This paper provides a synthetic and comprehensive overview on environmentally friendly anticorrosive polymeric coatings. Firstly, the economic and environmental impact of corrosion is presented to highlight the need of anticorrosive polymeric coatings as a flexible and effective solution to protect a metal. Secondly, the implementation of regulations together with the consumer awareness for environmental considerations and protection of health are the driving force for a progressive but significant change in the sector. Therefore, within the protective organic coatings market, this article provides a review of the most recent developments in environmentally friendly solutions, including bio-based and water-borne epoxy, hyperbranched polyester for low- volatile organic compounds (VOC) coatings, waterborne polyurethane and non-isocyanate polyurethanes (NIPUs), and graphene or bio-based fillers for acrylics. Moreover, this paper outlines new trends such as smart additives, bio-based corrosion inhibitors, and functional antibiocorrosive coatings as superhydrophobics. Finally, industrially relevant applications of environmentally friendly anticorrosive polymeric coatings including solutions for marine and off-shore industries are summarized.

A new technology consisting of new and sustainable chemical polishing treatment for aluminum components with complex shapes, such as heat exchangers, manifolds, busbars, aerospace devices, etc., manufactured by Additive Manufacturing (AM) technologies is described in this paper. This technology will contribute to the development of a more efficient manufacturing process driven by AM, reinforcing the main idea of AM, which is based on reducing the amount of material and achieving cost savings through smart and improved designs. The present study shows a significant reduction in the surface roughness of consolidated AlSi10Mg metal parts manufactured by the SLM technique after carrying out the new chemical polishing post-process investigated in this work. Roughness values have been measured by mechanical and optical profilometry. The results obtained demonstrate the effectiveness of the chemical polishing, decreasing the roughness by up to 40%, being a reproducible and repeatable post-process. The presence of smut as solid residues on such types of chemical treatments has been also analyzed with XRF and ICP-MS techniques. The results obtained show that Si and Mg precipitates are removed from the metal surface at the last step of the investigated post-process. The percentages of the elements decrease from 25.0% to 8.09% Si and from 0.86% to 0.42% Mg, achieving the alloy smut-free composition on the metal surface. Tensile strength measurements have shown that the post-process described not only maintains the mechanical properties of the bulk material but, in comparison with non-post-processed parts, a slight improvement is observed with respect to the initial values, Young modulus (61.1 GPa to final 62.2 GPa), yield strength (from 236.8 to 246.7 MPa), and tensile strength (from 371.9 to 382.5 MPa) is observed, suggesting that the post-process has positive impact on the printed metal part.