The knowledge of alloy–process–structure–property relationships is of particular interest for several safety-critical brazed components and requires a detailed characterization. Thus, three different nickel-based brazing filler metals were produced with varying chromium and molybdenum content and were used to braze butt joints of the austenitic stainless steel AISI 304L under vacuum. Two holding times were used to evaluate diffusion-related differences, resulting in six specimen variations. Significant microstructural changes due to the formation and location of borides and silicides were demonstrated. Using X-ray diffraction, alloy-dependent residual stress gradients from the brazing seam to the base material were determined and the thermal-induced residual stresses were shown through simulations. For mechanical characterization, impact tests were carried out to determine the impact toughness, as well as tensile tests at low and high strain rates to evaluate the strain-rate-dependent tensile strength of the brazed joints. Further thermal, electrical, and magnetic measurements enabled an understanding of the deformation mechanisms. The negative influence of brittle phases in the seam center could be quantified and showed the most significant effects under impact loading. Fractographic investigations subsequently enabled an enhanced understanding of the fracture mechanisms.

In general, formed components are lightweight as well as highly economic and resource efficient. However, forming-induced ductile damage, which particularly affects the formation and growth of pores, has not been considered in the design of components so far. Therefore, an evaluation of forming-induced ductile damage would enable an improved design and take better advantage of the lightweight nature as it affects the static and dynamic mechanical material properties. To quantify the amount, morphology and distribution of the pores, advanced scanning electron microscopy (SEM) methods such as scanning transmission electron microscopy (STEM) and electron channeling contrast imaging (ECCI) were used. Image segmentation using a deep learning algorithm was applied to reproducibly separate the pores from inclusions such as manganese sulfide inclusions. This was achieved via layer-by-layer ablation of the case-hardened steel 16MnCrS5 (DIN 1.7139, AISI/SAE 5115) with a focused ion beam (FIB). The resulting images were reconstructed in a 3D model to gain a mechanism-based understanding beyond the previous 2D investigations.

The paper will explain the formation and effects of brittle precipitates in form of borides and silicides during high-temperature vacuum diffusion brazing on the example of a nickel-based filler metal from the NiCrSiB system. This filler metal foil was used to braze butt joints of the metastable austenite AISI 304L. Energy and wavelength dispersive X-ray spectroscopy was applied to identify the precipitates. Using a focused ion beam in scanning electron microscopy, the brazed joint was removed layer by layer over a large area to gain insights into the 3D structure of the precipitates. Subsequently, a methodology will be presented on how to reconstruct a 3D model from the image data using deep learning-based image segmentation. The final model unravels the complex morphology of these precipitates and thus contributes to a better understanding of the solidification and precipitation mechanisms in diffusion brazing.