The obtaining and characterization of some polymeric eco-composites based on wood sawdust and natural rubber is presented. The natural rubber was cross-linked using the electron beam irradiation. The irradiation doses were of 75, 150, 300 and 600 kGy and the concentrations of wood sawdust were of 10 and 20 phr, respectively. As a result of wood sawdust adding, the physical and mechanical properties such as hardness, modulus at 100% elongation and tensile strength, showed significant improvements. The presence of wood sawdust fibers has a reinforcing effect on natural rubber, similar or better than of mineral fillers. An increase in the irradiation dose leads to the increasing of cross-link density, which is reflected in the improvement of hardness, modulus at 100% elongation and tensile strength of blends. The cross-linking rates, appreciated using the Flory-Rehner equation, have increased with the amount of wood sawdust in blends and with the irradiation dose. Even if the gel fraction values have varied irregularly with the amount of wood sawdust and irradiation dose it was over 90% for all blends, except for the samples without wood sawdust irradiated with 75 kGy. The water uptake increased with increasing of fiber content and decreased with the irradiation dose.

A natural fiber reinforced composite, belonging to the class of eco composites, based on ethylene-propylene-terpolymer rubber (EPDM) and wood wastes were obtained by electron beam irradiation at 75, 150, 300, and 600 kGy in atmospheric conditions and at room temperature using a linear accelerator of 5.5 MeV. The sawdust (S), in amounts of 5 and 15 phr, respectively, was used to act as a natural filler for the improvement of physical and chemical characteristics. The cross-linking effects were evaluated through sol-gel analysis, mechanical tests, and Fourier Transform Infrared FTIR spectroscopy comparatively with the classic method with dibenzoyl peroxide (P) applied on the same types of samples at high temperature. Gel fraction exhibits values over 98% but, in the case of P cross-linking, is necessary to add more sawdust (15 phr) to obtain the same results as in the case of electron beam (EB) cross-linking (5 phr/300 kGy). Even if the EB cross-linking and sawdust addition have a reinforcement effect on EPDM rubber, the medium irradiation dose of 300 kGy looks to be a limit to which or from which the properties of the composite are improved or deteriorated. The absorption behavior of the eco-composites was studied through water uptake tests.

Natural rubber composites reinforced with hemp, flax, and wood sawdust were obtained by irradiation at room temperature with an electron beam of 5.5 MeV in order to meet the actual need for new materials that are environmentally friendly and safe for human health. The natural fibers loading was between 5 and 20 phr and the processing doses were between 75 and 600 kGy. The kinetics of water absorption in these materials were studied. The water diffusion was analyzed through Fick’s law. The water absorption parameters (Qt and Qeq), diffusion parameters (k and n), diffusion coefficient (D), intrinsic diffusion coefficient (D*), sorption coefficient (S), and permeation coefficient (P) have depended on the fiber nature, amount used in blends, and irradiation dose. The obtained results showed that not in the case of each type of fiber used, the water absorption could be correlated with the specific cellulose and hemicellulose content, due to the changes induced by the electron beam.

Poly(acrylamide co-acrylic acid) hydrogels were prepared by free-radical copolymerization of acrylamide and acrylic acid in aqueous solutions using electron beam irradiation in the dose range of 2.5 kGy to 6 kGy in atmospheric conditions and at room temperature. The influence of the absorbed dose, the amount of cross-linker (trimethylolpropane trimethacrylate) and initiator (potassium persulfate) on the swelling properties and the diffusion coefficient and network parameters of hydrogels were investigated. The structure and morphology of hydrogels were characterized by Fourier Transform Infrared Spectroscopy (FTIR) and Scanning Electron Microscopy (SEM). The use of the obtained hydrogels by the removal of Cu²⁺ and Cr⁶⁺ from aqueous solutions was investigated at room temperature. During the adsorption of metal ions on hydrogels, the residual metal ion concentration in the solution was measured by an atomic absorption spectrophotometer (AAS). It has been established that the use of a relatively small amount of trimethylolpropane trimethacrylate for hydrogel preparation has led to the increasing of swelling up to 8500%.

Polymeric composites based on natural rubber (NR) and plasticized starch (PS) obtained by peroxide cross-linking have been subjected to electron beam irradiation in order to investigate their degradation. The amount of PS ranged from 10 to 50 phr and the irradiation dose from 150 to 450 kGy. Irradiation was performed in atmospheric conditions using a linear electron accelerator of 5.5 MeV. Changes in chemical, physical, structural, and morphological properties of composites were correlated with variables, such as PS loading and irradiation dose. Thus, mechanical properties, gel fraction, cross-linking degree, water uptake, weight loss in toluene/water were compared with those obtained before irradiation. The changes in structure and morphology were studied by Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy. Both PS loading and irradiation dose were found to be responsible for the degradation installing. Moreover, it has been shown that at the dose of 450 kGy, chain scission is dominant over cross-linking.

The goals of the paper were first the obtainment and characterization of sodium alginate-g-acrylamide polyelectrolytes by electron beam irradiation in the range of 0.5 to 2 kGy, and second, the evaluation of flocculation efficacy and heavy metal removal capacity from aqueous solutions of known concentrations. Based on sodium alginate concentration, two types of grafted polymers were obtained. Physical, chemical, and structural investigations were performed. Flocculation studies under different stirring conditions on 0.5, 0.1 and 0.2% kaolin suspension were done. The removal capacity of Cu²⁺ and Cr⁶⁺ ions was also investigated. The acrylamide grafting ratio on sodium alginate backbone was found up to 2000% for samples containing 1% sodium alginate and up to 500% for samples containing 2% sodium alginate. Transmittances between 98 and 100% were obtained using, in the flocculation studies, polyelectrolytes containing 2% sodium alginate in concentrations of 0.5 and 1 ppm on kaolin suspension of 0.1 wt %. The polymer concentration was found critical for kaolin suspension of 0.05 and 0.1 wt %. Polymers containing 1% sodium alginate were efficient in Cr⁶⁺ ion removal, while those containing 2% in Cu²⁺ ion removal.