Additive manufacturing (AM) is used in many fields and is a method used to replace wood components or wood-jointed furniture components in the furniture industry. Replacing wood joints by 3D printed connectors would be an advantage, considering the fact that during the process of assembling furniture, the execution technology of the joints is difficult, time-consuming, and labor-intensive. Advanced technology of AM applied in furniture manufacturing helps the designers to create new concepts of product design, with no limits of shape, number of joints, color, or size. The diversity of 3D printers and AM technologies provides the selection of materials in relation with the applicability of the 3D printed object. In this respect, the objective of the present research is to design a 3D printed connector to be used for jointing three chair components, namely the leg and two stretchers made from larch (Larix decidua Mill.) wood, and to use reinforced polylactic acid (PLA) fiberglass (20 wt. %) filament for 3D printing this connector using AM with fused filament fabrication (FFF) technology. The design of the connector, the possibility of using this type of material, and the deposition method of filament were investigated in this research. For this purpose, several evaluation methods were applied: microscopic investigation with 50×, 100×, and 200× magnifications, both of the filament and of the 3D printed connector; mechanical testing of corner joint formed with the help of connector between chair leg and the two stretchers; and a microscopic investigation of the connectors’ defects that occurred after applying the compression and tensile loads on the diagonal direction of the L-type joint. The microscopic investigation of the composite filament revealed the agglomerations of glass fibers into the core matrix and areas where the distribution of the reinforcements was poor. The heterogeneous structure of the filament and the defects highlighted in the 3D printed connectors by the microscopic investigation contributed to the mechanical behavior of L-type connecting joints. The bending moments resulting from compression and tensile tests of the 3D printed connectors were compared to the results recorded after testing, under the same conditions, the normal mortise–tenon joint used to assemble the abovementioned chair components. The larch wood strength influenced the mechanical results and the conclusions of the microscopic investigations, as well as the analysis of the broken connectors after testing recommended the change of connector design and filament deposition direction.

Effect of Particle Size and Geometry on the Performance of Single-layer and Three-layer Particleboard Made from Sunflower Seed Husks

The acoustic features of old resonance wood in violins exhibit a superior quality when compared to those from new resonance wood. This study focuses on an assessment of the sound quality of two types of wood for musical instruments, spruce and maple (class A and D), before and after aging via thermal and UV exposure. The samples were characterized before and after UV aging in terms of color change (using a Chroma meter), surface morphology (using a MarSurf XT20 instrument), chemical changes (monitored by FTIR spectroscopy), and sound propagation speed (using an ultrasound device). After UV treatment, the wavier surface increased the area of exposure and degradation. Also, the color changes were found to be more accentuated in the case of spruce compared to sycamore maple. The FTIR results indicated more advanced aging processes for spruce when compared to maple under the same experimental conditions. This difference resulted mostly from the increased formation of carbonyl-containing chromophores via oxidative processes in spruce rather than in maple, which is in agreement with the color change findings. Exposure of both species to thermal and UV radiation led to an increase in sound propagation speed, both longitudinally and radially, and to a greater extent in wood quality class A when compared to quality class D.

The aim of this research was to evaluate the potential of magnesium lignosulfonate as adhesive in particleboard manufacturing. Diphenylmethane diisocyanate (PMDI) between 1% and 3% and glucose (1% of the lignosulfonate content) were added as potential cross-linkers in the adhesive formulations. Mixed beech and spruce wood, 30% beech wood and 70% spruce wood, were employed for the configuration of the panel structure. The density, mechanical properties and formaldehyde emission of single-layer particleboard were investigated. Spectroscopic analysis (FTIR) revealed structural changes brought by oxidation that may indicate depolymerization by the splitting of C-O-C bonds and formation of carbonyl groups. Mechanical properties were improved, and the highest average values were recorded for panels having as adhesives oxidized lignin with cross-linkers as follow: 15 N/mm² (MOR), 3320 N/mm² (MOE) and 0.48 N/mm² (IB). The density profile presented higher values for faces in case of oxidized lignin panels. Changes were observed for oxidized lignin with cross-linker panels wherein the core had higher values. The results showed that the panels manufactured with adhesives composed of oxidized lignosulfonate (20% of the dried wood particles weight) and the addition of PMDI and glucose in various percentages have a positive influence on their formaldehyde release and mechanical properties requested by EN 312 (2004) standard.