The energetic and climate crises should pose a challenge for scientists in finding solutions in the field of renewable, green energy sources. Throughout more than two decades, the search for new opportunities in the energy industry made it possible to observe the potential use of hydrogen as an energy source. One of the greatest challenges faced by scientists for the sake of its use as an energy source is designing safe, usable, reliable, and effective forms of hydrogen storage. Moreover, the manner in which hydrogen is to be stored is closely dependent on the potential use of this source of green energy. In stationary use, the aim is to achieve high volumetric density of the container. However, from the point of view of mobile applications, an extremely important aspect is the storage of hydrogen, using lightweight tanks of relatively high density. That is why, a focus of scientists has been put on the use of carbon-based materials and graphene as a perspective solution in the field of H₂ storage. This review focuses on the comparison of different methods for hydrogen storage, mainly based on the carbon-based materials and focuses on efficiently using graphene and its different forms to serve a purpose in the future H₂-based economy.

Silver and copper as additives of various biomaterials have been reported as the potential solutions for biomedicine applications, mostly because of inducing bactericidal effects. The application of those admixtures in diamond-like carbon (DLC) coatings may be desirable for orthopedic implants. In the present manuscript, the biological effect of coatings with up to about 7 at.% and 14 at.% of, respectively, Cu and Ag is compared. The morphology, chemical structure, and composition of films deposited on AISI 316LVM and Ti6Al7Nb is characterized. The live/dead analysis conducted with Escherichia coli shows a higher bactericidal potential of silver than copper. Although the Cu-doped coatings can positively affect the proliferation of Saos-2 and EA.hy926 cell lines, the results of XTT test are on the verge of 70% of viability. Biological effect of silver on EA.hy926 cell lines is negative but that admixture ensures high proliferation of osteoblasts in contact with coatings deposited on titanium alloy (over 20% better than for substrate material). In that case, the viability is reaching about 85% for Ag-doped coatings on AISI 316LVM and 75% on Ti6Al7Nb. The results indicate that for the sake of bactericidal coatings that may promote osteointegration, the candidates are DLC with silver content no higher than 10 at.%.