Polymeric hydrogels are a complex class of materials with one common feature—the ability to form three-dimensional networks capable of imbibing large amounts of water or biological fluids without being dissolved, acting as self-sustained containers for various purposes, including pharmaceutical and biomedical applications. Transdermal pharmaceutical microneedles are a pain-free drug delivery system that continues on the path to widespread adoption—regulatory guidelines are on the horizon, and investments in the field continue to grow annually. Recently, hydrogels have generated interest in the field of transdermal microneedles due to their tunable properties, allowing them to be exploited as delivery systems and extraction tools. As hydrogel microneedles are a new emerging technology, their fabrication faces various challenges that must be resolved for them to redeem themselves as a viable pharmaceutical option. This article discusses hydrogel microneedles from a material perspective, regardless of their mechanism of action. It cites the recent advances in their formulation, presents relevant fabrication and characterization methods, and discusses manufacturing and regulatory challenges facing these emerging technologies before their approval.

Plasma technology has been widely used to increase the surface energy of the polymer surfaces for many industrial applications; in particular to increase in wettability. The present work was carried out to investigate how surface modification using plasma treatment modifies the surface energy of micro-injection moulded microneedles and its influence on drug delivery. Microneedles of polyether ether ketone and polycarbonate and have been manufactured using micro-injection moulding and samples from each production batch have been subsequently subjected to a range of plasma treatment. These samples were coated with bovine serum albumin to study the protein adsorption on these treated polymer surfaces. Sample surfaces structures, before and after treatment, were studied using atomic force microscope and surface energies have been obtained using contact angle measurement and calculated using the Owens-Wendt theory. Adsorption performance of bovine serum albumin and release kinetics for each sample set was assessed using a Franz diffusion cell. Results indicate that plasma treatment significantly increases the surface energy and roughness of the microneedles resulting in better adsorption and release of BSA.

Shape memory polymers with surface micropatterns have seen rising demand for high value applications such as adjustable adherence surfaces, dynamic micro-geometries for cell culture studies and switchable information carriers. Recently, microinjection molding has emerged as an efficient way to manufacture devices which contain surface micro-features using a wide range of polymers with high accuracy. In this study, shape memory polyurethane–carbon nanotube composites were prepared by twin-screw melt extrusion and subsequently processed using microinjection molding to obtain components with surface micropatterns. Then an electro-activated surface micropattern tuning system was developed which could recover the original micropatterned surface of the components after a thermal deformation by applying a current which heats the component using resistive heating. In order to optimize the technique, three key areas were investigated in this work: conductivity of the microinjection molded microparts, the retention of shape memory micropatterns on the surface of microparts during annealing treatment, and the macroscopic area shrinkage of microparts after thermal treatment. It has been found that the electrical conductivity of microinjection molded parts is relatively low due to the high shear rates prevalent in the process. An annealing treatment improves the electrical conductivity by several orders of magnitude, but can be detrimental to the dimensional stability of the micropatterns, which depends significantly on the micro-injection molding parameters, especially the mold temperature. Increasing the mold temperature, melt temperature, injection speed and injection pressure result in better retention of the micropattern and improved dimension stability during annealing treatment. This work demonstrates the potential of electro-activated surface micropattern control for microinjection molded electrically conductive shape memory polymer composites, which could be a promising technology for a range of application areas including electro-adjustable adherence, information storage, and anti-counterfeiting technology.

Inspired from the low wetting properties of Lotus leaves, the fabrication of dual micro/nanoscale topographies is of interest to many applications. In this research, superhydrophobic surfaces are fabricated by a process chain combining ultrashort pulsed laser texturing of steel inserts and injection molding to produce textured polypropylene (PP) parts. This manufacturing route is very promising and could be economically viable for mass production of polymeric parts with superhydrophobic properties. However, surface damages, such as wear and abrasion phenomena, can be detrimental to the attractive wetting properties of replicated textured surfaces. Therefore, the final product lifespan is investigated using mechanical cleaning of textured PP surfaces with multipurpose cloths following the ASTM D3450 standard. Second, the surface damage of replication masters after 350 injection molding cycles with glass-fiber-reinforced PP, especially to intensify mold wear, was investigated. In both cases, the degradation of the dual-scale surface textures had a clear impact on surface topography of the replicas and thus on their wetting properties, too.

The formation of blister in the injection moulded parts, especially in the film insert moulded parts, is one of most significant causes of part rejection due to cosmetic requirements or functionality issues. The mechanism and physics of blister formation for molded parts are not well-understood by the state-of-the-art literature. The current paper increases the fundamental understanding of the causes for blister formation. In the experiment, a membrane strip of 5 mm in width was overmoulded with Polypropylene (PP), which formed a disc-shaped part with a diameter of 17.25 mm and a thickness of 500 µm. To investigate the influence of the processing parameters, a full factorial design of experiments (DoE) setup was conducted, including mould temperature (T_m), barrel temperature (T_b), injection speed (V_i) and packing pressure (P_p) as variables. The degree of blistering at the surface was characterized by the areal surface roughness parameters Spk and Smr1, measured with a confocal laser microscope. The measurements were taken on the 10 mm long section of the membrane surface in the centre of the moulded part across the entire width of the film. In addition, the film insert moulding (FIM)-process was simulated and the average shrinkage of the substrate material under the membrane was investigated. Eventually, a method and processing window could be defined that could produce blister-free parts.