Additive manufacturing (AM) is used in many fields and is a method used to replace wood components or wood-jointed furniture components in the furniture industry. Replacing wood joints by 3D printed connectors would be an advantage, considering the fact that during the process of assembling furniture, the execution technology of the joints is difficult, time-consuming, and labor-intensive. Advanced technology of AM applied in furniture manufacturing helps the designers to create new concepts of product design, with no limits of shape, number of joints, color, or size. The diversity of 3D printers and AM technologies provides the selection of materials in relation with the applicability of the 3D printed object. In this respect, the objective of the present research is to design a 3D printed connector to be used for jointing three chair components, namely the leg and two stretchers made from larch (Larix decidua Mill.) wood, and to use reinforced polylactic acid (PLA) fiberglass (20 wt. %) filament for 3D printing this connector using AM with fused filament fabrication (FFF) technology. The design of the connector, the possibility of using this type of material, and the deposition method of filament were investigated in this research. For this purpose, several evaluation methods were applied: microscopic investigation with 50×, 100×, and 200× magnifications, both of the filament and of the 3D printed connector; mechanical testing of corner joint formed with the help of connector between chair leg and the two stretchers; and a microscopic investigation of the connectors’ defects that occurred after applying the compression and tensile loads on the diagonal direction of the L-type joint. The microscopic investigation of the composite filament revealed the agglomerations of glass fibers into the core matrix and areas where the distribution of the reinforcements was poor. The heterogeneous structure of the filament and the defects highlighted in the 3D printed connectors by the microscopic investigation contributed to the mechanical behavior of L-type connecting joints. The bending moments resulting from compression and tensile tests of the 3D printed connectors were compared to the results recorded after testing, under the same conditions, the normal mortise–tenon joint used to assemble the abovementioned chair components. The larch wood strength influenced the mechanical results and the conclusions of the microscopic investigations, as well as the analysis of the broken connectors after testing recommended the change of connector design and filament deposition direction.

The present paper investigates the possibility of replacing the traditional L-type corner joint used in chair construction with a 3D printed connector, manufactured using the Fused Filament Fabrication (FFF) method and black PLA as filament. The connector was designed to assemble the legs with seat rails and stretchers, and it was tested under diagonal tensile and compression loads. Its performance was compared to that of the traditional mortise-and-tenon joint. Stresses and displacements of the jointed members with connector were analyzed using non-linear Finite Element Method (FEM) analysis. Both connector and mortise-and-tenon joint were employed to build chair prototypes made from beech wood (Fagus sylvatica L.). Digital Image Correlation (DIC) method was used to analyze the displacements in the vicinity of the jointed members of the chairs. Seat and backrest static load tests were carried out in order to verify if the chairs withstand standard loading requirements. Results indicated that the 3D printed connector exhibited equivalent mechanical performance as the traditional joint. The recorded displacement values of the chair with 3D-printed connectors were higher than those of the traditional chair reaching 0.6 mm on the X-axis and 1.1 mm on the Y-axis, without any failures under a maximum vertical load of approximately 15 kN applied to the seat. However, it successfully withstood the loads for seating and backrest standard tests, in accordance with EN 1728:2012, without any structural failure. This paper presents a new approach for the chair manufacturing sector, with potential applicability to other types of furniture.

Additive manufacturing (AM) is a potential technology to be applied for replacing wood joints in the furniture industry. Overall, 3D-printed connectors have a lot of advantages in chair construction: the possibility of improving the design by using colored materials and new concepts with no limits of shape and size, avoiding the use of synthetic materials such as adhesives and finishing materials. The present research shows the results of the research conducted on 3D-printed connectors for a chair leg-stretchers joint. Larch (Larix decidua Mill.) wood was used for chair components and selective laser sintering (SLS) technology was employed for the 3D-printing connector designed to assemble the chair elements. Diagonal tensile and compression tests were performed on the L-type joints with 3D-printed connectors and the bending moments were determined and compared to the results obtained after testing the leg-stretchers mortise–tenon joints made of larch wood, taken as a reference. Micrograph investigation was finally performed on the broken areas of the 3D-printed connectors as a result of mechanical testing failures. The results show that the SLS printing technology applied to build the connector does not ensure enough strength to the assembly, and changes in printing parameters are needed for further research, in terms of laser power and scan speed.