Real-time strain monitoring of large composite structures such as wind turbine blades requires scalable, easily processable and lightweight sensors. In this study, a new type of strain-sensing coating based on 2D MXene nanoparticles was developed. A Ti₃C₂T_z MXene was prepared from Ti₃AlC₂ MAX phase using hydrochloric acid and lithium fluoride etching. Epoxy and glass fibre–reinforced composites were spray-coated using an MXene water solution. The morphology of the MXenes and the roughness of the substrate were characterised using optical microscopy and scanning electron microscopy. MXene coatings were first investigated under various ambient conditions. The coating experienced no significant change in electrical resistance due to temperature variation but was responsive to the 301–365 nm UV spectrum. In addition, the coating adhesion properties, electrical resistance stability over time and sensitivity to roughness were also analysed in this study. The electromechanical response of the MXene coating was investigated under tensile loading and cyclic loading conditions. The gauge factor at a strain of 4% was 10.88. After 21,650 loading cycles, the MXene coating experienced a 16.25% increase in permanent resistance, but the response to loading was more stable. This work provides novel findings on electrical resistance sensitivity to roughness and electromechanical behaviour under cyclic loading, necessary for further development of MXene-based nanocoatings. The advantages of MXene coatings for large composite structures are processability, scalability, lightweight and adhesion properties.

The surface-enhanced Raman scattering (SERS) properties of low-dimensional semiconducting MXene nanoflakes have been investigated over the last decade. Despite this fact, the relationship between the surface characteristics and SERSing performance of a MXene layer has yet to be comprehensively investigated and elucidated. This work shows the importance of surface morphology on the overall SERS effect by studying few-layer Ti₃C₂T_x MXene-based SERS substrates fabricated by vacuum-assisted filtration (VAF) and spray coating on filter paper. The VAF deposition results in a dense MXene layer suitable for SERS with high spot-to-spot and substrate-to-substrate reproducibility, with a significant limit of detection (LoD) of 20 nM for Rhodamine B analyte. The spray-coated MXenes film revealed lower uniformity, with a LoD of 50 nM for drop-casted analytes. Moreover, we concluded that the distribution of the analyte deposited onto the MXene layer is affected by the presence of MXene aggregates created during the deposition of the MXene layer. Accumulation of the analyte molecules in the vicinity of MXene aggregates was observed for drop-casted deposition of the analyte, which affects the resulting SERS enhancement. Ti₃C₂T_x MXene layers deposited on filter paper by VAF offer great potential as a cost-effective, easy-to-manufacture, yet robust, platform for sensing applications.

Smart protective coatings and devices are currently of great interest. In particular, they can absorb or reflect harmful waves of electromagnetic interference (EMI). In this work, novel binary and ternary composites with highly amorphous poly(vinyl alcohol) (HAVOH) as a matrix and single-walled carbon nanotubes (SWCNTs) and MXenes as nanofillers were prepared. HAVOH is a recently patented kind of poly(vinyl alcohol) (PVOH) that was modified with diol monomers. MXenes are a new type of inorganic two-dimensional (2D) nanoparticle consisting of carbides, nitrides and carbonitrides. Three series of composites, HAVOH/SWCNTs, HAVOH/MXenes and HAVOH/SWCNTs/MXenes, were prepared using the solvent casting method. Samples were tested with various methods to study their structure, electrical properties, thermal behavior and EMI-shielding properties. HAVOH/3.0 wt.% SWCNTs/3.0 wt.% MXene specimens revealed a shielding effectiveness of 55 dB, which is 122 times better than that of the neat matrix. These results are promising for the fabrication of films with protective effects against EMI.

Two-dimensional (2D) nanomaterials are promising for many different applications. Therefore, detailed characterization and knowledge of their properties are needed. This work focused on graphene oxide (GO) and a new 2D nanomaterial, MXene, type Ti ₃ C ₂ T _x . The spray coating method was used to create thin GO and MXene films on a glass substrate. Their composition was characterized by X-ray photoelectron spectroscopy. Scanning probe microscopy (SPM) imaging and surface free energy calculation confirmed the homogenous coating of the substrate. The mechanical properties of the prepared films were measured by nanoindentation. The elastic modulus was independent of the film thickness; it was approximately 89 GPa for the MXene samples and approximately 100 GPa for the GO samples. Lower hardness values were determined for thicker films: 10.5 GPa for 5-layer MXene vs. 7.5 GPa for 10-layer MXene and 13.0 GPa for 5-layer GO vs. 9.8 GPa for 10-layer GO. Contact angle measurements and surface energy calculations were performed for all prepared films with 5 or 10 layers. MXenes oxidize on air over time, and the highly conductive Ti ₃ C ₂ T _x structure changes to less conductive titanium oxides. The aging of MXene was studied by monitoring the MXene film conductivity within two months, which showed a decrease, but the 10-layer films were more stable than the thinner 5-layer films.

MXenes, a new family of two-dimensional transition-metal carbides and nitrides, have attracted significant interest in biomedicine because of their tunable surface groups and multifunctional properties. Hydrogels, with their three-dimensional polymeric networks rich in water, provide excellent biocompatibility and structural similarity to those of biological tissues. Although synthetic polymer–based MXene hydrogels are well studied, polysaccharide-based systems remain underexplored despite their biodegradability and biomedical relevance. In this work, MXene nanosheets were incorporated into a sodium alginate (ALG)–gellan gum (GG) polymeric blend to develop polysaccharide/MXene hydrogels. Two dehydration approaches, conventional drying and freeze-drying were used to evaluate their influence on the characteristics of the composite, including microstructure, surface roughness, compressive behavior, water states, and thermal stability. Conventionally dried polysaccharide/MXene nanocomposites with 1.0% wt. MXene have reduced the swelling ratio by ~60% and the volume change by 40% compared to polysaccharide blend. Freeze-dried polysaccharide/MXene nanocomposite hydrogels developed a porous, interconnected network, making them promising for applications requiring high surface area, such as adsorption and tissue engineering. In contrast, conventionally dried samples formed compact, smooth structures with improved barrier and mechanical performance. These results demonstrate that the dehydration strategy strongly governs the polymer network architecture, water states, and material functionality, offering pathways to tailor hydrogel modified with MXene for specific biomedical applications.