Selective laser melted Titanium grade 23 was characterized by low porosity, relatively large surface roughness and pronounced surface texture (i.e. surface grooves orientation). The band/layer microstructure was built of mixed α and β phases. The as printed structure exhibited very high compressive residual stresses with strong anisotropy (i.e., − 512 ± 17 MPa and − 282 ± 14 MPa along the laser scanning direction and along the transverse direction, respectively) and strong fiber crystallographic texture. The latter one is responsible for the anisotropy of hardness in the material. Annealing at 600 °C during four hours significantly removed residual stresses (i.e. to − 14 ± 2.8 MPa) and slightly weakened the texture. Yield strength, 1120 ± 50 MPa, and ultimate tensile strength, 1210 ± 50 MPa, of the annealed material are significantly higher and tensile elongation, 3.9%, lower than for commercial Titanium grade 23. Final mechanical polishing to obtain flat and relatively smooth surface induced desired compression residual stress in the subsurface (i.e., equal to about − 90 MPa). Low absorbed gas contents (oxygen, nitrogen, hydrogen) and low porosity of the printed material indicates the correctness of the technology and allows the printed material to be classified as meeting the requirements of ASTM standards for Titanium grade 23. Besides traditional testing techniques, the optical profilometry, X-ray analysis (texture and residual stresses measurement) and infrared absorption method were applied for the product characterization and some potential of these testing methods and usefulness in technological practice was discussed, what can be particularly interesting both to practitioners from industry and researches from scientific laboratories.

Evolution of microstructure and hardness in quenched ultrahigh carbon steel Fe-0.85Mo-0.6Si-1.4C by warm compression on a Bähr plastometer-dilatometer at 775 °C and at 0.001 to 1 s⁻¹ strain rate range is reported. The material was prepared via powder metallurgy: cold pressing and liquid phase sintering. Independent of strain rate, the initial martenstic microstructure was transformed to ferrite and spheroidized cementite. Strain rate had an effect on size and shape of spheroidized Fe₃C precipitates: the higher the strain rate, the smaller the precipitates. Morphology of the spheroidized carbides influenced hardness, with the highest hardness, 362 HV10, for strain rate 1 s⁻¹ and the lowest, 295 HV10, for the lowest strain rate 0.001 s⁻¹. Resultant microstructure and ambient temperature mechanical properties were comparable to those of the material that had undergone a fully spheroidizing treatment with increased time and energy consumption, indicating that it can be dispensed with in industrial processing. All our results are consistent with the Hall–Petch relation developed for spheroidized steels.

Rebielskij-type design of a rolled con rod preform and appropriate upper and lower dies are presented. The proposed process was tested by Simufact Forming program and modifications made to satisfy the criteria of shape, stress and strain state and temperature distribution during processing. Based on the CAD documentation, a STL file was prepared for 3D polymer printing the die, the con rod preform and the forging. The results will enable 3D printing of prototypes in the appropriate metallic materials, leading to tool manufacture and processing in industrial conditions.