Polymeric composites based on natural rubber (NR) and plasticized starch (PS) obtained by peroxide cross-linking have been subjected to electron beam irradiation in order to investigate their degradation. The amount of PS ranged from 10 to 50 phr and the irradiation dose from 150 to 450 kGy. Irradiation was performed in atmospheric conditions using a linear electron accelerator of 5.5 MeV. Changes in chemical, physical, structural, and morphological properties of composites were correlated with variables, such as PS loading and irradiation dose. Thus, mechanical properties, gel fraction, cross-linking degree, water uptake, weight loss in toluene/water were compared with those obtained before irradiation. The changes in structure and morphology were studied by Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy. Both PS loading and irradiation dose were found to be responsible for the degradation installing. Moreover, it has been shown that at the dose of 450 kGy, chain scission is dominant over cross-linking.

Composites based on natural rubber reinforced with mineral (precipitated silica and chalk) and organic (sawdust and hemp) fillers in amount of 50 phr were obtained by peroxide cross-linking in the presence of trimethylolpropane trimethacrylate and irradiated by electron beam in the dose range of 150 and 450 kGy with the purpose of degradation. The composites mechanical characteristics, gel fraction, cross-linking degree, water uptake and weight loss in water and toluene were evaluated by specific analysis. The changes in structure and morphology were also studied by Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy. Based on the results obtained in the structural analysis, possible mechanisms specific to degradation are proposed. The increasing of irradiation dose to 450 kGy produced larger agglomerated structures, cracks and micro voids on the surface, as a result of the degradation process. This is consistent with that the increasing of irradiation dose to 450 kGy leads to a decrease in crosslinking and gel fraction but also drastic changes in mechanical properties specific to the composites’ degradation processes. The irradiation of composites reinforced with organic fillers lead to the formation of specific degradation compounds of both natural rubber and cellulose (aldehydes, ketones, carboxylic acids, compounds with small macromolecules). In the case of the composites reinforced with mineral fillers the degradation can occur by the cleavage of hydrogen bonds formed between precipitated silica or chalk particles and polymeric matrix also.

In the present paper, hydrogels based on acrylic acid (20%), sodium alginate (0.5%) and poly(ethylene oxide) (0.1%) were obtained by electron beam irradiation at room temperature with doses between 5 and 20 kGy, using potassium persulfate in concentrations up to 0.3% as a reaction initiator. The influence of initiator concentration and irradiation dose on hydrogel network parameters, swelling and deswelling behavior, gelation and degradation points, structure and morphology were investigated. Cross-link density increased with the irradiation dose and initiator addition, except at 20 kGy. The gel fraction was over 87.0% in all cases. Swelling experiments in distilled water showed swelling degrees of 40,000% at an irradiation dose of 5 kGy when a concentration of 0.1% initiator was added. A relationship between the swelling degree and irradiation dose, cross-linking degree (that increases from 0.044 × 10² to 0.995 × 10² mol/cm³) and mesh size (that decreases from about 220 nm to 26 nm) was observed. The addition of only 0.1% of PP led to the obtaining of hydrogels with a swelling degree of 42,954% (about 430 g/g) at an irradiation dose of 5 kGy and of 7206% (about 62 g/g) at 20 kGy, which are higher percentages than those obtained in the same irradiation conditions but without PP.

The interest in ultrathin silver (Ag) films has increased due to their high surface plasmon resonance for coatings of only a few nm. Low roughness ultrathin films of 1 to 9 nm have been deposited on different substrates, such as polyethylene terephthalate (PET) and optical glass, using radio frequency (RF) magnetron sputtering. Films show good surface plasmon resonance up to 7 nm thickness, as revealed by the ultraviolet-visible (UV-Vis) spectra. The roughness of the films, investigated by Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM), is small, and one can conclude that depositions are smooth and homogeneous. The bandgap values decrease with film thickness. The refractive index of the films, calculated from ellipsometry measurements, leads to values of under 1 visible domain, with minima in the wavelength range of 400–600 nm. The results are useful for obtaining lower roughness ultrathin Ag films with good surface plasmon resonance for photonic applications.

Herein, three different recipes of multi-component hydrogels were synthesized by e-beam irradiation. These hydrogels were obtained from aqueous polymer mixtures in which different proportions of bovine collagen gel, sodium carboxymethylcellulose (CMC), poly(vinylpyrrolidone), chitosan, and poly(ethylene oxide) were used. The cross-linking reaction was carried out exclusively by e-beam cross-linking at 25 kGy, a dose of irradiation sufficient both to complete the cross-linking reaction and effective for hydrogel sterilization. The hydrogels developed in this study were tested in terms of physical and chemical stability, mechanical, structural, morphological, and biological properties. They are transparent, maintain their structure, are non-adhesive when handling, and most importantly, especially from the application point of view, have an elastic structure. Likewise, these hydrogels possessed different swelling degrees and expressed rheological behavior characteristic of soft solids with permanent macromolecular network. Morphologically, collagen- and CMC based-hydrogels showed porous structures with homogeneously distributed pores assuring a good loading capacity with drugs. These hydrogels were investigated by indirect and direct contact studies with Vero cell line (CCL-81™, ATCC), demonstrating that they are well tolerated by normal cells and, therefore, showed promising potential for further use in the development of drug delivery systems based on hydrogels.