Plastic bottles are generally recycled by remolding them into numerous products. In this study, waste from plastic bottles was used to fabricate recycled polyethylene terephthalate (r-PET) nanofibers via the electrospinning technique, and high-performance conductive polyethylene terephthalate nanofibers (r-PET nanofibers) were prepared followed by copper deposition using the electroless deposition (ELD) method. Firstly, the electrospun r-PET nanofibers were chemically modified with silane molecules and polymerized with 2-(methacryloyloxy) ethyl trimethylammonium chloride (METAC) solution. Finally, the copper deposition was achieved on the surface of chemically modified r-PET nanofibers by simple chemical/ion attraction. The water contact angle of r-PET nanofibers, chemically modified r-PET nanofibers, and copper deposited nanofibers were 140°, 80°, and 138°, respectively. The r-PET nanofibers retained their fibrous morphology after copper deposition, and EDX results confirmed the presence of copper on the surface of r-PET nanofibers. XPS was performed to analyze chemical changes before and after copper deposition on r-PET nanofibers. The successful deposition of copper one r-PET nanofibers showed an excellent electrical resistance of 0.1 ohms/cm and good mechanical strength according to ASTM D-638.

Silica fiber under high pressure increases the risk of fiber breakage or permanent deformation, which may cause sensor failure due to mechanical strength limitations. High pressure can also induce birefringence in optical fiber. In this study, we present a simple design and low-cost high pressure sensor using polymer optical fiber (POF) based on the intensity-variation technique. A side-coupling mechanism in the sensor structure is adopted, which varies the intensity with applied pressure. Two POFs are twisted together to create a sensing region where the light is launched in the first fiber and measurement is taken from the second fiber. In sensing phenomena, cladding mode frustrated total internal reflection occurs when pressure increases. Silicone gel is used in the pressure chamber for sealing and preventing leakage. The sensor structure is able to detect high pressure in the MPa range, where we tested up to 4 MPa. For higher sensitivity, twisted and bend structure is analyzed, and sensitivity is achieved at about 432.21 nW/MPa. However, twisted helical structure is adopted to enhance sensing range which is about 50 cm. The proposed high-pressure sensor structure is easier to fabricate and has high stability because it doesn’t require any destructive method as compared to other conventional methods.

Fast drug-dissolving systems have been introduced to mediate the drugs which are difficult to swallow or having poor water solubility. Rizatriptan benzoate is a drug recommended for the patients of migraine which effect one out of every 5 women and 15 men globally. But least bioavailability (40%–50%) and reduced on set action always increases the demand of a drug carrier in order to overcome these limitations. Here in pullulan mediated fast drug-dissolving systems was developed by using rizatriptan benzoate as a model drug. While rizatriptan loaded pullulan nanofiber mat was prepared via electrospinning. Physiochemical outcomes (SEM, FTIR, and XRD) revealed good compatibility of pullulan nanofibers and rizatriptan thoroughly distributed on electrospun NFs matrix. Wetting time (1 s) and dissolutions time (3 s) suggests burst release of the drug from the polymers matrix as dissolution time is directly proportional with release profile. Further, this was confirmed by UV-release profile studies and maximum release was found within 30 s. In vitro release kinetics were analyzed by fitting the results with higuchi and korsmeyer models.