The continuous industrial development that occurs worldwide generates the need to develop new materials with increasingly higher functional properties. This need also applies to the basic material for electricity purposes, which is copper. In this article, we carry out studies on the influence of various alloying elements such as Mg, In, Si, Nb, Hf, Sb, Ni, Al, Fe, Zr, Cr, Zn, P, Ag, Sc, Pb, Sn, Co, Ti, Mn, Te and Bi on the electrical and mechanical properties of ETP-grade copper. The research involves producing copper alloys using the gravity die casting method with alloy additions of 0.1 wt.%, 0.3 wt.% and 0.5 wt.%. All resulting materials are cold-worked to produce wires, which are subsequently homogenized and annealed. The materials produced in this manner undergo testing to determine their specific electrical conductivity, tensile strength, yield strength, elongation and Vickers hardness (HV10 scale).

Today’s world is a place where lack of electrical energy would be unimaginable for most of society. All the conductors in the world, both aluminum and copper, have their origin in various types of casting lines where the liquid metal after crystallization is being processed into the form of wires and microwires. However, the efficiency of the continuous casting processes of metals and the final quality of the manufactured product strictly depend on the design of the used crystallizers, the materials used during its production and its quality. Research conducted in this paper focuses on the latter, i.e., external surface quality of the graphite crystallizer at the place of contact with the primary cooling system. In order to quantify its influence on the continuous casting process numerical analyses using the finite element method has been conducted, which results have been further confirmed during empirical tests in laboratory conditions. It has been proven with all of the proposed methods that the temperature of the obtained cast rod is closely linked to the aforementioned surface quality, as when its roughness coefficient surpasses a certain value the temperature of the obtained product increases almost twofold from approx. 150–170 °C to 300–320 °C. These values might influence the quality and final properties of the cast rod, the susceptibility to wire drawing process and possible formation of wire drawing defects and therefore be of much importance to the casting and processing industry.

This study presents results on developing new copper alloys for electrode caps used in resistance spot welding (RSW) of galvanized steel sheets. Two copper alloys—CuCr0.7Zr0.05 and CuCr0.3Ni0.1Zr0.05—were modified with scandium (Sc) additions of 0.01 and 0.05 wt. %. Within this article, the influence of scandium content on Vickers hardness (HV) and electrical conductivity during alloy aging was investigated. In addition, the electrode life of the produced electrodes was subjected to detailed analysis. The results demonstrated that Sc modification enables an increase in hardness with only a minimal decrease in electrical conductivity. Moreover, Sc-modified electrodes exhibited a significantly reduced diffusion layer thickness in the electrode material, which led to lower degradation of the working face geometry and reduced material loss compared with commercial Cu–Cr–Zr electrodes. Mechanical testing showed that spot joints produced with the new electrodes exceed the minimum shear–tension strength requirements even after 500 welds. These results confirm that the proposed alloying approach extends electrode cap life and improves spot weld quality, supporting its application in industrial RSW.