Within the scope of this research the transformation of the Al₆Fe metastable phase was analyzed via Differential Scanning Calorimetry (DSC), optical and Scanning Electron Microscopy (SEM) and X-ray Diffraction (XRD). A binary Al-Fe1.1 low-impurity alloy was produced with refined raw materials in a controlled environment. With a cooling rate of 35 K/s, solidification of the Al₆Fe metastable phase was achieved. The samples were homogenized at 600 °C for 2–24 h. Results of a qualitative analysis of metallographic samples show that the transformation began on grain boundaries, forming an Fe-phase free region, but after 2 h began to take place within the eutectic region. The transformation is mostly complete after 12 h, but after 24 h of homogenization it is fully complete as all samples, except the 24 h homogenized one, contain both the metastable Al₆Fe and the stable Al₁₃Fe₄ phase.

The high-temperature oxidation of hot-work tool steel AISI H11 was studied. The high-temperature oxidation was investigated in two conditions, the soft annealed condition, and the hardened and tempered condition. First, calculations of the compositions of the oxide layers formed were carried out using the CALPHAD method. The samples were oxidised in a chamber furnace and in a simultaneous thermal analysis instrument, for 100 h in the temperature range between 400 °C and 700 °C. The first samples were used for metallographic (optical microscopy and scanning electron microscopy) and X-ray diffraction analysis of the formed oxide layers, and the second ones for the analysis of the oxidation kinetics by thermogravimetric analysis. Equations describing the high-temperature oxidation kinetics were derived. The kinetics can be described by three mathematical functions, namely: exponential, parabolic, and cubic. However, which function best describes the kinetics depends on the oxidation temperature and the thermal condition of the steel. Hardened and tempered samples have been shown to oxidise less, resulting in a slower oxidation rate. The oxide layers consist of three sublayers, the inner one being spinel-like oxide (Fe, Cr)₃O₄, the middle one a mixture of magnetite and hematite and the outer one of hematite. At 700 °C there is also some wüstite in the inner oxide sublayer of the soft annealed sample.

The production of clean steel is associated with high-quality steel grades for demanding applications. The formation of oxide inclusions mainly depends on the deoxidation practice; it is usually carried out through Al additions, but alumina inclusions can have detrimental effects. An alternative zirconium inclusion modification was used in a creep-resistant steel to improve the cleanliness of laboratory-made steel. The thermodynamics behind the inclusion modification are presented, the reaction products are identified and the steel cleanliness improvement is quantified. The resulting influence of zirconium addition on non-metallic inclusions and mechanical properties is discussed. While the Zr additions drastically reduce the non-metallic inclusion size and area, additions above a certain amount result in the formation of zirconium nitrides that ultimately soften the martensitic steel due to the depletion of nitrogen in solid solution.

Additive manufacturing is a form of powder metallurgy, which means the properties of the initial metal powders (chemical composition, powder morphology and size) impact the final properties of the resulting parts. A complete characterization, including thermodynamic effects and the behavior of the metal powders at elevated temperatures, is crucial when planning the manufacturing process. The analysis of the Fe-Mn and Fe-Mn-Ag powder mixtures, made from pure elemental powders, shows a high susceptibility to sintering in the temperature interval from 700 to 1000 °C. Here, numerous changes to the manganese oxides and the αMn to βMn transformation occurred. The problems of mechanically mixed powders, when using selective laser melting, were highlighted by the low flowability, which led to a less controllable process, an uncontrolled arrangement of the powder and a large percentage of burnt manganese. All this was determined from the altered chemical compositions of the produced parts. The impact of the increased manganese content on the decreased probability of the transformation from γ-austenite to ε-martensite was confirmed. The ε-martensite in the microstructure increased the hardness of the material, but at the same time, its magnetic properties reduce the usefulness for medical applications. However, the produced parts had comparable elongations to human bone.

The influence of chemical composition and heat treatment on the mechanical properties and formability of the selected commercial aluminium alloy EN AW 5454 was investigated. The main properties of alloy 5454 from the AA 5xxx series are very good corrosion resistant and has good formability. From the cast slab a 50 mm thick slice was taken in the width cross section in the slab centre. One half of the slice was homogenised for 10 hours at a temperature of 530 °C. The cast and homogenised samples were investigated using light and scanning electron microscopy. For the study of the influence of the heat treatment, samples in the as-cast state were annealed in the laboratory furnace at a temperature of 530 °C for 4, 6, 8, 10 and 12 hours. To study the influence of chemical composition, four different samples were prepared: the first without additions, the second with an addition of 1 wt% Mn, the third with 3 wt% Mg and the fourth with an addition of both elements, Mn and Mg. The XRF analyses confirmed the desired chemical composition of all four produced alloys. Half of each alloy’s sample was homogenised at the same temperature and time as the base alloy in the as-cast state. The hot deformation behaviour of the different alloys was investigated using cylindrical hot compression tests performed on a Gleeble 1500D thermo-mechanical simulator. By comparing flow curves a high influence of the thermo-mechanical parameters on the alloy formability can be seen. The alloy has good workability and with the addition of Mn and Mg, the stress values are higher than those of the base alloy.

During the die-casting process as well as the hot forming process, the tool is subjected to complex thermal, mechanical, and chemical stresses that can cause various types of damage to different parts of the tool. This study was carried out to determine the resistance of various tool steels, i.e., UTOPMO1, HTCS-130, and W600, in molten Al99.7 aluminum alloy at a temperature of 700 °C. The formation kinetics of the interaction layer between the molten aluminum and tool steels was studied using differential scanning calorimetry. Light and field-emission scanning electron microscopy were used to analyze the thickness and nature of the interaction layers, while thermodynamic calculations using the Thermo-Calc software were used to explain the results. The stability of the HTCS-130 and W600 tool steels is better than the stability of the UTOPMO1 tool steel in the molten Al99.7 aluminum. Two interaction layers were formed, which in all cases indicate an intermetallic Al₁₃Fe₄ layer near the aluminum alloy and an intermetallic Al₅Fe₂ layer near the tool steels, containing small round carbides. It was confirmed that Ni reduces the activity of aluminum in the ferrite matrix and causes a reduction in the thickness of the intermetallic layer.