Titanium additions are often used for boron factor and primary austenite grain size control in boron high- and ultra-high-strength alloys. Due to the risk of formation of coarse TiN during solidification the addition of titanium is limited in respect to nitrogen. The risk of coarse nitrides working as non-metallic inclusions formed in the last solidification front can degrade fatigue properties and weldability of the final product. In the presented study three microalloying systems with minor additions were tested, two without any titanium addition, to evaluate grain size evolution and mechanical properties with pre-defined as-cast, hot forging, hot rolling, and off-line heat-treatment strategy to meet demands for S1100QL steel. Microstructure evolution from hot-forged to final martensitic microstructure was observed, continuous cooling transformation diagrams of non-deformed austenite were constructed for off-line heat treatment, and the mechanical properties of Nb and V–Nb were compared to Ti–Nb microalloying system with a limited titanium addition. Using the parameters in the laboratory environment all three micro-alloying systems can provide needed mechanical properties, especially the Ti–Nb system can be successfully replaced with V–Nb having the highest response in tensile properties and still obtaining satisfying toughness of 27 J at –40 °C using Charpy V-notch samples.

The objective of the study is to improve understanding of the practical role of niobium (Nb) in the case of industrial inconsistent rolling processes such as the rolling of heavy gauge plates where a lower stored energy rolling practice will result in a less stable and less repeatable static recrystallization (SRX) activation that prevents complete recrystallization. In the current study, these variabilities are validated by comparing the mean flow stress (MFS) indirectly determined from the rolling force measured on a reverse four-high rolling mill stand. The material resistance to deformation and grain size evolution of a C-Mn steel during hot rolling was observed and validated with and without Nb addition. The pre-defined rolling schedule was predicted to exhibit incomplete recrystallization in the roughing phase due to the limited stored energy of deformation that resulted from low rolling loads and a higher number of rolling passes. The prior austenite grain size (PAGS) distribution was predicted and compared to the measured effective ferrite grain (FG) size distribution after the completion of hot rolling and phase transformation achieved using natural air plate cooling. Both the predicted PAG and measured FG distributions revealed the presence of multimodality, and both distributions were used for grain size reduction factor determination for γ → α transformation for the current study with 1.96 for 0 Nb and 1.70 for 240 Nb. The results presented in this paper are not only limited to the rolling schedule used in this paper because instabilities resulting in incomplete austenite conditioning are also observed when evaluating the cross-sections of other heavy plates and various steel grades utilizing different processing routes with comparable compositions such as modern lean abrasion-resistant steels, regular line pipe steels, and other similar grades.

The aim of this study was to evaluate the effect of austempering compared to quenching and low-temperature tempering on wear resistance of an as-cast medium carbon high-silicon steel intended for rock breaking. Austempering was done by isothermal holding at 270, 300 and 350 °C in molten salt baths, while quenching was done in water. The austempering treatments resulted in microstructural combinations of bainite and martensite. The isothermal holding at 270 °C resulted in bainite and self-tempered martensite, while isothermal holdings at 300 and 350 °C resulted in bainite and untempered martensite. The two quench and temper treatments resulted in tempered martensite. In general austempering resulted in lower hardness values when compared to quenching and tempering but higher impact toughness. The wear resistance was best for quenching and low temperature tempering, followed by austempering at 270 °C, but at slightly lower hardness and 25% higher impact toughness. The other two austempering treatments resulted in worse wear resistance.

A study was undertaken to investigate the effects of small boron additions on the solidification and microstructure of hypo-eutectic alloyed grey cast iron. The characteristic temperatures upon crystallisation of the treated metal melt were recorded, specifically those concerning small boron addition by using thermal analysis with the ATAS system. Additionally, a standardised wedge test was set to observe any changes in chill performance. The microstructures of thermal analysis samples were analysed using a light optical microscope (LOM) and field emission scanning electron microscopy (FE-SEM) equipped with energy dispersive spectroscopy (EDS), which reveal variations in graphite count number with the addition of boron within observed random and undercooled flake graphite. The effect of boron was estimated by the classical analytical and statistical approach. The solidification behaviour under equilibrium conditions was predicted by a thermodynamic approach using Thermo-Calc. Based on all gathered data, a response model was set with boron for given melt quality and melt treatment using the experimentally determined data. The study reveals that boron as a ferrite and carbide-promoting element under the experimental set shows weak nucleation potential in synergy with other heterogenic nuclei at increased solidification rates, but no considerable changes were observed by the TA samples solidified at slower cooling rates, indicating the loss of the overall inoculation effect. The potential presence of boron nitride as an inoculator for graphite precipitation for a given melt composition and melt treatment was not confirmed in this study. It seems that boron at increased solidification rates can contribute to overall inoculation, but at slower cooling rates these effects are gradually lost. In the last solidification range, an increased boron content could have a carbide forming nature, as is usually expected. The study suggests that boron in traces could affect the microstructure and properties of hypo-eutectic alloyed grey cast iron.

Medium carbon high-silicon abrasion resistant (AR) steel was examined by performing dilatometry, light optical microscopy (LOM), scanning electron microscopy (SEM), and hardness measurements after isothermal bainitization and modified martempering and compared to direct quenching technology. A commercial thermodynamic tool was used for hardness prediction and compared to the measured one and revealed a rather good agreement for direct quenching, as was the case for isothermal holdings near to the martensite start (Ms). The predicted martensite start temperatures were in good agreement with the experimental data, the experimental value was 321 °C, while the predicted values were 324 and 296 °C. However, a higher discrepancy appeared for isothermal holding much above the martensite transition in the bainite region resulting in lower measured hardness compared to the predictions related to the actual kinetics and complexity of the formed final volume percentages of phase constituents such as bainite, martensite, and rest austenite, later as a part of unfinished bainite transformation at studied temperature. The predicted hardness values for quenching, isothermal holding at 280, 300 and 350 °C were 50.6, 50.6, 49.4 and 49.4 HRC, while the measured values were 53.3, 48.3, 48 and 43 HRC, respectively. A very good agreement between the thermodynamic prediction was achieved by comparing the measured Ms concerning prior austenite grain size as one of the crucial parameters for setting a proper heat treatment strategy of various isothermal quenchings making thermodynamic predictions for low alloyed steels a powerful tool for optimizing the heat-treating operations.