The research paper presents the impact of the scandium additive and various conditions of the heat treatment on copper mechanical, electrical and heat resistance properties. The performed research works included manufacturing of CuSc0.15 and CuSc0.3 alloys through metallurgical synthesis with the use of induction furnace and following crystallization in graphite crucibles at ambient temperature. Additionally, a CuZr0.15 alloy was produced as a reference material for previously synthesized Cu–Sc alloys. During research, the selection of heat treatment for the produced materials was conducted in order to obtain the highest mechanical–electrical properties ratio. Materials obtained in such a way were next subjected to thermal resistance tests. Parameters of thermal resistance test included temperatures from the range of 200–700 °C and 1 h of annealing time. The research has shown that CuSc0.15 and CuSc0.3 alloys have higher heat resistance after their precipitation hardening compared to the Cu–Zr alloy. The paper also presents microstructural research of the produced materials, which showed that alloying elements precipitates are mainly localized at the grain boundaries of the material structure.

The continuous industrial development that occurs worldwide generates the need to develop new materials with increasingly higher functional properties. This need also applies to the basic material for electricity purposes, which is copper. In this article, we carry out studies on the influence of various alloying elements such as Mg, In, Si, Nb, Hf, Sb, Ni, Al, Fe, Zr, Cr, Zn, P, Ag, Sc, Pb, Sn, Co, Ti, Mn, Te and Bi on the electrical and mechanical properties of ETP-grade copper. The research involves producing copper alloys using the gravity die casting method with alloy additions of 0.1 wt.%, 0.3 wt.% and 0.5 wt.%. All resulting materials are cold-worked to produce wires, which are subsequently homogenized and annealed. The materials produced in this manner undergo testing to determine their specific electrical conductivity, tensile strength, yield strength, elongation and Vickers hardness (HV10 scale).

Today’s world is a place where lack of electrical energy would be unimaginable for most of society. All the conductors in the world, both aluminum and copper, have their origin in various types of casting lines where the liquid metal after crystallization is being processed into the form of wires and microwires. However, the efficiency of the continuous casting processes of metals and the final quality of the manufactured product strictly depend on the design of the used crystallizers, the materials used during its production and its quality. Research conducted in this paper focuses on the latter, i.e., external surface quality of the graphite crystallizer at the place of contact with the primary cooling system. In order to quantify its influence on the continuous casting process numerical analyses using the finite element method has been conducted, which results have been further confirmed during empirical tests in laboratory conditions. It has been proven with all of the proposed methods that the temperature of the obtained cast rod is closely linked to the aforementioned surface quality, as when its roughness coefficient surpasses a certain value the temperature of the obtained product increases almost twofold from approx. 150–170 °C to 300–320 °C. These values might influence the quality and final properties of the cast rod, the susceptibility to wire drawing process and possible formation of wire drawing defects and therefore be of much importance to the casting and processing industry.