountain flow under the complex flow field. The mechanism of structure formation is elucidated in detail. The experimental results clearly indicate that the effect of extensional pulse on the polymer melt is restrained and further diminished due to either the transverse tumble of fountain flow or the rapid retraction of stretched high molecular weight tails. However, the residual shish-kebab structures in the core layer of the far-end of channel suggest that the effect of extensional pulse should be considered in the small-scaled geometries or under the high strain rate condition.Early online publication on 22 Jul 2015

Shape memory polymer (SMP) products have been developed for application as crack closure devices in concrete. They have been made from PET in the form of both fibres and hollow tubes. Here, manufacturing methods using die-drawing and mandrel-drawing to induce shape memory are reported. The fibre-based devices are incorporated into concrete and, upon triggering, exert shrinkage restraint forces that close cracks in the concrete. The evolution of shrinkage restraint force in the fibres as manufactured was measured as a function of temperature, showing stresses in excess of 35 MPa. Tendons consisting of fibre bundles are incorporated into concreate beams subjected to controlled cracking. When activated, the tendons reduce the crack widths by 80%. The same fibres are used to produce another class of device known as knotted fibres, which have knotted ends that act as anchor points when they incorporated directly into concrete. Upon activation within the cracked concrete, these devices are shown to completely close cracks. The tubes are used to enclose and restrain prestressed Kevlar fibres. When the tubes are triggered, they shrink and release the prestress force in the Kevlar, which is transferred to the surrounding concrete in the form of a compressive force, thereby closing cracks. The Kevlar fibres also provide substantial reinforcement after activation. The devices are shown to be able to partially and fully close cracks that have been opened to 0.3 mm and achieve post-activation flexural strengths comparable to those of conventional reinforced and prestressed structural elements. Finally, a preliminary life cycle assessment study was used to assess the carbon footprint a nominal unit of concrete made with SMPs fibres compared to conventional concrete.

Gold on polydimethylsiloxane (PDMS) stretchable conductors were prepared using a novel approach by interlacing an hydrogenated amorphous carbon (a-C : H) layer between the deposited metal layer and the elastomer. AFM analysis of the a-C : H film surface before gold deposition shows nanoscale buckling, the corresponding increase in specific surface area corresponds to a strain compensation for the first 4–6% of bi-axial tensile loading. Without this interlayer, the deposited gold films show much smaller and uni-directional ripples as well as more cracks and delaminations. With a-C : H interlayer, the initial electrical resistivity of the metal film decreases markedly (280-fold decrease to 8 × 10⁻⁶ Ω cm). This is not due to conduction within the carbon interlayer; both a-C : H/PDMS and PDMS substrates are electrically insulating. Upon cyclic tensile loading, both films become more resistive, but return to their initial state after 20 tensile cycles up to 60% strain. Profiling experiments using secondary ion mass spectroscopy and x-ray photoelectron spectroscopy indicate that the a-C : H layer intermixes with the PDMS, resulting in a graded layer of decreasing stiffness. We believe that both this graded layer and the surface buckling contribute to the observed improvement in the electrical performance of these stretchable conductors.