Considering the before and after phonon softening, the gap in a CoO₆-octahedral crystal electric fields (CEF) and the thermally activated spin gap, were observed of ∼0.5 meV and Q ∼ 25 meV in defect-free LaCoO₃ single crystal, respectively.

The gadolinium sesquioxide (Gd₂O₃) with its bandgap of ∼5.4 eV and high dielectric permittivity and refractive index has been used widely in optics, magnetic resonance imaging, and high k dielectrics. Electron energy loss spectroscopy (EELS) reveals spectral features at 13.5 eV and 15 eV, which can be interpreted as surface and volume plasmons, respectively. The unusual surface exciton polariton, with surface resonances associated with excitonic onsets, was also observed at ∼7.5 eV. Because of the differences in electronic structures between the cubic and the monoclinic phases of Gd₂O₃, it is straightforward to distinguish the two phases using the low-loss regime and O K-edge as a fingerprint. We further successfully performed EELS and electron diffraction to identify the crystalline phase of a single-crystal Gd₂O₃ film epitaxially grown on a Si(111) substrate.

A direct Z-scheme heterojunction via decorating Ag ₃ PO ₄ quantum dots on SnS ₂ nanosheets results in highly selective and efficient solar-driven CO ₂ -to-CO photoreduction.