The present study investigates the feasibility of utilizing polylactic acid (PLA) and PLA-based natural fiber-reinforced composites (NFRCs) in mechanical recycling. A conical twin screw extrusion (CTSE) process was utilized to recycle PLA and PLA-based NFRCs consisting of 90 wt.% PLA and a 10 wt.% proportion of either basalt fibers (BFs) or halloysite nanotubes (HNTs) for up to six recycling steps. The recycled material was then injection molded to produce standard test specimens for impact strength and tensile property analysis. The mechanical recycling of virgin PLA led to significant discoloration of the polymer, indicating degradation during the thermal processing of the polymer due to the formation of chromatophores in the structure. Differential scanning calorimetry (DSC) analysis revealed an increase in glass transition temperature (T_g) with respect to increased recycling steps, indicating an increased content of crystallinity in the PLA. Impact strength testing showed no significant detrimental effects on the NFRCs’ impact strength up to six recycling steps. Tensile testing of PLA/HNT NFRCs likewise did not show major decreases in values when tested. However, PLA/BF NFRCs exhibited a significant decrease in tensile properties after three recycling steps, likely due to a reduction in fiber length beyond the critical fiber length. Scanning electron microscopy (SEM) of the fracture surface of impact specimens revealed a decrease in fiber length with respect to increased recycling steps, as well as poor interfacial adhesion between BF and PLA. This study presents a promising initial view into the mechanical recyclability of PLA-based composites.

Poly (N-vinylcaprolactam) is a polymer that is biocompatible, water-soluble, thermally sensitive, non-toxic, and nonionic. In this study, the preparation of hydrogels based on Poly (N-vinylcaprolactam) with diethylene glycol diacrylate is presented. The N-Vinylcaprolactam-based hydrogels are synthesised by using a photopolymerisation technique using diethylene glycol diacrylate as a crosslinking agent, and Diphenyl (2, 4, 6-trimethylbenzoyl) phosphine oxide as a photoinitiator. The structure of the polymers is investigated via Attenuated Total Reflectance–Fourier Transform Infrared Spectroscopy. The polymers are further characterised using differential scanning calorimetry and swelling analysis. This study is conducted to determine the characteristics of P (N-vinylcaprolactam) with diethylene glycol diacrylate, including the addition of Vinylacetate or N-Vinylpyrrolidone, and to examine the effects on the phase transition. Although various methods of free-radical polymerisation have synthesised the homopolymer, this is the first study to report the synthesis of Poly (N-vinylcaprolactam) with diethylene glycol diacrylate by using free-radical photopolymerisation, using Diphenyl (2, 4, 6-trimethylbenzoyl) phosphine oxide to initiate the reaction. FTIR analysis shows that the NVCL-based copolymers are successfully polymerised through UV photopolymerisation. DSC analysis indicates that increasing the concentration of crosslinker results in a decrease in the glass transition temperature. Swelling analysis displays that the lower the concentration of crosslinker present in the hydrogel, the quicker the hydrogels reach their maximum swelling ratio.

Four-dimensional printing is primarily based on the concept of 3D printing technology. However, it requires additional stimulus and stimulus-responsive materials. Poly-N-vinylcaprolactam is a temperature-sensitive polymer. Unique characteristics of poly-N-vinylcaprolactam -based hydrogels offer the possibility of employing them in 4D printing. The main aim of this study is to alter the phase transition temperature of poly-N-vinylcaprolactam hydrogels. This research focuses primarily on incorporating two additional monomers with poly-N-vinylcaprolactam: Vinylacetate and N-vinylpyrrolidone. This work contributes to this growing area of research by altering (increasing and decreasing) the lower critical solution temperature of N-vinylcaprolactam through photopolymerisation. Poly-N-vinylcaprolactam exhibits a lower critical solution temperature close to the physiological temperature range of 34–37 °C. The copolymers were analysed using various characterisation techniques, such as FTIR, DSC, and UV-spectrometry. The main findings show that the inclusion of N-vinylpyrrolidone into poly-N-vinylcaprolactam increased the lower critical solution temperature above the physiological temperature. By incorporating vinylacetate, the lower critical solution temperature dropped to 21 °C, allowing for potential self-assembly of 4D-printed objects at room temperature. In this case, altering the lower critical solution temperature of the material can potentially permit the transformation of the 4D-printed object at a particular temperature.

This review details the extraction, characterization and utilization of seaweed-derived biopolymers for future packaging applications. The review is contextualized within the broader scope of the challenge of plastic pollution and the current urgent need for more sustainable packaging materials. Macroalgae (or seaweed) has been highlighted as a promising source of biopolymers, most commonly sodium alginate, agar and carrageenan, for reasons such as a rapid growth rate and decreased environmental impact when compared with terrestrial plant life. Extraction methods detailed include traditional solvent-based extraction and more sustainable developments such as ultrasound-assisted extraction, microwave-assisted extraction and bead milling. This review additionally presents the characterization techniques most pertinent in determining the applicability of these biopolymers in packaging applications. Properties of key importance to the development of sustainable packaging materials such as thermal properties, mechanical strength, barrier properties and biodegradability are highlighted in comparison to conventional petroleum-based plastics. This review concludes by realistically identifying the challenges faced by implementing seaweed-based biopolymers into packaging structures, such as cost-effectiveness, scalability and performance while suggesting future directions to mitigate these issues and improve the commercial viability of these materials for the packaging industry.

This study addresses the gap in research on the application of thermochromic polymers (TPs) in food packaging and their potential for real-time temperature monitoring, aiding in the assessment of food quality and shelf-life. TPs exhibit a visible color change in response to temperature variations. A comprehensive systematic review (SR) across multiple engineering peer-review databases using predefined terms was conducted. Additionally, international patent databases were investigated using the same predefined terms. Independent experts reviewed the methodology to identify and address potential biases. A total of 288 eligible articles and 922 patents were identified. After a duplicate selection and extraction process according to the inclusion criteria, four related full-text publications were selected from the initial 288 articles, and five relevant patents were selected from the 922 patents. The qualitative review suggests that TPs hold significant promise as food packaging materials due to their unique physical properties. The study concludes that TPs offer valuable properties for the food packaging industry, meriting further investigation to exploit their benefits fully.

This study aimed to demonstrate the feasibility of hot-melt extrusion in the development of extended-release formulations of Fenbendazole (Fen) dispersed in PEO/PCL blend-based matrices. Their thermal, physical, chemical and viscosity properties were assessed by differential scanning calorimetry, thermogravimetric analysis/derivative thermogravimetry, Fourier transform infrared spectroscopy, X-ray diffraction spectroscopy, and melt flow index. Drug dispersion was analyzed by scanning electron microscopy with electron dispersive X-ray spectroscopy, and drug release was evaluated by ultraviolet-visible spectroscopy. A thermal analysis indicated the conversion of the drug to its amorphous state. FTIR analysis endorsed the thermal studies pointing to a decrease in the drug’s crystallinity with the establishment of intermolecular interactions. XRD analysis confirmed the amorphous nature of Fen. MFI test revealed that PCL acts as a plasticizer when melt-processed with PEO. SEM images displayed irregular surfaces with voids and pores, while EDX spectra demonstrated a homogeneous drug distribution throughout the polymeric carrier. Dissolution testing revealed that PCL retards the drug release proportionally to the content of such polymer incorporated. These melt-extruded matrices showed that the drug release rate in a PEO/PCL blend can easily be tailored by altering the ratio of PCL to address the issues related to the multiple-dosing regimen of Fen in ruminants.